苯甲酸钠对AM60镁合金在氯化钠溶液中的缓蚀作用

doi:10.3969/j.issn.0438-1157.2013.10.032

化工学报 ›› 2013, Vol. 64 ›› Issue (10): 3714-3724.DOI: 10.3969/j.issn.0438-1157.2013.10.032

苯甲酸钠对AM60镁合金在氯化钠溶液中的缓蚀作用

赵阳, 梁平, 史艳华, 王旭

辽宁石油化工大学机械工程学院, 辽宁抚顺 113001

收稿日期:2012-11-11 修回日期:2013-05-30 出版日期:2013-10-05 发布日期:2013-10-05
通讯作者: 梁平
作者简介:赵阳(1989-),男,硕士研究生。
基金资助:
辽宁省教育厅2012年科学研究一般项目(L2012127)

Corrosion inhibition of sodium benzoate for AM60 magnesium alloys in 3.5% NaCl solution

ZHAO Yang, LIANG Ping, SHI Yanhua, WANG Xu

School of Mechanical Engineering, Liaoning Shihua University, Fushun 113001, Liaoning, China

Received:2012-11-11 Revised:2013-05-30 Online:2013-10-05 Published:2013-10-05
Supported by:
supported by the 2012 General Science Study Project of Education Department of Liaoning Province(L2012127).

摘要/Abstract

摘要： 为了改善AM60镁合金的抗腐蚀性能,通过电化学阻抗、极化曲线和浸泡等方法研究了苯甲酸钠(SB)对AM60镁合金在3.5%氯化钠溶液中的缓蚀作用,并考察了温度对缓蚀率的作用规律,借助扫描电镜观察了不同温度和不同SB浓度下镁合金腐蚀后的表面形貌,分析了SB的缓蚀机制。结果表明:SB明显减缓了AM60镁合金的腐蚀速率,当其浓度为0.5 mol·L^-1时,缓蚀率达到75%以上,这主要是因为SB在AM60镁合金表面发生了物理吸附,这种吸附为放热、熵增的自发过程,形成的多分子吸附层隔离了镁合金和腐蚀介质的直接接触。随着SB浓度增加,镁合金腐蚀反应活化能增大,缓蚀率随之而增大。当SB浓度增大到0.7 mol·L^-1以后,由于分子间排斥作用占主导作用,导致缓蚀率没有明显增加,且随着温度从25℃升高到70℃,SB的缓蚀率略有下降。

关键词: 苯甲酸钠, AM60镁合金, 吸附, 缓蚀率

Abstract: To improve the corrosion resistance of magnesium alloys,corrosion inhibition of sodium benzoate(SB)for AM60 magnesium alloy in 3.5%NaCl solution and influence of temperature on inhibition efficiency were investigated with electrochemical impedance spectroscopy(EIS),polarization curves and immersion.Surface morphology of magnesium alloy after corroding with different concentrations of SB at different temperatures was observed with scanning electron microscope(SEM),and corrosion inhibition mechanism of SB was analyzed.SB reduced obviously the corrosion rate of AM60 magnesium alloy in 3.5% NaCl solution,and inhibition efficiency was more than 75% at 0.5 mol·L^-1 SB.Physical adsorption of SB occurred on AM60 magnesium alloy,and it belonged to an exothermic,entropy increase and spontaneous process.A multi-molecular adsorption layer was formed on the magnesium alloy surface to prevent the magnesium alloy from contacting corrosive solution.The activation energy for the corrosive reaction increased with increasing SB concentration,resulting in increasing inhibition efficiency.When SB concentration was up to 0.7 mol·L^-1,inhibition efficiency did not increase,because intermolecular repulsion dominated with increasing SB concentrations.Moreover,inhibition efficiency did not increase when temperature changed from 25℃ to 70℃.

Key words: sodium benzoate, AM60 magnesium alloy, adsorption, inhibition efficiency

中图分类号:

TG174.42

赵阳, 梁平, 史艳华, 王旭. 苯甲酸钠对AM60镁合金在氯化钠溶液中的缓蚀作用[J]. 化工学报, 2013, 64(10): 3714-3724.

ZHAO Yang, LIANG Ping, SHI Yanhua, WANG Xu. Corrosion inhibition of sodium benzoate for AM60 magnesium alloys in 3.5% NaCl solution[J]. CIESC Journal, 2013, 64(10): 3714-3724.

