煤基泡沫炭复合F-TiO2光催化降解苯酚

doi:10.11949/0438-1157.20230834

摘要/Abstract

摘要：

采用溶剂热法及随后的KF溶液浸泡制备了氟掺杂TiO₂（F-TiO₂），以煤疏中质组为原料制备多级孔泡沫炭（CCF），采用浸渍法将F-TiO₂负载于CCF上制得复合型光催化剂F-TiO₂/CCF。以苯酚溶液为目标降解物，研究了氟离子浓度、浸泡时间以及泡沫炭活化时间对催化剂催化性能的影响。分别采用XRD、XPS、SEM、N₂吸附、UV-Vis-DRS等对样品进行表征。结果表明，F-TiO₂/CCF的最佳制备条件为KF溶液浓度0.1 mol/L、浸泡时间24 h、泡沫炭水蒸气活化时间1 h。由此制得的复合催化剂在模拟太阳光下6 h对苯酚的光降解率达76%，总脱除率达89%，比F-TiO₂纳米颗粒的光催化活性提高了2.7倍。4次连续降解循环实验后对苯酚的脱除率仍维持在84%左右。掺杂氟原子的强电负性使F-TiO₂上的Ti化合价更正，更有利于与苯酚上的氧原子进行吸附配位。而泡沫炭载体不仅促进了光生载流子的高效分离，其大/中/微孔的共同作用保证了光的有效利用和苯酚的快速吸附扩散，使F-TiO₂/CCF光催化性能得到了显著的提高。

关键词: 煤基泡沫炭, TiO₂, F掺杂, 光催化降解, 苯酚

Abstract:

Fluorine-doping of TiO₂ (F-TiO₂) was prepared by using solvothermal method and subsequent soaking in KF solution, and hierarchical porous carbon foam (CCF) was prepared by using coal loose medium component as raw material. A composite photocatalyst F-TiO₂/CCF was then prepared by impregnating F-TiO₂ onto CCF. With phenol as the target pollution, the effects of F ion concentration, soaking time and activation time of CCF on the catalytic performance of the catalysts were studied. The samples were characterized by using XRD, XPS, SEM, N₂ adsorption, UV-Vis-DRS, etc. The results showed that the optimized preparation conditions of F-TiO₂/CCF were 0.1 mol/L of KF concentration, 24 h of soaking time, and 1 h of steam activation of CCF. The prepared composite catalyst had a photodegradation rate of 76% for phenol under 6 h of simulated sunlight which was 2.7 times higher than that of F-TiO₂ nanoparticles, and a total removal rate of 89%. After four consecutive degradation cycles, the removal rate of phenol remained around 84%. The strong electronegativity of doped fluorine atoms make the Ti in F-TiO₂ more positive, which is more conducive to coordinate with oxygen atoms in phenol. While the CCF support not only promotes the separation of photoexcited carriers, but also ensures the effective use of light and the rapid adsorption and diffusion of phenol due to its macro/meso/micro porous structure. All these factors contribute to the significant improvement of the photocatalytic performance of F-TiO₂/CCF.

Key words: coal-based carbon foam, TiO₂, F doping, photocatalytic degradation, phenol

中图分类号:

TQ 032.4

杨小芹, 刘馨雨, 杨玉寒, 叶彦, 贾琼, 杨浩男, 秦志宏. 煤基泡沫炭复合F-TiO₂光催化降解苯酚[J]. 化工学报, 2023, 74(12): 4914-4925.

Xiaoqin YANG, Xinyu LIU, Yuhan YANG, Yan YE, Qiong JIA, Haonan YANG, Zhihong QIN. Coal-based carbon foam coated with F-TiO₂ for photocatalytic degradation of phenol[J]. CIESC Journal, 2023, 74(12): 4914-4925.

