天然矿物共混活性焦联合低温脱硫脱硝

doi:10.11949/0438-1157.20201118

摘要/Abstract

摘要：

以P1/Ti2-15@AC天然矿物共混改性活性焦，模拟研究移动床反应器系统中活性焦联合脱硫脱硝反应过程。研究结果表明，采用新型天然矿物共混改性活性焦，结合加热再生设计，可以很好地将烟气脱硫和脱硝过程结合，从而实现高效率、低成本的一体化联合脱硫脱硝。研究表明，循环脱硫再生后P1/Ti2-15@AC-Rn的脱硝活性得到显著提升，P1/Ti2-15@AC-R1和P1/Ti2-15@AC-R2的脱硝NO转化率接近100.0%，第三次再生后降低至85.0%左右并保持基本稳定。这主要是因为脱硫再生后活性焦表面酸性C—O、C—S等酸性官能团增加，增强了脱硝时活性焦表面NH₃的吸附过程，从而提升脱硝反应效率。

关键词: 催化剂, 烟道气, 活性焦, 天然矿物, 共混, 联合脱硫脱硝

Abstract:

In this paper, P1/Ti2-15@AC natural minerals are blended to modify activated coke to simulate the combined desulfurization and denitrification reaction process of activated coke in a moving bed reactor system. The results indicate that the low-temperature, highly efficient and low-cost flue gas desulfurization and denitrification process could be well combined by the natural mineral blending modified activated coke integrate thermal regeneration method. The NO conversion of the P1/Ti2-15@AC-Rn was improved significantly after the desulfurization-regeneration process. The P1/Ti2-15@AC-R1 and P1/Ti2-15@AC-R2 had almost 100.0% NO conversion, and it kept relative stable at 85.0% after the third regeneration cycles. The enhanced NO removal performance is mainly because the acidic C—O, C—S and other acidic functional groups on the surface of activated coke increase after desulfurization regeneration, which enhances the adsorption process of NH₃on the surface of activated coke during denitration, thereby improving the efficiency of denitration reaction.

Key words: catalyst, flue gas, activated coke, natural mineral, blending modification, combined denitrification and desulfurization

中图分类号:

X 506

杨林, 孟小谜, 姚露, 赖雨果, 蒋文举. 天然矿物共混活性焦联合低温脱硫脱硝[J]. 化工学报, 2021, 72(4): 2241-2248.

YANG Lin, MENG Xiaomi, YAO Lu, LAI Yuguo, JIANG Wenju. Combined low-temperature flue gas denitrification and desulfurization over the natural mineral blending modified activated coke[J]. CIESC Journal, 2021, 72(4): 2241-2248.