参考文献 24

[1]	Barchiche C E,Rocca E,Juers C,Hazan J,Steinmetz J. Corrosion resistance of plasma-anodized AZ91D magnesium alloy by electrochemical methods[J].Electrochim. Acta,2007,53(2):417-25
[2]	Mordike B L,Ebert T.Magnesium:properties applications potential[J].Mater. Sci. Eng.,2001,A302(1):37-45
[3]	Genevieve Baril,Nadine Pebere.The corrosion of pure magnesium in aerated and deaerated sodium sulphate solutions[J].Corros. Sci.,2001, 43(3):471-484
[4]	Ambat R,Aung N N,Zhou W.Evaluation of microstructural effects on corrosion behavior of AZ91D magnesium alloy[J].Corros. Sci.,2000,42(8):1433-1455
[5]	Song Guangling(宋光铃).Corrosion and Protection of Magnesium Alloys(镁合金腐蚀与防护)[M].Beijing:Chemical Industry Press,2006:282
[6]	Wu Guohua(吴国华),Fan Yu(樊昱),Zhai Chunquan(翟春泉),Ding Wenjiang(丁文江).Effect of La on the corrosion resistance of AZ91D magnesium alloy in NaCl aqueous solution[J].Acta Metall. Sin.(金属学报),2008,44(10):1247-1252
[7]	Bohm S,Greef R,Mcmurray H N,Powell S M,Worsley D A.Kinetic and mechanistic studies of rare earth-rich protective film formation using in situ ellipsometry[J].J. Electrochem. Soc.,2000,147(9):3286-3293
[8]	Bastos A C,Ferreir M G,Simoes A M.Corrosion inhibition by chromate and phosphate extracts for iron substrates studied by EIS and SVET[J].Corros. Sci.,2006,48(6):1500-1512
[9]	Li Lingjie(李凌杰),Yao Zhiming(姚志明),Lei Jinglei(雷惊雷),Xu Hui(徐辉),Zhang Shengtao(张胜涛),Pan Fusheng(潘复生).Adsorption and corrosion inhibition behavior of sodium dodecylbenzeesulfonate on AZ31 magnesium alloy[J].Acta Physico-Chimica Sinica(物理化学学报),2009,25(7):1332-1336
[10]	Li Lingjie(李凌杰),Lei Jinglei(雷惊雷),Yu Shenghai(于生海),Zhao Chuan(赵川),Zhang Shengtao(张胜涛),Pan Fusheng(潘复生).Inhibition of corrosion of magnesium alloy by molybdate in simulated cooling water[J].Journal of Chemical Industry and Engineering(China)(化工学报),2008,59(5):1223-1227
[11]	Wu Yinshun(吴荫顺),Zheng Jiashen(郑家燊).Electrochemical Protection and Corrosion Inhibition Technology(电化学保护和缓蚀剂应用技术)[M].Beijing:Chemical Industry Press,2005:6
[12]	Ramazan Kahraman.Inhibition of atmospheric corrosion of mild steel by sodium benzoate treatment[J].J. Mater. Eng. Perform.,2002,11(1):46-50
[13]	Badiea A Mohammed,Kikkeri N Mohana.The effect of the sodium benzoate and sodium 4-(phenylamino)benzenesulfonate on the corrosion behavior of low carbon steel[J].Monatshefte fur Chemie,2009,140(1):1-8
[14]	Jha G S,Choudhary B P,Sanyl S.Inhibition by benzoate on corrosion of mild steel in binary mixture of aggressive ions[J].Transactions of the SAEST,2006,41(1):18-26
[15]	Li Lingjie(李凌杰),Yao Zhiming(姚志明),Lei Jinglei(雷惊雷),Tang Anming(唐安明),Zhang Shengtao(张胜涛),Pan Fusheng(潘复生).Corrosion inhibition of sodium benzoate on AZ31 magnesium alloy[J].Materials Protection(材料保护),2009,42(11):24-26
[16]	Cao Chunan(曹楚南),Zhang Jianqing(张鉴清).Introduction of Electrochemical Impedance Spectroscopy(电化学阻抗谱导论)[M].Beijing:Science Press,2002:46
[17]	Baril G,Blane C,Pebere N.AC impedance spectroscopy in characterizing time-dependent corrosion of AZ91 and AM50 magnesium alloys:characterization with respect to their microstructures[J].J. Electrochem. Soc.,2001, 148(12):B489-B496
[18]	Song G,Atrens A,Stjohn D,Nairn J,Li Y.The electrochemical corrosion of pure magnesium in 1N NaCl[J].Corros. Sci.,1997,39(5):855-875
[19]	El-Dahan H A,Soror T Y,El-Sherif R M.Studies on the inhibition of aluminum dissolution by hexamine-halide blends(Ⅰ):Weight loss,open circuit potential and polarization measurements[J].Mate. Chem. Phys.,2005, 89(2/3):260-267
[20]	Nan Z Y,Ishihara S,Goshima T.Corrosion fatigue behavior of extruded magnesium alloy AZ31 in sodium chloride solution[J].Inte. J. Fatigue,2008, 30(7):1181-1188
[21]	Tavakolli H,Shahrabi T,Hosseini M G.Synergistic effect on corrosion inhibition of copper by sodium dodecylbenzenesulphonate(SDBS)and 2-meicaptobenzoxazole[J].Mater. Chem. Phys.,2008,109(2),281-286
[22]	Mu Guannan,Li Xueming,Liu Guangheng.Synergistic inhibition between Tween 60 and NaCl on the corrosion of cold rolled steel in 0.5 M sulfuric acid[J].Corros. Sci.,2005,47(8):1932-1952
[23]	Physical Chemistry Teaching and Research Section of the Tianjin University(天津大学物理化学教研室).Physical Chemistry(next volume)(物理化学(下册))[M].Beijing:Higher Education Press,2001:219
[24]	Mu Guannan,Li Xianghong,Qu Qing,Zhou Jun. Molybdate and tungstate as corrosion inhibitors for cold rolling steel in hydrochloric acid solution[J].Corros. Sci.,2006,48(2):445-459