图/表 9

图1 不同浓度KF溶液改性的TiO2模拟太阳光降解苯酚结果

Fig.1 Results of phenol degradation under simulated sunlight over TiO2 catalysts modified by different concentrations of KF solution

图2 不同KF溶液浸泡时间的F-TiO2模拟太阳光降解苯酚结果

Fig.2 Results of phenol degradation under simulated sunlight over F-TiO2 catalysts with different soaking times of KF solution

图3 不同煤基泡沫炭载体负载的F-TiO2模拟太阳光降解苯酚结果

Fig.3 Results of phenol degradation under simulated sunlight over F-TiO2 catalysts loaded on different CCF supports

图4 F-TiO2/CCF-2模拟太阳光降解苯酚的循环稳定性测试

Fig.4 Recycle test of phenol degradation under simulated sunlight over F-TiO2/CCF-2

图5 不同样品的SEM图和F-TiO2 /CCF-2的EDS 元素分布

Fig.5 SEM images of different samples and EDS element mappings of F-TiO2 /CCF-2

图6 样品的XRD谱图和XPS高分辨谱图

Fig.6 XPD patterns and high resolution XPS spectra for samples

图7 多级孔泡沫炭载体和TiO2光催化剂样品的N2吸附-脱附曲线和孔径分布

Fig.7 N2 adsorption-desorption isotherm curves and pore size distribution of the CCF supports and TiO2 photocatalysts

表1 煤基多级孔泡沫炭载体和TiO2光催化剂样品的孔结构参数

Table 1 Pore structure parameters of CCFs and TiO2 catalysts

样品	S_BET/ (m²/g)	D_ap/ nm	V_t/ (cm³/g)	V_mic/ (cm³/g)	V_meso/ (cm³/g)
CCF-1	225.6	1.95	0.12	0.09	0.02
CCF-2	301.8	2.01	0.15	0.10	0.03
CCF-3	543.1	2.02	0.28	0.17	0.06
CCF-4	618.7	2.16	0.33	0.18	0.09
TiO₂	188.8	4.62	0.22	0.00	0.18
F-TiO₂	143.7	6.40	0.23	0.00	0.21
F-TiO₂/CCF-2	230.1	4.06	0.23	0.04	0.15

图8 样品的紫外可见漫反射光谱、(F(r)hv)1/2的光能对应图、光致发光光谱和光照1 min后DMPO-·OH的ESR 光谱

Fig.8 UV-Vis diffuse reflectance spectra, the plotting of (F(r)hv)1/2vshv, PL spectra and ESR signals of DMPO-·OH after 1 min irradiation for the samples

