CIESC Journal ›› 2017, Vol. 68 ›› Issue (1): 320-328.DOI: 10.11949/j.issn.0438-1157.20160872

Previous Articles     Next Articles

Mulberry SCMP pulp adsorption characteristic and action mechanism of anionic groups

HU Lingyu1, YAN Zhaoqing1, LI Mingfu1, JIN Ye1, CUI Fulin1, QIN Rui1, LUO Lianxin1,2   

  1. 1 Light Industry and Food Engineering Institute, Guangxi University, Nanning 530004, Guangxi, China;
    2 Guangxi Key Laboratory of Clean Pulping and Papermaking and Pollution Control, Nanning 530004, Guangxi, China
  • Received:2016-06-27 Revised:2016-09-20 Online:2017-01-05 Published:2017-01-05
  • Contact: 10.11949/j.issn.0438-1157.20160872

桑枝SCMP浆阴离子基团的吸附过程及吸附机理

胡玲玉1, 闫兆晴1, 李明富1, 金叶1, 崔富林1, 覃睿1, 骆莲新1,2   

  1. 1 广西大学轻工与食品工程学院, 广西 南宁 530004;
    2 广西清洁化制浆造纸与污染控制重点实验室, 广西 南宁 530004
  • 通讯作者: 骆莲新
  • 基金资助:

    广西自然科学基金项目(2015GXNSFBA139038);广西清洁化制浆造纸与污染控制重点实验室项目(2013GXNSFFA019005)。

Abstract:

By the experiments of anionic groups(AGs) in the mulberry SCMP adsorption of methylene blue(MB), the results of mulberry SCMP pulp of AGs in the hydrogen peroxide(H2O2) bleaching adsorption of methylene blue(MB) were fitted by the Langmuir isotherm equation and the Freundlich isotherm equation.It showed that the mulberry SCMP adsorption process of MB conformed to the Langmuir adsorption model.The adsorption process was monolayer adsorption and non uniform adsorption coexistence of preferential adsorption.By X-ray photo-electron spectroscopy(XPS) analysis of anionic groups in pulp and surface elements and the change of species in paper pulp.H2O2 bleaching can form new SAGs and improve the pulp fiber surface sulfonation degree, while reduce the lignin content in the pulp fiber and increase the contents of cellulose and hemicellulose.

Key words: anionic groups, methylene blue, absorption thermodynamics, kinetic modeling, mechanism analysis

摘要:

通过研究桑枝SCMP浆中阴离子基团(AGs)对亚甲基蓝(MB)的吸附性能实验,运用Langmuir等温方程和Freundlich等温方程对桑枝SCMP浆H2O2漂白中AGs对亚甲基蓝(MB)的吸附结果进行拟合,表明桑枝SCMP浆对MB的吸附过程更符合Langmuir吸附模型,得出该吸附过程是单分子层吸附与非匀质吸附共存的优惠型吸附;并采用X射线光电子能谱(XPS)分析纸浆中阴离子基团和纸浆表面元素及种类的变化情况。H2O2漂白会形成新的SAGs,提高纸浆纤维表面的磺化程度,同时纸浆纤维中木素含量降低,纤维素和半纤维素含量增加。

关键词: 阴离子基团, 亚甲基蓝, 吸附热力学, 动力学模型, 机理分析