钙铝比对11.3CaO·7Al2O3微观结构及其溶出性能的影响

doi:10.3969/j.issn.0438-1157.2014.10.057

化工学报 ›› 2014, Vol. 65 ›› Issue (10): 4183-4190.DOI: 10.3969/j.issn.0438-1157.2014.10.057

• 材料化学工程与纳米技术 • 上一篇下一篇

钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响

王波, 宗书凤, 孙会兰, 张建新

河北科技大学材料科学与工程学院, 河北省材料近净成形技术重点实验室, 河北石家庄 050018

收稿日期:2014-03-05 修回日期:2014-05-22 出版日期:2014-10-05 发布日期:2014-10-05
通讯作者: 王波
基金资助:
国家自然科学基金项目（51104053）；中国博士后科学基金项目（2012M510821）；河北省自然科学基金项目（E2012208047）。

Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃

WANG Bo, ZONG Shufeng, SUN Huilan, ZHANG Jianxin

Hebei Key Laboratory of Material Near-Net Forming Technology, School of Material Science and Engineering, Hebei University of Science and Technology, Shijiazhuang 050018, Hebei, China

Received:2014-03-05 Revised:2014-05-22 Online:2014-10-05 Published:2014-10-05
Supported by:
supported by the National Natural Science Foundation of China (51104053), China Postdoctoral Science Foundation (2012M510821) and the Natural Science Foundation of Hebei Province (E2012208047).

摘要/Abstract

摘要： 通过高温烧结法在不同钙铝比（C/A）的条件下合成了铝酸钙熟料。利用XRD对不同C/A下合成产物进行物相分析，对含量进行半定量分析，并计算其晶格常数。采用SEM观察不同C/A下合成产物的显微结构，并通过EDS佐证所得物相；最后研究了不同C/A下氧化铝的溶出性能。结果表明：当C/A<1.6时得到的产物为CaO·Al₂O₃和11.3CaO·7Al₂O₃（C_11.3A₇），且随着C/A的增大，C_11.3A₇的含量增高，氧化铝的溶出率提高；当C/A＝1.6时得到的产物只有C_11.3A₇，溶出率达到最大；当C/A>1.6时由于3CaO·Al₂O₃的形成，溶出率有所降低。C_11.3A₇晶格中CaO的缺失，促进了溶出反应的进行。

关键词: 烧结, 钙铝比, 11.3CaO·7Al₂O₃, 显微结构, 氧化铝, 溶出率

Abstract: Calcium aluminate clinkers with different calcium/aluminum ratios (C/A) were obtained by the high-temperature sintering method. Phase composition, phase semi-quantitative content and crystal constant of sinter were studied with different C/A by XRD. SEM and EDS were used to observe microstructure and element contents. The alumina leaching property of sinter was studied. When C/A was lower than 1.6, the products were CaO·Al₂O₃and 11.3CaO·7Al₂O₃ (C_11.3A₇) and increase of calcium/aluminum ratio could lead to increase in the content of C_11.3A₇and leaching ratio of alumina. When C/A was 1.6, the phase was almost completely C_11.3A₇and the leaching rate of alumina reached a maximum. When C/A was higher than 1.6, the products were C_11.3A₇and 3CaO·Al₂O₃, and the leaching rate of alumina decreased accordingly. The lack of CaO in C_11.3A₇lattice improved the leaching reaction.

Key words: sintering, calcium/aluminum ratio, 11.3CaO·7Al₂O₃, microstructure, alumina, leaching rate

中图分类号:

TF803.21

王波, 宗书凤, 孙会兰, 张建新. 钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响[J]. 化工学报, 2014, 65(10): 4183-4190.

WANG Bo, ZONG Shufeng, SUN Huilan, ZHANG Jianxin. Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃[J]. CIESC Journal, 2014, 65(10): 4183-4190.