参考文献 26

1	侯晨涛, 张欣. WO₃/TiOF₂-TiO₂复合催化剂的制备及其光催化性能研究[J]. 北京化工大学学报(自然科学版), 2021, 48(3): 36-47.
	Hou C T, Zhang X. Preparation and photocatalytic performance of a WO₃/TiOF₂-TiO₂ composite photocatalyst[J]. Journal of Beijing University of Chemical Technology (Natural Science Edition), 2021, 48(3): 36-47.
2	马荣, 孙杰, 李东辉, 等. 基于Cu/TiO₂/C-Wood 复合材料的聚光太阳能驱动自漂浮高效海水汽化催化分解制氢体系[J]. 化工学报, 2022,73(4): 1695-1703.
	Ma R, Sun J, Li D H, et al. Self-floating high-efficient evaporative catalytic seawater hydrogen production system driven by concentrated solar energy based on Cu/TiO₂/C-Wood composite [J]. CIESC Journal, 2022, 73(4): 1695-17037.
3	Loo W W, Pang Y L, Lim S, et al. Enhancement of photocatalytic degradation of Malachite Green using iron doped titanium dioxide loaded on oil palm empty fruit bunch-derived activated carbon[J]. Chemosphere, 2021, 272: 129588.
4	Minero C, Mariella G, Maurino V, et al. Photocatalytic transformation of organic compounds in the presence of inorganic anions ( Ⅰ ) : Hydroxyl-mediated and direct electron-transfer reactions of phenol on a titanium dioxide-fluoride system[J]. Langmuir, 2000, 16(6): 2632-2641.
5	Zayadi R A, Abu Bakar F. Comparative study on the performance of Au/F-TiO₂ photocatalyst synthesized from Zamzam water and distilled water under blue light irradiation[J]. Journal of Photochemistry and Photobiology A: Chemistry, 2017, 346: 338-350.
6	Gao Q Z, Si F Y, Zhang S S, et al. Hydrogenated F-doped TiO₂ for photocatalytic hydrogen evolution and pollutant degradation[J]. International Journal of Hydrogen Energy, 2019, 44(16): 8011-8019.
7	Yu Y, Wu H H, Zhu B L, et al. Preparation, characterization and photocatalytic activities of F-doped TiO₂Nanotubes[J]. Catalysis Letters, 2008, 121(1): 165-171.
8	Le T K, Flahaut D, Martinez H, et al. Surface fluorination of single-phase TiO₂ by thermal shock method for enhanced UV and visible light induced photocatalytic activity[J]. Applied Catalysis B: Environmental, 2014, 144: 1-11.
9	钟永辉, 周琪, 刘家琴, 等. 氟化改性TiO₂空心微球的制备及光催化性能[J]. 无机化学学报, 2013, 29(10): 2133-2139.
	Zhong Y H, Zhou Q, Liu J Q, et al. Preparation of fluorizated TiO₂ hollow microspheres and their photocatalytic activity[J]. Chinese Journal of Inorganic Chemistry, 2013, 29(10): 2133-2139.
10	Qian X F, Ren M, Yue D T, et al. Mesoporous TiO₂ films coated on carbon foam based on waste polyurethane for enhanced photocatalytic oxidation of VOCs[J]. Applied Catalysis B: Environmental, 2017, 212: 1-6.
27	Lv K L, Cheng B, Yu J G, et al. Fluorine ions-mediated morphology control of anatase TiO₂ with enhanced photocatalytic activity[J]. Physical Chemistry Chemical Physics, 2012, 14(16): 5349-5362.
28	Dozzi M V, Zuliani A, Grigioni I, et al. Photocatalytic activity of one step flame-made fluorine doped TiO₂ [J]. Applied Catalysis A: General, 2016, 521: 220-226.
29	Dozzi M V, Selli E. Doping TiO₂ with p-block elements: effects on photocatalytic activity[J]. Journal of Photochemistry and Photobiology C: Photochemistry Reviews, 2013, 14: 13-28.
30	Babusenan A, Pandey B, Roy S C, et al. Charge transfer mediated photoluminescence enhancement in carbon dots embedded in TiO₂ nanotube matrix[J]. Carbon, 2020, 161: 535-541.
31	Zhang Z Y, Xiong Z Y, Zhao C C, et al. In-situ carbon-coated TiO₂ boosting the visible-light photocatalytic hydrogen evolution[J]. Applied Surface Science, 2021, 565: 150554.
32	Mrowetz M, Selli E. Enhanced photocatalytic formation of hydroxyl radicals on fluorinated TiO₂ [J]. Physical Chemistry Chemical Physics: PCCP, 2005, 7(6): 1100-1102.
33	Minero C, Mariella G, Maurino V, et al. Photocatalytic transformation of organic compounds in the presence of inorganic ions(Ⅱ): Competitive reactions of phenol and alcohols on a titanium dioxide-fluoride system[J]. Langmuir, 2000, 16(23): 8964-8972.
