Effects of graphene oxide on electromagnetic wave absorption properties of porous silica ceramic

doi:10.3969/j.issn.0438-1157.2013.07.052

Abstract

Abstract: A particle packing method was developed to prepare porous silica ceramics aggregated by sintering silica powder with methyl cellulose as binding agent at 1300℃ for 1 h.The result of electromagnetic wave absorption showed obvious electromagnetic wave absorption properties with a bandwidth of 9 GHz and-3 dB reflectivity.The electromagnetic wave absorption properties changed after graphene oxide (GO)layers were incorporated into the samples.When the mass fraction of graphene oxide impregnated samples was 0.004%,an increase of 75% in absorption was observed with the greatest reflectivity of-5 dB.The eddy current damping caused by these GO layers was responsible for the enhanced absorption efficiency.While excess GO made the porous sample to be a reflector for incident waves.

Key words: silica, porous ceramic, electromagnetic wave absorption properties, graphene

摘要： 采用颗粒堆积法,以石英砂为骨料,甲基纤维素为黏结剂干压成型后,在1300℃保温1 h烧结制备得到SiO₂多孔陶瓷样品。通过对样品吸波性能的测试,发现样品的吸波带较宽达到9 GHz,反射率约-3 dB。经过浸渍氧化石墨烯后,样品的吸波性能发生较大改变。在氧化石墨烯质量分数为0.004%时,由于氧化石墨烯的涡流损耗,样品的吸波性能较纯SiO₂多孔陶瓷样品的吸波性能提高75%,反射率达到-5 dB。过量的氧化石墨烯使多孔陶瓷样品呈现出对电磁波的全反射。

关键词: 石英砂, 多孔陶瓷, 吸波性能, 石墨烯

CLC Number:

TQ028

ZHANG Guoying, LIANG Wenge. Effects of graphene oxide on electromagnetic wave absorption properties of porous silica ceramic[J]. CIESC Journal, 2013, 64(7): 2696-2700.

张国英, 梁文阁. 氧化石墨烯对SiO₂多孔陶瓷吸波性能的影响[J]. 化工学报, 2013, 64(7): 2696-2700.