参考文献 25

[1]	Lü Zijian(吕子剑). Research development in extracting alumina from fly ash[J]. Light Metals(轻金属), 2010(7):12-14，19
[2]	Hu Qinhai(胡勤海), Zhang Hui(张辉), Bai Guanghui(白光辉), Xu Peng(徐鹏), Wang Zhanxiu(王占修), Zhu Jianhang(朱建航). Progress of utilization of fly ash with high concentration alumina[J]. Chemical Industry and Engineering Progress(化工进展), 2011,30(7):1613-1617
[3]	Grzymek J, Derdacka-Grzymek A, Konik Z, J. The new way of alumina lixiviation from sinters containing 12CaO·7Al2O3 in J.Grzymek's method//Light Metal[C]. Warrendale, 1988:129-133
[4]	Smith P. The processing of high silica bauxites-review of existing and potential processes[J]. Hydrometallurgy, 2009, 98(1): 162-176
[5]	Paramguru R, Rath P, Misra V. Trends in red mud utilization-a review[J]. Mineral Processing & Extractive Metall. Rev., 2004, 26(1): 1-29
[6]	Goodboy K P. Investigation of a sinter process for extraction of Al2O3 from coal wastes[J]. Metallurgical and Materials Transactions B, 1976, 7(4): 716-718
[7]	Seeley F G, Mcdowell W J, Felker L K, Kelmers A D, Egan B Z. Determination of extraction equilibria for several metals in the development of a process designed to recover aluminum and other metals from coal combustion ash[J]. Hydrometallurgy, 1981, 6(3/4): 277-290
[8]	Li Laishi(李来时), Zhai Yuchun(翟玉春), Qin Jinguo(秦晋国), Wu Yan(吴艳), Liu Yingying(刘瑛瑛). Extracting high purity alumina from fly ash[J]. Journal of Chemical Industry and Engineering(China) (化工学报), 2006, 57(9):2189-2193
[9]	Wójcik M. The thermal decomposition of the carbonate reaction products[J]. Journal of Thermal Analysis and Calorimetry, 1995, 43(1): 149-156
[10]	Xiao Wei(肖玮), Liu Wei(刘卫), Zhang Nianbing(张念炳), Li Zhiying(黎志英). Study on the process of extracting alumina from the middling grade bauxite using lime sinter[J]. Journal of Guizhou University of Technology:Natural Science Edition(贵州工业大学学报：自然科学版), 2008, 37(5): 41-43
[11]	Li Zhiying(黎志英), Zhang Nianbing(张念炳), Xiao Wei(肖玮), Liu Wei(刘卫). Research on the intensified sintering mechanism of middle-grade bauxite and its digestion performances[J]. Light Metals(轻金属), 2009(12):14-17
[12]	Zhang Wu(张武). Research on the phase compositions and leaching properties of sintering products in CaO-Al2O3-SiO2 system[D]. Shenyang: Northeastern University, 2011
[13]	Bartl H, Scheller T. Zur Struktur des 12CaO· 7Al2O3[J]. Neues Jahrb. Mineral. Monatsh, 1970, 35: 547-552
[14]	Christensen A N. Neutron powder diffraction profile refinement studies on Ca11.3А114O32.3 and CaClO [J]. Acta Chemica Scandinavia A, 1987, 41: 110-112
[15]	Teng Hui, Wang Jun, Ren Xiaoqian, Chen Demin. Disproportionation of toluene by modified ZSM-5 zeolite catalysts with high shape-selectivity prepared using chemical liquid deposition with tetraethyl orthosilicate[J]. Chinese Journal ofChemical Engineering, 2011, 19(2): 292-298
[16]	Scrivener K, Füllmann T, Gallucci E, Walenta G, Bermejo E. Quantitative study of Portland cement hydration by X-ray diffraction/Rietveld analysis and independent methods[J]. Cement and Concrete Research, 2004, 34(9): 1541-1547
[17]	Tong Zhifang(佟志芳), Xie Senlin(谢森林), Zhang Liheng(张立恒), Chen Tao(陈涛), Liu Wei(刘卫). Preparation and application of the 12CaO·7Al2O3 material[J]. The Chinese Journal of Nonferrrous Metals(有色金属科学与工程), 2011, 2(6):16-21
[18]	Sun Jianqiu, Gong Lu, Shen Jing, Lin Dan, Li Quanxin. Sol-gel preparation of porous C12A7-Cl- Crystals[J]. Acta Physico-Chimica Sinica, 2010, 26(3):795-798
[19]	Colla E L, Reaney I M, Setter N. Effect of structural changes in complex perovskites on the temperature coefficient of the relative permittivity[J]. Journal of Applied Physics, 1993, 74(5): 3414
[20]	Li Bochun(李柏春), Tian Shuna(田淑娜), Zhang Changwei(张昌伟), Xu Jingrui(徐敬瑞), Lü Longzhu(吕龙柱). Study on reaction magnitude of solid reactive spray tray[J]. Chemical Industry and Engineering Progress(化工进展), 2011, 30(8): 1687-1692
[21]	Toda Y, Miyakawa M, Hayashi K, Kamiya T, Hirano M, Hosono H. Thin film fabrication of nano-porous 12CaO·7Al2O3 crystal and its conversion into transparent conductive films by light illumination[J]. Thin Solid Films, 2003, 445(2): 309-312
[22]	Chatterjee A, Nishioka M, Mizukami F. A periodic first principle study to design microporous crystal 12MO, 7Al2O3 for selective and active O- radicals encaging[J]. Chemical Physics Letters, 2004, 390(4/5/6): 335-339
[23]	Di Yuezhong(狄跃忠), Wang Zhihui(王智慧), Wang Yaowu(王耀武), Peng Jianping(彭建平), Feng Naixiang(冯乃祥). Extract of high-whiteness aluminum hydroxide from residues of novel process of magnesium production by aluminothermic reduction[J].CIESC Journal (化工学报), 2013, 64(3):1106-1111
[24]	Ren Genkuan(任根宽). Behavior of sodium carbonate during leaching process of alumina sinter[J]. Nonferrous Metals:Extractive Metallurgy(有色金属：冶炼部分), 2009 (4):20-22, 48
[25]	Wang Bo, Sun Huilan, Guo Dong , Zhang Xuezheng. Effect of Na2O on alumina leaching property and phase transformation of MgO-containing calcium aluminate slags[J]. Transactions of Nonferrous Metals Society of China, 2011, 21(12):2752-2757"

钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响

Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 25

相关文章 15

编辑推荐

Metrics

本文评价

[1]	曾如宾, 沈中杰, 梁钦锋, 许建良, 代正华, 刘海峰. 基于分子动力学模拟的Fe₂O₃纳米颗粒烧结机制研究[J]. 化工学报, 2023, 74(8): 3353-3365.
[2]	刘春雨, 周桓宇, 马跃, 岳长涛. CaO调质含油污泥干燥特性及数学模型[J]. 化工学报, 2023, 74(7): 3018-3027.
[3]	葛泽峰, 吴雨青, 曾名迅, 查振婷, 马宇娜, 侯增辉, 张会岩. 灰化学成分对生物质气化特性的影响规律[J]. 化工学报, 2023, 74(5): 2136-2146.
[4]	吴学红, 栾林林, 陈亚南, 赵敏, 吕财, 刘勇. 可降解柔性相变薄膜的制备及其热性能[J]. 化工学报, 2023, 74(4): 1818-1826.
[5]	何金峰, 李秀珍, 寇建耀, 陶庭杰, 余灿, 刘欢, 陈永元, 赵豪健, 江大好, 李小年. 乙醇制高级醇有序介孔氧化铝负载铜基催化剂研究[J]. 化工学报, 2023, 74(3): 1082-1091.
[6]	郭祥, 乔金硕, 王振华, 孙旺, 孙克宁. 碳燃料固体氧化物燃料电池结构研究进展[J]. 化工学报, 2023, 74(1): 290-302.
[7]	袁妮妮, 郭拓, 白红存, 何育荣, 袁永宁, 马晶晶, 郭庆杰. 化学链燃烧过程Fe₂O₃/Al₂O₃载氧体表面CH₄反应：ReaxFF-MD模拟[J]. 化工学报, 2022, 73(9): 4054-4061.
[8]	李亚芾, 付亮亮, 白浩隆, 白丁荣, 许光文. 菱镁矿浮选尾矿直接合成同时制备镁橄榄石和镁砂研究[J]. 化工学报, 2022, 73(8): 3679-3687.
[9]	郭志强, 燕可洲, 张吉元, 柳丹丹, 高阳艳, 郭彦霞. 煤矸石/粉煤灰对赤泥钠化还原焙烧反应的影响机制[J]. 化工学报, 2022, 73(5): 2194-2205.
[10]	孙雄康, 李强. 多级复合芯结构的强化沸腾传热研究[J]. 化工学报, 2022, 73(3): 1127-1135.
[11]	王晓蓉, 曾玺, 王芳, 张光义, 许德平, 许光文. 温度和气氛对高K高S糠醛渣灰分的烧结特性研究[J]. 化工学报, 2022, 73(1): 411-424.
[12]	周东一, 肖湘华, 肖飚, 刘益才. 脂肪类复合相变储能材料中脂肪酸最佳质量含量的确定方法[J]. 化工学报, 2021, 72(S1): 560-566.
[13]	高姣丽, 李恩泽, 康锦, 成怀刚. 盐湖老卤动态变温分离高纯结晶硫酸镁[J]. 化工学报, 2021, 72(6): 3022-3030.
[14]	田锐, 王沛力, 吕超, 段雪. 有机-无机复合材料中无机相分散度三维荧光分析[J]. 化工学报, 2021, 72(6): 3002-3013.
[15]	朱慧红, 茆志伟, 杨涛, 冯翔, 金浩, 彭冲, 杨朝合, 王继锋, 方向晨. 催化剂形貌对沸腾床渣油加氢Ni-Mo/Al₂O₃ 催化剂活性位的影响机制[J]. 化工学报, 2021, 72(4): 2076-2085.