11	杨玉寒, 杨小芹, 庞军国, 等. 泡沫材料负载TiO₂光催化剂的研究进展[J]. 化工新型材料, 2021, 49(11): 294-299.
	Yang Y H, Yang X Q, Pang J G, et al. Research progress on TiO₂ photocatalyst supported on foam material[J]. New Chemical Materials, 2021, 49(11): 294-299.
12	Uricchio A, Nadal E, Plujat B, et al. Low-temperature atmospheric pressure plasma deposition of TiO₂-based nanocomposite coatings on open-cell polymer foams for photocatalytic water treatment[J]. Applied Surface Science, 2021, 561: 150014.
13	Parale V G, Kim T, Phadtare V D, et al. Enhanced photocatalytic activity of a mesoporous TiO₂ aerogel decorated onto three-dimensional carbon foam[J]. Journal of Molecular Liquids, 2019, 277: 424-433.
14	Yang X Q, Jia Q, Pang J G, et al. Hierarchical porous N-TiO₂/carbon foam composite for enhancement of photodegradation activity under simulated sunlight[J]. Diamond and Related Materials, 2022, 128: 109234.
15	Wang C, Shi Z H, Peng L, et al. Preparation of carbon foam-loaded nano-TiO₂ photocatalyst and its degradation on methyl orange[J]. Surfaces and Interfaces, 2017, 7: 116-124.
16	秦志宏. 煤嵌布结构模型理论[J]. 中国矿业大学学报, 2017, 46(5): 939-958.
	Qin Z H. Theory of coal embedded structure model[J]. Journal of China University of Mining & Technology, 2017, 46(5): 939-958.
17	Liu M, Qin Z H, Yang X Q, et al. Fabricating controllable hierarchical pores on smooth carbon sheet for synthesis of supercapacitor materials[J]. Vacuum, 2019, 168: 108806.
18	王芳, 王雪芹, 程凯, 等. MoS₂负载量对MoS₂/TiO₂光催化降解苯酚效率的影响及其作用机理研究[J]. 燃料化学学报, 2017, 45(8): 1001-1008.
	Wang F, Wang X Q, Cheng K, et al. Effect of MoS₂ loading on the photocatalytic performance of MoS₂/TiO₂ nanocomposites in phenol degradation and the corresponding reaction mechanism analysis[J]. Journal of Fuel Chemistry and Technology, 2017, 45(8): 1001-1008.
19	Marques J, Gomes T D, Forte M A, et al. A new route for the synthesis of highly-active N-doped TiO₂ nanoparticles for visible light photocatalysis using urea as nitrogen precursor[J]. Catalysis Today, 2019, 326: 36-45.
20	Pirsaheb M, Asadi A, Sillanpää M, et al. Application of carbon quantum dots to increase the activity of conventional photocatalysts: a systematic review[J]. Journal of Molecular Liquids, 2018, 271: 857-871.
21	李彦涵, 梁淑芬, 刘孟浩, 等. 介孔生物质基活性炭负载TiO₂的光催化降解动力学研究[J]. 太阳能学报, 2020, 41(7): 17-25.
	Li Y H, Liang S F, Liu M H, et al. Photocatalytic degradation kinetics of mesoporous bio-based activated carbon supported titanium dioxide[J]. Acta Energiae Solaris Sinica, 2020, 41(7): 17-25.
22	Zeng G N, You H Z, Du M M, et al. Enhancement of photocatalytic activity of TiO₂ by immobilization on activated carbon for degradation of aquatic naphthalene under sunlight irradiation[J]. Chemical Engineering Journal, 2021, 412: 128498.
23	Yang Y H, Yang X Q, Jia Q, et al. Enhanced photocatalytic performance of (N, F) co-doped TiO₂ loaded on coal-based hierarchical porous carbon foam under simulated sunlight[J]. Vacuum, 2023, 207: 111577.
24	Velasco L F, Tsyntsarski B, Petrova B, et al. Carbon foams as catalyst supports for phenol photodegradation[J]. Journal of Hazardous Materials, 2010, 184(1/2/3): 843-848.
25	Xu Q C, Zeng J X, Li X Y, et al. 3D nano-macroporous structured TiO₂-foam glass as an efficient photocatalyst for organic pollutant treatment[J]. RSC Advances, 2016, 6(57): 51888-51893.
26	Luo H Y, Nie X, Li G Y, et al. Structural characterization and photocatalytic activity of hydrothermally synthesized mesoporous TiO₂ for 2, 4, 6-tribromophenol degradation in water[J]. Chinese Journal of Catalysis, 2011, 32(6/7/8): 1349-1356.

