Novel mixed matrix composite membranes containing MCM-41 for CO2 separation

doi:10.11949/j.issn.0438-1157.20150257

Abstract

Abstract:

To improve the performance of CO₂ separation membrane, MCM-41 modified by amines (MCM-NH₂) was filled into polyvinylamine (PVAm) aqueous solution to fabricate PVAm-MCM-NH₂ coating solutions. PVAm-MCM-NH₂/polysulfone (PSf) mixed matrix composite membranes were prepared by coating PVAm-MCM-NH₂ solutions on PSf ultrafiltration membranes. The separation layer of the composite membrane was very thin, which benefited the improvement of CO₂ permeance. The amine groups grafted to MCM-41 facilitated the transport of CO₂ through reversible reaction and simultaneously improved the filler-polymer interface compatibility. The separation performance of PVAm-MCM-NH₂/PSf membranes with different MCM-NH₂ content was tested using CO₂/N₂ mixed gas (15% (vol) CO₂ + 85%(vol) N₂). When m_MCM-NH2/m_PVAm in the coating solution was 0.2 at testing temperature of 22℃ and feed gas pressure of 0.11 MPa, the composite membrane exhibited a CO₂ permeance of 4.66×10^-⁷ mol·m^-²·s^-¹·Pa^-¹ and a CO₂/N₂ selectivity of 150. The high-performance PVAm-MCM-NH₂/PSf membrane showed promising applications in CO₂ capture from flue gas. Moreover, the effects of the wet coating thickness, the heat treatment and the introduction of the small molecule amines on the separation performance of PVAm-MCM-NH₂/PSf membrane were investigated. The results indicated that the increase of wet coating thickness (from 50 μm to 100 μm) with heat treatment under 80℃ or the introduction of ethanediamine would lead to the improvement of the pressure stability, but the loss of CO₂/N₂ separation performance under low pressures.

Key words: mix matrix membranes, composite membranes, molecular sieves, MCM-41, flue gas, CO₂ capture

摘要：

为了提高CO₂分离膜的性能,将接枝了氨基的MCM-41分子筛(MCM-NH₂)添加到聚乙烯基胺(PVAm)水溶液中配制涂膜液,并将PVAm-MCM-NH₂涂膜液涂覆到聚砜(PSf)超滤膜上制备PVAm-MCM-NH₂/PSf混合基质复合膜。复合膜分离层较薄,有利于CO₂渗透速率的提高。接枝的胺基提高了分子筛与聚合物的相容性和膜内胺基含量,有利于膜渗透选择性能的提高。使用CO₂/N₂混合气(15% CO₂ + 85% N₂,体积分数)考察了不同MCM-NH₂添加量的PVAm-MCM-NH₂/PSf膜的渗透选择性能。当涂膜液中m_MCM-NH2/m_PVAm为0.2、湿涂层厚度为50 μm,测试温度为22℃、进料气压力为0.11 MPa时,膜的CO₂渗透速率可达4.66×10^-7 mol·m^-2·s^-1·Pa^-1,CO₂/N₂分离因子可达150。较高的CO₂/N₂分离性能表明PVAm-MCM-NH₂/PSf膜在烟道气碳捕集领域具有良好的应用前景。此外,考察了湿涂层厚度、热处理、添加小分子胺等条件对膜渗透选择性能的影响。

关键词: 混合基质膜, 复合膜, 分子筛, MCM-41, 烟道气, 二氧化碳捕集

CLC Number:

TQ028.8

HE Yupeng, WANG Zhi, QIAO Zhihua, YUAN Shuangjie, WANG Jixiao. Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation[J]. CIESC Journal, 2015, 66(10): 3979-3990.

何玉鹏, 王志, 乔志华, 远双杰, 王纪孝. 含有MCM-41分子筛的混合基质复合膜用于CO₂分离[J]. 化工学报, 2015, 66(10): 3979-3990.