参考文献 44

1	Du X, Li C, Zhao L, et al. Promotional removal of HCHO from simulated flue gas over Mn-Fe oxides modified activated coke[J]. Appl. Catal. B: Environ., 2018, 232: 37-48.
2	Wang M X, Guo Z, Huang Z H, et al. NH₃-activated carbon nanofibers for low-concentration NO removal at room temperature[J]. Catal. Commun., 2015, 62: 83-88.
3	Yang L, Jiang X, Yang Z, et al. Effect of MnSO₄ on the removal of SO₂ by manganese-modified activated coke[J]. Ind. Eng. Chem. Res., 2015, 54(5): 1689-1696.
4	Yuan J, Jiang X, Zou M, et al. Copper ore-modified activated coke: highly efficient and regenerable catalysts for the removal of SO₂[J]. Ind. Eng. Chem. Res., 2018, 57(46): 15731-15739.
5	Gao X, Liu S, Zhang Y, et al. Physicochemical properties of metal-doped activated carbons and relationship with their performance in the removal of SO₂ and NO[J]. J. Hazard. Mater., 2011, 188(1/2/3): 58-66.
6	Wang J, Yan Z, Liu L, et al. Low-temperature SCR of NO with NH₃ over activated semi-coke composite-supported rare earth oxides[J]. Appl. Surf. Sci., 2014, 309: 1-10.
7	Li J, Kobayashi N, Hu Y. A new flue gas activation process for SO₂ removal with activated coke in coal power plant[J]. J. Environ. Eng., 2007, 2(4): 740-751.
8	Jüntgen H, Richter E, Knoblauch K, et al. Catalytic NO_x reduction by ammonia on carbon catalysts[J]. Chem. Eng. Sci., 1988, 43(3): 419-428.
9	Guo Z, Xie Y, Hong I, et al. Catalytic oxidation of NO to NO₂ on activated carbon[J]. Energy Convers. Manage., 2001, 42(15): 2005-2018.
10	Yao L, Yang L, Jiang W, et al. Removal of SO₂ from flue gas on a copper modified activated coke prepared by a novel one-step carbonization activation blending method[J]. Ind. Eng. Chem. Res., 2019, 58(34): 15693-15700.
11	Zhao B, Yi H, Tang X, et al. Copper modified activated coke for mercury removal from coal-fired flue gas[J]. Chem. Eng. J., 2016, 286: 585-593.
12	Wang J, Yan Z, Liu L, et al. In situ DRIFTS investigation on the SCR of NO with NH₃ over V₂O₅ catalyst supported by activated semi-coke[J]. Appl. Surf. Sci., 2014, 313: 660-669.
13	Fan L, Chen J, Guo J, et al. Influence of manganese, iron and pyrolusite blending on the physiochemical properties and desulfurization activities of activated carbons from walnut shell[J]. J. Anal. Appl. Pyrol., 2013, 104: 353-360.
14	Belhachemi M, Rios R V R A, Addoun F, et al. Preparation of activated carbon from date pits: effect of the activation agent and liquid phase oxidation[J]. J. Anal. Appl. Pyrol., 2009, 86(1): 168-172.
15	Huang T, Li Y, Guo J, et al. Desulfurization activity of cobalt-blended into activated carbon by one-step activation method[J]. Asian J. Chem., 2014, 26(4): 1058-1062.
16	Yang L, Jiang X, Huang T, et al. Physicochemical characteristics and desulfurization activity of pyrolusite-blended activated coke[J]. Environ. Technol., 2015, 36(22): 2847-2854.
17	Wang P, Jiang X, Zhang C, et al. Desulfurization and regeneration performance of titanium ore modified activated coke[J]. Energ. Fuel., 2017, 31(5): 5266-5274.
18	Yang L, Jiang X, Jiang W, et al. Cyclic regeneration of pyrolusite-modified activated coke by blending method for flue gas desulfurization[J]. Energ. Fuel., 2017, 31(4): 4556-4564.
19	Yang L, Jiang W, Yao L, et al. Suitability of pyrolusite as additive to activated coke for low-temperature NO removal[J]. J. Chem. Technol. Biot., 2018, 93(3): 690-697.
20	Ma J, Liu Z, Liu Q, et al. SO₂and NO removal from flue gas over V₂O₅/AC at lower temperatures—role of V₂O₅ on SO₂ removal[J]. Fuel Process. Technol., 2008, 89(3): 242-248.
21	Li Y, Zhang X, Huangfu L, et al. The simultaneous removal of SO₂ and NO from flue gas over activated coke in a multi-stage fluidized bed at low temperature[J]. Fuel, 2020, 275: 117862.
22	Jung S, Oh S, Choi G, et al. Production and characterization of microporous activated carbons and metallurgical bio-coke from waste shell biomass[J]. J. Anal. Appl. Pyrol., 2014, 109: 123-131.
23	Sreńscek Nazzal J, Glonek K, Młodzik J, et al. Increase the microporosity and CO₂ adsorption of a commercial activated carbon[J]. Appl. Mech. Mater., 2015, 749: 17-21.
