搅拌速率及其改变点对高抗冲聚苯乙烯相转变的影响

doi:10.11949/j.issn.0438-1157.20160639

摘要/Abstract

摘要：

以四官能度过氧化物JWEB50为引发剂，本体接枝共聚法制备高抗冲聚苯乙烯（HIPS）。分别采用透射电镜以及相对扭矩变化对聚合体系的粒子结构、黏度变化进行研究，来分析恒定搅拌以及分段搅拌条件下聚合过程的相转变。研究发现，两种分析方法所得结果相近，相转变时的转化率随恒定搅拌速率的增大而降低。采用分段搅拌方式时，相转变前降低搅拌速率可使相转变时的转化率增大，相转变后降低搅拌速率对相转变时的转化率无影响；相转变过程对应的搅拌速率才是影响相转变的“有效搅拌速率”。上述结果对HIPS的产品性能控制具有极其重要的参考价值。

关键词: 高抗冲聚苯乙烯, 聚合, 聚合物, 相变, 搅拌速率, 搅拌速率改变点

Abstract:

High impact polystyrene (HIPS) was prepared by bulk graft copolymerization with four tetrafunctional peroxide JWEB50 as initiator. Phase inversion at constant and staged stirring conditions was analyzed through study of particle structure and viscosity of the polymerization system by transmission electron microscope and change in relative torque. Similar results were obtained from both analyses. For constant stirring, conversion at phase inversion decreased with the increase of stirring speed. For staged stirring, conversion at phase inversion increased when stirring speed was reduced before phase inversion and no effect on conversion at phase inversion was observed if stirring speed was reduced after phase inversion. Therefore, only “effective stirring speed” corresponding to the stirring speed at phase inversion process actually influenced phase inversion. These results could be very important for performance control of HIPS.

Key words: high impact polystyrene, polymerization, polymer, phase change, stirring speed, change time for stirring speed

中图分类号:

TQ325.2

李志丹, 单国荣, 潘鹏举. 搅拌速率及其改变点对高抗冲聚苯乙烯相转变的影响[J]. 化工学报, 2017, 68(2): 788-794.

LI Zhidan, SHAN Guorong, PAN Pengju. Effect of stirring speed and its change time on phase inversion of high impact polystyrene[J]. CIESC Journal, 2017, 68(2): 788-794.

参考文献 20

[1]	FISCHER M, HELLMANN G P. On the evolution of phase patterns during the high-impact-modified polystyrene process[J]. Macromolecules, 1996, 29(7):2498-2509.
[2]	SOTO G, NAVA E, ROSAS M, et al. Bulk polymerization of styrene in presence of polybutadiene:effect of the initiator type and prepolymerization condition on particle morphology[J]. Journal of Polymer Science, 2004, 92(3):1397-1412.
[3]	YEH G C, HAYNIE F H, MOSES R A. Phase-volume relationship at the point of phase inversion in liquid dispersions[J]. AIChE Journal, 1964, 10(2):260-265.
[4]	SPERLING L H, FRIEDMAN D W. Synthesis and mechanical behavior of interpenetrating polymer networks-poly(ethyl acrylate) and polystyrene[J]. Journal of Polymer Science Part A-2:Polymer Physics, 1969, 7(2):425-427.
[5]	SELKER A H, SLEICHER C A. Factors affecting which phase will disperse when immiscible liquids are stirred together[J]. The Canadian Journal of Chemical Engineering, 1965, 43(6):298-301.
[6]	MOLAU G E, KESKKULA H. Heterogneous polymer systems(Ⅳ):Mechanism of rubber particle formation in rubber-modified vinyl polymers[J]. Journal of Polymer Science Part A-1:Polymer Chemistry, 1966, 4(4):1595-1607.
[7]	FREEGUARD G F. Structural control of rubber modified thermoplastic as produced by the mass process[J]. British Polymer Journal, 1974, 6(4):205-228.
[8]	BENDER B W. Dispersion of microgel in impact polystyrene[J]. Journal of Applied Polymer Science, 1965, 9(9):2887-2894.
[9]	李杨, 王梅, 刘宏海, 等. 高抗冲聚苯乙烯的研制[J]. 合成树脂及塑料, 1997, 14(3):10-14. LI Y, WANG M, LIU H H, et al. Research and preparation of high-impact polystyrene[J]. China Synthetic Resin and Plastic, 1997, 14(3):10-14.
[10]	陈连清, 董正卿, 王志, 等. 高抗冲聚苯乙烯的合成、改性与表征(Ⅰ):搅拌条件对抗冲性能的影响[J]. 石油化工, 2002, 31(9):725-729. CHEN L Q, DONG Z Q, WANG Z, et al. Synthesis, modification and characterization of HIPS(Ⅰ):Influence of agitation conditions on impact properties of HIPS[J]. Petrochemical Technology, 2002, 31(9):725-729.
[11]	ESTENOZ D A, LEAL G P, LOPEZ Y R, et al. Bulk polymerization of styrene in the presence of polybutadiene. The use of bifunctional initiators[J]. Journal of Applied Polymer Science, 1996, 62(62):917-939.
[12]	FREEGUARDr G F, KARMARKAR M. The production of rubbermodified polystyrene(Ⅰ):Rheological behavior of the polymerizing system[J]. Journal of Applied Polymer Science, 1971, 15(7):1649-1655.
[13]	BAER M. Studies on heterogeneous polymeric systems(Ⅰ):Influence of morphology on mechanical properties[J]. Journal of Applied Polymer Science, 1972, 16(5):1109-1123.
[14]	WAGNER E R, ROBESON L M. Impact polystyrene:factors controlling the rubber efficiency[J]. Rubber Chemical Technology, 1970, 43(5):1129-1137.
[15]	ESTENOZ D A, MEIRA G R, GÓMEZ N. Mathematical model of a continuous industrial high-impact polystyrene process[J]. AIChE Journal, 1998, 44(44):427-441.
[16]	LEAL G P, ASUA J M. Evolution of the morphology of HIPS particles[J]. Polymer, 2009, 50(1):68-76.
[17]	姚臻, 李伯耿, 曹堃, 等. 高抗冲聚苯乙烯的合成机理与结构, 性能[J]. 化工生产与技术, 1997, (3):20-25. YAO Z, LI B G, CAO K, et al. The synthesis mechanism, structure and properties of high impactive polystyrene[J]. Chemical Production and Technology, 1997, (3):20-25.
[18]	陈媛, 李宝芳, 曹堃, 等. N-PMI-St-PB本体聚合过程中的相转变(Ⅰ):相转变过程中体系物理特征的变化[J].化工学报, 2000, 51(3):362-366. CHEN Y, LI B F, CAO K, et al. Phase inversion during N-phenylmaleimide/styrene in presence of polybutadiene(Ⅰ):Changes of physical characteristics of copolymerizing system during phase inversion[J]. Journal of Chemical Industry and Engineering (China), 2000, 51(3):362-366.
[19]	MUI ETC, BOATENG V B, FELLERS J F, et al. Interaction of polymerization conditions, structural variables, and mechanical properties of rubber-modified plastics produced from bulk polymerized styrene/poly(butadiene-co-styrene)[J]. Journal of Applied Polymer Science, 1982, 27(4):1395-1407.
[20]	MOLAU G E. Heterogeneous polymer systems(Ⅱ):Mechanism of stabilization of polymeric oil-in-oil emulsions[J]. Journal of Polymer Science Part A General Papers, 1965, 3(12):4235-4242.