Abstract:

Silica was prepared by alkali dissolution-precipitation with oil shale as starting material, and the content of SiO₂ in oil shale was reduced.The detailed processing conditions were as follows: molar ratio of NaOH to SiO₂ was 4, mass ratio of water to oil shale was 1, the treating condition was at 100℃ for 6 h, and grain size was more than 0.15 mm.Then acid leaching of oil shale was performed to prepare γ-Al₂O₃, and the content of Al₂O₃ and Fe₂O₃ in oil shale was reduced too.The acid leachate solution was modulated to pH＝12.0 by adding alkali solution, and a mixture of γ-Al₂O₃ and Fe₂O₃ was precipitated and filtered, then γ-Al₂O₃ and Fe₂O₃ were separated completely by adding acid solution to pH＝6.0.Finally, the treated oil shale had a kerogen content of 71.6％ and the kerogen was validated by FT-IR.