References 39

[1]	Lin H, van Wagner E, Freeman B D, Toy L G, Gupta R P. Plasticization-enhanced hydrogen purification using polymeric membranes [J]. Science, 2006, 311 (5761): 639-642.
[2]	Ma Z, Qiao Z, Wang Z, Cao X, He Y, Wang J, Wang S. CO2 separation enhancement of the membrane by modifying the polymer with a small molecule containing amine and ester groups [J]. RSC Advances, 2014, 4 (41): 21313-21317.
[3]	Zhu Xiang(朱祥), Lü Wenjie(吕文杰), Hu Jun(胡军), Wang Hualin(汪华林), Liu Honglai(刘洪来). Progress in study on CO2 capture and separation by porous organic polymers [J]. CIESC Journal (化工学报), 2014, 65(5): 1553-1562.
[4]	He Wenjuan(何文娟), Wang Zhi(王志), Li Wen(李雯), Li Shichun(李诗纯), Wang Jixiao(王纪孝). Interfacially polymerized thin film composite membranes containing propylene oxide groups for CO2 separation [J]. CIESC Journal (化工学报), 2014, 65(11): 4420-4429.
[5]	Powell C E, Qiao G G. Polymeric CO2/N2 gas separation membranes for the capture of carbon dioxide from power plant flue gases [J]. J. Membr. Sci., 2006, 279(1): 1-49.
[6]	Wang Zhi(王志),Yuan Fang(袁芳),Wang Ming(王明),Wang Jixiao(王纪孝),Wang Shichang(王世昌). Membranes for carbon dioxide separation [J]. Membrane Science and Technology(膜科学与技术),2011, 31(3): 11-17.
[7]	Qiao Z, Wang Z, Zhang C, Yuan S, Zhu Y, Wang J, Wang S. PVAm-PIP/PSf composite membrane with high performance for CO2/N2 separation [J]. AIChE Journal, 2013,59 (1): 215-228.
[8]	Powell C E, Qiao G G. Polymeric CO2/N2 gas separation membranes for the capture of carbon dioxide from power plant flue gases [J]. Journal of Membrane Science, 2006,279 (1/2): 1-49.
[9]	Yang D, Wang Z, Wang J, Wang S. Potential of two-stage membrane system with recycle stream for CO2 capture from postcombustion gas [J]. Energy & Fuels, 2009,23 (10): 4755-4762.
[10]	Chung T S, Jiang L Y, Li Y, Kulprathipanja S. Mixed matrix membranes (MMMs) comprising organic polymers with dispersed inorganic fillers for gas separation [J]. Progress in Polymer Science, 2007,32 (4): 483-507.
[11]	Mahajan R, Koros W J. Factors controlling successful formation of mixed-matrix gas separation materials [J]. Industrial & Engineering Chemistry Research, 2000,39 (8): 2692-2696.
[12]	Widjojo N, Zhang S D, Chung T S, Liu Y. Enhanced gas separation performance of dual-layer hollow fiber membranes via substructure resistance reduction using mixed matrix materials [J]. Journal of Membrane Science, 2007,306 (1/2): 147-158.
[13]	Vu D Q, Koros W J, Miller S J. Mixed matrix membranes using carbon molecular sieves (Ⅰ): Preparation and experimental results [J]. Journal of Membrane Science, 2003,211: 311-334.
[14]	Ahmad A L, Jawad Z A, Low S C, Zein S H S. A cellulose acetate/multi-walled carbon nanotube mixed matrix membrane for CO2/N2 separation [J]. Journal of Membrane Science, 2014,451: 55-66.
[15]	Zhao D, Ren J, Li H, Li X, Deng M. Gas separation properties of poly(amide-6-b-ethylene oxide)/amino modified multi-walled carbon nanotubes mixed matrix membranes [J]. Journal of Membrane Science, 2014,467: 41-47.
[16]	Shahid SNijmeijer K. Performance and plasticization behavior of polymer-MOF membranes for gas separation at elevated pressures [J]. Journal of Membrane Science, 2014,470: 166-177.
[17]	Yilmaz G, Keskin S. Molecular modeling of MOF and ZIF-filled MMMs for CO2/N2 separations [J]. Journal of Membrane Science, 2014,454: 407-417
[18]	Chew T L, Ahmad A L, Bhatia S. Ordered mesoporous silica (OMS) as an adsorbent and membrane for separation of carbon dioxide (CO2) [J]. Advances in Colloid and Interface Science, 2010,153 (1/2): 43-57.
[19]	Zornoza B, Irusta S, Tellez CCoronas J. Mesoporous silica sphere-polysulfone mixed matrix membranes for gas separation [J]. Langmuir, 2009,25 (10): 5903-5909.
[20]	Zornoza B, Téllez C, Coronas J. Mixed matrix membranes comprising glassy polymers and dispersed mesoporous silica spheres for gas separation [J]. Journal of Membrane Science, 2011,368 (1/2): 100-109.