24	Liu Y, Qu Y, Guo J, et al. Thermal regeneration of manganese supported on activated carbons treated by HNO₃ for desulfurization[J]. Energ. Fuel., 2015, 29(3): 1931-1940.
25	谢银银. 锰系脱硝催化剂的制备及表征[D]. 重庆: 重庆大学, 2012.
	Xie Y Y. Preparation and characterization of manganese-based catalysts [D]. Chongqing: Chongqing University, 2012.
26	Yang S, Qi F, Xiong S, et al. MnO_x supported on Fe–Ti spinel: a novel Mn based low temperature SCR catalyst with a high N₂ selectivity[J]. Appl. Catal. B: Environ., 2016, 181: 570-580.
27	Zhan S, Qiu M, Yang S, et al. Facile preparation of MnO₂ doped Fe₂O₃ hollow nanofibers for low temperature SCR of NO with NH₃[J]. J. Mater. Chem. A, 2014, 2(48): 20486-20493.
28	Ţucureanu V, Matei A, Avram A M. FTIR spectroscopy for carbon family study[J]. Crit. Rev. Anal. Chem., 2016, 46(6): 502-520.
29	Teng L H, Tang T D. IR study on surface chemical properties of catalytic grown carbon nanotubes and nanofibers[J]. J. Zhejiang Univ.-Sci. A, 2008, 9(5): 720-726.
30	Liao L, Pan C. Enhanced electrochemical capacitance of nitrogen-doped carbon nanotubes synthesized from amine flames[J]. Soft Nanoscience Letters, 2011, 1(1): 16-23.
31	Mansor N A, Tessonnier J P, Rinaldi A, et al. Chemically modified multi-walled carbon nanotubes (MWCNTs) with anchored acidic groups[J]. Sains Malaysiana, 2012, 41(5): 603-609.
32	Jin R, Liu Y, Wang Y, et al. The role of cerium in the improved SO₂ tolerance for NO reduction with NH₃ over Mn-Ce/TiO₂ catalyst at low temperature[J]. Appl. Catal. B: Environ., 2014, 148: 582-588.
33	Szymański G S, Grzybek T, Papp H. Influence of nitrogen surface functionalities on the catalytic activity of activated carbon in low temperature SCR of NO_x with NH₃[J]. Catal. Today, 2004, 90(1): 51-59.
34	Rubio B, Izquierdo M T. Low cost adsorbents for low temperature cleaning of flue gases[J]. Fuel, 1998, 77(6): 631-637.
35	Wang S, Zhu Z H. Effects of acidic treatment of activated carbons on dye adsorption[J]. Dyes and Pigments, 2007, 75(2): 306-314.
36	翟润生, 蔡茂盛, Kolb D M. 硫酸溶液中Pt(111)电极面上存在SO₄^2-的XPS证据[J]. 物理化学学报, 1994, 10(8): 741-743.
	Zhai R S, Cai M S, Kolb D M. XPS evidence of sulfate anion adsorption on emersed Pt(111) in H₂SO₄ solution [J]. Acta Physico-Chimica Sinica, 1994, 10(8): 741-743.
37	David G O, Tsuji K, Shiraishi I. The reduction of gas phase air toxics from combustion and incineration sources using the MET-Mitsui-BF activated coke process[J]. Fuel Process. Technol., 2000, 65(99): 393-405.
38	Tang Q, Zhang Z G, Zhu W P, et al. SO₂ and NO selective adsorption properties of coal-based activated carbons[J]. Fuel, 2005, 84(4): 461-465.
39	许绿丝, 岑泽文, 曾汉才, 等. 活性炭纤维吸附 NO和SO₂的试验研究[J]. 华中科技大学学报(自然科学版), 2006, 34(2): 105-107.
	Xu L S, Cen Z W, Zeng H C, et al. An experimental study on the adsorption of NO and SO₂ by activated carbon fibers [J]. J. Huazhong Univ. Sci. Technol. (Natural Science Edition), 2006, 34(2): 105-107.
40	Rubel A M, Stencel J M. The effect of low-concentration SO₂ on the adsorption of NO from gas over activated carbon[J]. Fuel, 1997, 76(6): 521-526.
41	Li K, Ling L, Lu C, et al. Catalytic removal of SO₂ over ammonia-activated carbon fibers[J]. Carbon, 2001, 39(12): 1803-1808.
42	周静, 于才渊. 改性炭基催化剂低温烟气选择性还原脱硝性能研究[J]. 干燥技术与设备, 2015, 13(2): 33-38.
	Zhou J, Yu C Y. Investigation of modified carbon-based catalyst on low-temperature selective reduction of flue gas denitration performance [J]. Dry. Technol. Equip., 2015, 13(2): 33-38.
43	张翠平. SO₂对MnO_x/PG催化剂低温脱硝活性影响行为及机理研究[D]. 合肥: 合肥工业大学, 2013.
	Zhang C P. The factors and mechanism study of SO₂ influence on the denitration of MnO_x/PG catalysts at low temperature [D]. Hefei: Hefei University of Technology, 2013.
44	吕晓纬, 万亚锋, 刘波, 等. 锰前驱体对负载型氧化锰催化剂脱硝性能的影响[J]. 工业催化, 2014, 22(12): 953-957.
	Lyu X W, Wan Y F, Liu B, et al. Effects of Mn precursors on performance of supported Mn/Al₂O₃ catalysts for selective catalytic reduction of NO[J]. Industrial Catalysis, 2014, 22(12): 953-957.