苯甲酸钠对AM60镁合金在氯化钠溶液中的缓蚀作用

Corrosion inhibition of sodium benzoate for AM60 magnesium alloys in 3.5% NaCl solution

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 24

相关文章 15

编辑推荐

Metrics

本文评价

[1]	晁京伟, 许嘉兴, 李廷贤. 基于无管束蒸发换热强化策略的吸附热池的供热性能研究[J]. 化工学报, 2023, 74(S1): 302-310.
[2]	杨学金, 杨金涛, 宁平, 王访, 宋晓双, 贾丽娟, 冯嘉予. 剧毒气体PH₃的干法净化技术研究进展[J]. 化工学报, 2023, 74(9): 3742-3755.
[3]	高燕, 伍鹏, 尚超, 胡泽君, 陈晓东. 基于双流体喷嘴的磁性琼脂糖微球的制备及其蛋白吸附性能探究[J]. 化工学报, 2023, 74(8): 3457-3471.
[4]	盛冰纯, 于建国, 林森. 铝基锂吸附剂分离高钠型地下卤水锂资源过程研究[J]. 化工学报, 2023, 74(8): 3375-3385.
[5]	张瑞航, 曹潘, 杨锋, 李昆, 肖朋, 邓春, 刘蓓, 孙长宇, 陈光进. ZIF-8纳米流体天然气乙烷回收工艺的产品纯度关键影响因素分析[J]. 化工学报, 2023, 74(8): 3386-3393.
[6]	王杰, 丘晓琳, 赵烨, 刘鑫洋, 韩忠强, 许雍, 蒋文瀚. 聚电解质静电沉积改性PHBV抗氧化膜的制备与性能研究[J]. 化工学报, 2023, 74(7): 3068-3078.
[7]	陈吉, 洪泽, 雷昭, 凌强, 赵志刚, 彭陈辉, 崔平. 基于分子动力学的焦炭溶损反应及其机理研究[J]. 化工学报, 2023, 74(7): 2935-2946.
[8]	王新悦, 王俊杰, 曹思贤, 王翠, 李灵坤, 吴宏宇, 韩静, 吴昊. 玻璃内包材界面修饰对机械应力诱导的单克隆抗体聚集体形成的影响[J]. 化工学报, 2023, 74(6): 2580-2588.
[9]	陈韶云, 徐东, 陈龙, 张禹, 张远方, 尤庆亮, 胡成龙, 陈建. 单层聚苯胺微球阵列结构的制备及其吸附性能[J]. 化工学报, 2023, 74(5): 2228-2238.
[10]	蔺彩虹, 王丽, 吴瑜, 刘鹏, 杨江峰, 李晋平. 沸石中碱金属阳离子对CO₂/N₂O吸附分离性能的影响[J]. 化工学报, 2023, 74(5): 2013-2021.
[11]	李辰鑫, 潘艳秋, 何流, 牛亚宾, 俞路. 基于碳微晶结构的炭膜模型及其气体分离模拟[J]. 化工学报, 2023, 74(5): 2057-2066.
[12]	王蕾, 王磊, 白云龙, 何柳柳. SA膜状锂离子筛的制备及其锂吸附性能[J]. 化工学报, 2023, 74(5): 2046-2056.
[13]	肖川宝, 李林洋, 刘武锋, 钟年丙, 解泉华, 钟登杰, 常海星. 光催化与离子交换吸附耦合有效去除2，4，6-三氯苯酚[J]. 化工学报, 2023, 74(4): 1587-1597.
[14]	潘煜, 王子航, 王佳韵, 王如竹, 张华. 基于可得然-氯化锂复合吸附剂的除湿换热器热湿性能研究[J]. 化工学报, 2023, 74(3): 1352-1359.
[15]	吴选军, 王超, 曹子健, 蔡卫权. 数据与物理信息混合驱动的固定床吸附穿透深度学习模型[J]. 化工学报, 2023, 74(3): 1145-1160.