[21]	Kim S, Marand E. High permeability nano-composite membranes based on mesoporous MCM-41 nanoparticles in a polysulfone matrix [J]. Microporous and Mesoporous Materials, 2008,114 (1-3): 129-136.
[22]	Khan A L, Klaysom C, Gahlaut A, Vankelecom I F J. Polysulfone acrylate membranes containing functionalized mesoporous MCM-41 for CO2 separation [J]. Journal of Membrane Science, 2013,436: 145-153.
[23]	Wu H, Li X, Li Y, Wang S, Guo R, Jiang Z, Wu C, Xin Q, Lu X. Facilitated transport mixed matrix membranes incorporated with amine functionalized MCM-41 for enhanced gas separation properties [J]. Journal of Membrane Science, 2014,465: 78-90.
[24]	Deng L, Kim T J, Hägg M B. Facilitated transport of CO2 in novel PVAm/PVA blend membrane [J]. Journal of Membrane Science, 2009,340 (1/2): 154-163.
[25]	Yuan S, Wang Z, Qiao Z, Wang M, Wang J, Wang S. Improvement of CO2/N2 separation characteristics of polyvinylamine by modifying with ethylenediamine [J]. Journal of Membrane Science, 2011,378 (1/2): 425-437.
[26]	Klaysom C, Marschall R, Moon S H, Ladewig B P, Lu G Q M, Wang L. Preparation of porous composite ion-exchange membranes for desalination application [J]. Journal of Materials Chemistry, 2011,21 (20): 7401-7409.
[27]	Yu X, Wang Z, Wei Z, Yuan S, Zhao J, Wang J, Wang S. Novel tertiary amino containing thin film composite membranes prepared by interfacial polymerization for CO2 capture [J]. Journal of Membrane Science, 2010, 362(1): 265-278.
[28]	Zou J, Ho W S W. CO2-selective polymeric membranes containing amines in crosslinked poly(vinyl alcohol) [J]. Journal of Membrane Science, 2006,286 (1/2): 310-321.
[29]	Cai Yan(蔡彦). Study on methods and theories for improving permeance of fixed carrier facilitated transport membranes[D]. Tianjin: Tianjin University, 2008.
[30]	Wilhelm M, Jeske M, Marschall R, Cavalcanti W L, Tölle P, Köhler C, Koch D, Frauenheim T, Grathwohl G, Caro J, Wark M. New proton conducting hybrid membranes for HT-PEMFC systems based on polysiloxanes and SO3H-functionalized mesoporous Si-MCM-41 particles [J]. Journal of Membrane Science, 2008,316 (1/2): 164-175.
[31]	Kim Y C, Jeong J Y, Hwang J Y, Kim S D, Yi S C, Kim W J. Incorporation of heteropoly acid, tungstophosphoric acid within MCM-41 via impregnation and direct synthesis methods for the fabrication of composite membrane of DMFC [J]. Journal of Membrane Science, 2008,325 (1): 252-261.
[32]	Park J W, Kim Y C, Jeong Y J, Kim S D, Ha H Y, Kim W J. Effects of organo-functionalization and sulfonation of MCM-41on the proton selectivities of MCM-41/Nafion composite membranes for DMFC [J]. Microporous and Mesoporous Materials, 2008,114 (1-3): 238-249.
[33]	Bos A, Pünt I G M, Wessling M, Strathmann H. CO2-induced plasticization phenomena in glassy polymers [J]. J. Membr. Sci., 1999, 155(1): 67-78.
[34]	Zhang C, Wang Z, Cai Y, Yi C, Yang D, Yuan S. Investigation of gas permeation behavior in facilitated transport membranes: relationship between gas permeance and partial pressure [J]. Chemical Engineering Journal, 2013,225: 744-751.
[35]	Wessling M, Lidon Lopez M, Strathmann H. Accelerated plasticization of thin-film composite membranes used in gas separation [J]. Separation and Purification Technology, 2001,24 (1/2): 223-233.
[36]	Freeman B. Materials Science of Membranes for Gas and Vapor Separation[M]. Chichester, England: John Wiley & Sons, 2006,412.
[37]	Hu C C, Chang C S, Ruaan R C. Effect of free volume and sorption on membrane gas transport [J]. Journal of Membrane Science, 2003, 226(1): 51-61.
[38]	Kanehashi S, Kusakabe A, Sato S, Nagai K. Analysis of permeability; solubility and diffusivity of carbon dioxide; oxygen; and nitrogen in crystalline and liquid crystalline polymers [J]. Journal of Membrane Science, 2010,365 (1/2): 40-51.
[39]	Ismail A F, Lorna W. Suppression of plasticization in polysulfone membranes for gas separations by heat-treatment technique [J]. Separation and Purification Technology, 2003,30 (1): 37-46.

Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation

含有MCM-41分子筛的混合基质复合膜用于CO₂分离

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References 39

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Lei MAO, Guanzhang LIU, Hang YUAN, Guangya ZHANG. Efficient preparation of carbon anhydrase nanoparticles capable of capturing CO₂ and their characteristics [J]. CIESC Journal, 2023, 74(6): 2589-2598.
[2]	Hao WANG, Siyang TANG, Shan ZHONG, Bin LIANG. An investigation of the enhancing effect of solid particle surface on the CO₂ desorption behavior in chemical sorption process with MEA solution [J]. CIESC Journal, 2023, 74(4): 1539-1548.
[3]	Guohua SHI, Linshen HE, Xiling ZHAO, Shigang ZHANG. Study of removal characteristics of particulate matters within flue gas by spray tower for waste-heat recovery [J]. CIESC Journal, 2023, 74(4): 1735-1745.
[4]	Shaozhuang WANG, Dunxi YU, Jiayi LI, Jingkun HAN, Xin YU, Fangqi LIU. Effects of torrefaction with flue gas on grindability of corn stalk [J]. CIESC Journal, 2023, 74(2): 861-870.
[5]	Yingxi DANG, Peng TAN, Xiaoqin LIU, Linbing SUN. Temperature swing for CO₂ capture driven by radiative cooling and solar heating [J]. CIESC Journal, 2023, 74(1): 469-478.
[6]	Xuqing WANG, Shenglin YAN, Litao ZHU, Xibao ZHANG, Zhenghong LUO. Research progress on the mass transfer process of CO₂ absorption by amines in a packed column [J]. CIESC Journal, 2023, 74(1): 237-256.
[7]	Yujun MA, Xiangjun LIU. Theoretical studies of water recovery from flue gas by using ceramic membrane [J]. CIESC Journal, 2022, 73(9): 4103-4112.
[8]	Jiaming WANG, Xuehua RUAN, Gaohong HE. Research progress of membrane separation materials for different industrial CO₂-containing mixtures [J]. CIESC Journal, 2022, 73(8): 3417-3432.
[9]	Mai ZHANG, Yao TIAN, Zhiqi GUO, Ye WANG, Guangjin DOU, Hao SONG. Design and optimization of photocatalysis-biological hybrid system for green synthesis of fuels and chemicals [J]. CIESC Journal, 2022, 73(7): 2774-2789.
[10]	Tao ZHENG, Haiyan LIU, Rui ZHANG, Xianghai MENG, Yuanyuan YUE, Zhichang LIU. Research progress on mesoscale activation of natural aluminosilicate minerals based on green synthesis of molecular sieve [J]. CIESC Journal, 2022, 73(6): 2334-2351.
[11]	Chan WANG, Guoxi XIAO, Xiaoxue GUO, Renwei XU, Yuanyuan YUE, Xiaojun BAO. Green synthesis and application of Beta zeolite prepared via mesoscale depolymerization-reorganization strategy [J]. CIESC Journal, 2022, 73(6): 2690-2697.
[12]	Miao LI, Hong ZHAO, Biao JIANG, Siyuan CHEN, Long YAN. Thermodynamic analysis on synthesis of key intermediate BaC₂ in coal to acetylene [J]. CIESC Journal, 2022, 73(5): 1908-1919.
[13]	Chao JI, Wei LIU, Hong QI. Flue gas dehumidification through air cooling enhanced by hydrophobic ceramic membranes [J]. CIESC Journal, 2022, 73(5): 2174-2182.
[14]	Wuyu WANG, Yuzhu SHI, Long YAN, Xinghua ZHANG, Longlong MA, Qi ZHANG. Synthesis of valerate biofuels on supported Co-based bifunctional catalysts [J]. CIESC Journal, 2022, 73(2): 689-698.
[15]	Guixian LI, Ke WANG, Jian WANG, Wenliang MENG, Jingwei LI, Yong YANG, Zongliang FAN, Dongliang WANG, Huairong ZHOU. Optimal design of membrane separation process for capturing CO₂ from flue gas of coal-fired power plant [J]. CIESC Journal, 2022, 73(11): 5065-5077.