References 22

[1]	Yusoff A N,Abdullah M H,Ahmad S H,Jusoh S F,Mansor A A,Hamid S A A.Electromagnetic and absorption properties of some microwave absorbers[J].J.Appl.Phys.,2002,92(2):876-882
[2]	Maeda T,Sugimoto S,Kagotani T,Tezuka N,Inomata K.Effect of the soft/hard exchange interaction on natural resonance frequency and electromagnetic wave absorption of the rare earth-iron-boron compounds[J].J. Magn. Magn.Mater.,2004,281(2/3):195-205
[3]	Zou Zheng(邹正),Xuan Aiguo(宣爱国),Wu Yuanxin(吴元欣),He Jun(何俊),He Jia(何佳).Preparation of nano Fe/SiO2 core-shell composite particles from copper/iron ore cinder and their microwave absorption properties[J].CIESC Journal(化工学报),2009,60(5):1322-1326
[4]	Yusoff A N,Abdullah M H.Microwave electromagnetic and absorption properties of some LiZn ferrites[J].J.Magn.Magn.Mater.,2004,269(2):271-280
[5]	Giannakopoulou T,Oikonomou A,Kordas G.Double-layer microwave absorbers based on materials with large magnetic and dielectric losses[J].J.Magn.Magn.Mater.,2004,271(2/3):224-229
[6]	Huang Dong(黄东),Qiu Tai(丘泰),Feng Yongbao(冯永宝).Electromagnetic and microwave absorbing properties of stainless steel 409L alloy microwave absorbing materials[J].Journal of Magnetic Materials and Devices (磁性材料及器件),2010,41(5):44-47
[7]	Costa A C F M,Diniz A P,Silva V J,Kiminami R H G A,Cornejo D R,Gama A M,Rezende M C,Gama L.Influence of calcination temperature on the morphology and magnetic properties of Ni-Zn ferrite applied as an electromagnetic energy absorber[J].J.Alloy Compd.,2009,483(1/2):563-565
[8]	Liu X G,Geng D Y,Zhang Z D.Microwave-absorption properties of FeCo microspheres self-assembled by Al2O3-coated FeCo nanocapsules[J].Appl.Phys.Lett.,2008,92(24):243110-243112
[9]	Wen Fusheng,Zhang Fang,Liu Zhongyuan.Investigation on microwave absorption properties for multiwalled carbon nanotubes/Fe/Co/Ni nanopowders as lightweight absorbers[J].J.Phys.Chem.C,2011,115(29):14025-14030
[10]	Yang Yi(杨毅),Liu Yongzhi(刘永峙),Li Fengsheng(李凤生),Liu Hongying(刘宏英).Preparation of nanometer NiO/Al composite particle[J].Journal of Chemical Industry and Engineering (China)(化工学报),2005,56(11):2228-2232
[11]	Ren Dengfeng(任登凤),Xuan Yimin(宣益民),Han Yuge(韩玉阁).Effect of multi-scale features on radiation property of nanoporous materials[J].CIESC Journal(化工学报),2012,63(S1):119-224
[12]	Meng Yanyan(孟琰琰),Zhang Xiong(张雄).Research on the application technology of ferrite wave-absorbing environmental materials[J].Materials Review (材料导报),2006,20(2):145-146,150
[13]	Garcia-Vidal F J,Pitarke J M,Pendry J B.Effective medium theory of the optical properties of aligned carbon nanotubes[J].Phys.Rev.Lett.,1997,78(22):4289-4291
[14]	Li Zhong(李忠),Shi Tiejun(史铁钧),Guo Liying(郭立颖).Preparation,morphology,structure and properties of fir flour/ZrO2 hybird material with interpenetrating network[J].Journal of Chemical Industry and Engineering (China)(化工学报),2008,59(11):2922-2928
[15]	Liu Xin(刘欣),Xue Xiangxin(薛向欣),Duan Peining(段培宁).Effect of pore structure on microwave absorption of porous materials[J].Journal of Materials and Metallurgy (材料与冶金学报),2007,6(4):306-310
[16]	Rao C N R,Sood A K,Subrahmanyam K S,Govindaraj A.Graphene:the new two-dimensional nanomaterial[J].Angew.Chem.Int.Ed.,2009,48(42):7752-7777
[17]	Guo Anran,Liu Jiachen,Dong Xue,Liu Mengxia. Preparation of porous silica ceramics from silica spinning solution and introduced silica particles by electrospinning[J].Materials Letters,2013,95:74-77
[18]	Chen Y J,Gao P,Zhu C L,Wang R X,Wang L J,Cao M S,Fang X Y.Synthesis,magnetic and electromagnetic wave absorption properties of porous Fe3O4/Fe/SiO2 core/shell nanorods[J].J.Appl.Phys.,2009,106(5):054303-054306
[19]	He Fuan,Fan Jintu,Ma Dong,Zhang Liming,Leung Chiwah,Chan Helen Laiwa.The attachment of Fe3O4 nanoparticles to grapheme oxide by covalent bonding[J].Carbon,2010,48(11):3139-3144
[20]	Jia Haipeng(贾海鹏),Su Xunjia(苏勋家),Hou Genliang(侯根良),Guo Feng(郭锋),Liu Zhaohui(刘朝晖),Mei Bing(梅冰).Progress of fabrication and microwave absorption capacity of grapheme/polymer nanocomposites[J].CIESC Journal(化工学报),2012,63(6):1663-1668
[21]	Sun Xin,He Jianping,Li Guoxian,Tang Jing,Wang Tao,Guo Yunxia,Xue Hairong.Laminated magnetic graphene with enhanced electromagnetic wave absorption properties[J].J.Mater.Chem.C,2013,1(4):765-777
[22]	Fang Jianjun(方建军),Li Sufang(李素芳),Cha Wenke(查文珂),Cong Hongyun(从洪云),Chen Junfang(陈俊芳).Microwave absorbing properties of nickel-coated graphene[J].Journal of Inorganic Materials (无机材料学报),2011,26(5):467-471