编辑推荐 0

Metrics

阅读次数

全文

135

HTML			PDF

最新录用	在线预览	正式出版	最新录用	在线预览	正式出版
2	0	14	3	0	116

来源	本网站	其他网站

次数	77	58
比例	57%	43%

摘要

191

最新录用	在线预览	正式出版

18	0	173

来源	本网站	其他网站

次数	64	127
比例	34%	66%

[1]	杨欣, 彭啸, 薛凯茹, 苏梦威, 吴燕. 分子印迹-TiO₂光电催化降解增溶PHE废水性能研究[J]. 化工学报, 2023, 74(8): 3564-3571.
[2]	肖川宝, 李林洋, 刘武锋, 钟年丙, 解泉华, 钟登杰, 常海星. 光催化与离子交换吸附耦合有效去除2，4，6-三氯苯酚[J]. 化工学报, 2023, 74(4): 1587-1597.
[3]	毛恒, 王月, 王森, 刘伟民, 吕静, 陈甫雪, 赵之平. APTES改性ZIF-L/PEBA混合基质膜强化渗透汽化分离苯酚研究[J]. 化工学报, 2022, 73(3): 1389-1402.
[4]	方丽君, 王景梅, 林巧靖, 陈建华, 杨谦. 二苯并-18-冠醚-6/聚醚嵌段酰胺膜富集水中苯酚性能研究[J]. 化工学报, 2021, 72(7): 3716-3727.
[5]	黄文媛, 孙士杰, 唐宏震, 苏智芳, 钟秦迪, 刘幽燕, 李青云. 聚氨酯泡沫固定化Alcaligenes sp.DN25去除苯酚的研究[J]. 化工学报, 2021, 72(5): 2783-2791.
[6]	李超凡, 温玉娟, 曹楠, 孙东, 宋晓明, 杨悦锁. 耐低温对硝基苯酚降解菌的降解动力学研究[J]. 化工学报, 2021, 72(3): 1692-1701.
[7]	史玉婷, 皇甫林, 李长明, 王月, 高士秋, 伞晓广, 韩振南, 余剑. V₂O₅-MoO₃/TiO₂催化滤袋的制备及中试应用[J]. 化工学报, 2021, 72(11): 5598-5606.
[8]	梁文俊, 朱玉雪, 石秀娟, 孙慧频, 任思达. Ce掺杂对Ru/TiO₂催化氯苯性能的影响[J]. 化工学报, 2020, 71(8): 3585-3593.
[9]	徐燕青, 李文飞, 吴梦瑶, 沈江南. 用于喷墨印花染料纯化的自组装GO/TiO₂复合纳滤膜的制备[J]. 化工学报, 2020, 71(3): 1352-1361.
[10]	吴娜, 董依慧, 吉晓燕, 皇甫长安, 陆小华. TiO₂纳米管阵列粗糙度调控及其与蛋白相互作用[J]. 化工学报, 2020, 71(2): 831-842.
[11]	杨霁豪,耿莉莉,叶松寿,谢建榕,张诺伟,陈秉辉. 稳定高效Ru/TiO₂-ZrO₂催化剂处理苯酚磺酸废水[J]. 化工学报, 2020, 71(12): 5561-5567.
[12]	皋海岭,徐斌,高月香,朱月明,张松贺,张毅敏. TiO₂改性石墨烯电极电吸附去除污水中NH₄⁺[J]. 化工学报, 2020, 71(11): 5309-5319.
[13]	周黄, 常禹, 范兴, 张楠楠, 陶长元. TiO₂纳米管阵列电合成的扩散-反应耦合强化机制研究[J]. 化工学报, 2020, 71(10): 4663-4673.
[14]	洪迪昆, 操政, 杨昌敏, 刘亮, 郭欣. 钙催化苯酚反应的分子动力学模拟[J]. 化工学报, 2019, 70(5): 1788-1794.
[15]	王家德, 袁通斌, 周丹飞, 周栩乐, 甘永平. 基于原位红外光谱的水相苯酚电氧化机理研究[J]. 化工学报, 2019, 70(12): 4821-4827.

煤基泡沫炭复合F-TiO₂光催化降解苯酚

Coal-based carbon foam coated with F-TiO₂ for photocatalytic degradation of phenol

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 9

参考文献 26

相关文章 15

编辑推荐 0

Metrics

本文评价