[1]	杨学金, 杨金涛, 宁平, 王访, 宋晓双, 贾丽娟, 冯嘉予. 剧毒气体PH₃的干法净化技术研究进展[J]. 化工学报, 2023, 74(9): 3742-3755.
[2]	李艺彤, 郭航, 陈浩, 叶芳. 催化剂非均匀分布的质子交换膜燃料电池操作条件研究[J]. 化工学报, 2023, 74(9): 3831-3840.
[3]	陈杰, 林永胜, 肖恺, 杨臣, 邱挺. 胆碱基碱性离子液体催化合成仲丁醇性能研究[J]. 化工学报, 2023, 74(9): 3716-3730.
[4]	杨菲菲, 赵世熙, 周维, 倪中海. Sn掺杂的In₂O₃催化CO₂选择性加氢制甲醇[J]. 化工学报, 2023, 74(8): 3366-3374.
[5]	李凯旋, 谭伟, 张曼玉, 徐志豪, 王旭裕, 纪红兵. 富含零价钴活性位点的钴氮碳/活性炭设计及甲醛催化氧化应用研究[J]. 化工学报, 2023, 74(8): 3342-3352.
[6]	杨欣, 彭啸, 薛凯茹, 苏梦威, 吴燕. 分子印迹-TiO₂光电催化降解增溶PHE废水性能研究[J]. 化工学报, 2023, 74(8): 3564-3571.
[7]	余娅洁, 李静茹, 周树锋, 李清彪, 詹国武. 基于天然生物模板构建纳米材料及集成催化剂研究进展[J]. 化工学报, 2023, 74(7): 2735-2752.
[8]	李盼, 马俊洋, 陈志豪, 王丽, 郭耘. Ru/α-MnO₂催化剂形貌对NH₃-SCO反应性能的影响[J]. 化工学报, 2023, 74(7): 2908-2918.
[9]	涂玉明, 邵高燕, 陈健杰, 刘凤, 田世超, 周智勇, 任钟旗. 钙基催化剂的设计合成及应用研究进展[J]. 化工学报, 2023, 74(7): 2717-2734.
[10]	张琦钰, 高利军, 苏宇航, 马晓博, 王翊丞, 张亚婷, 胡超. 碳基催化材料在电化学还原二氧化碳中的研究进展[J]. 化工学报, 2023, 74(7): 2753-2772.
[11]	张谭, 刘光, 李晋平, 孙予罕. Ru基氮还原电催化剂性能调控策略[J]. 化工学报, 2023, 74(6): 2264-2280.
[12]	王辰, 史秀锋, 武鲜凤, 魏方佳, 张昊虹, 车寅, 吴旭. 氧化还原法制备Mn₃O₄催化剂及其甲苯催化氧化性能与机理研究[J]. 化工学报, 2023, 74(6): 2447-2457.
[13]	李勇, 高佳琦, 杜超, 赵亚丽, 李伯琼, 申倩倩, 贾虎生, 薛晋波. Ni@C@TiO₂核壳双重异质结的构筑及光热催化分解水产氢[J]. 化工学报, 2023, 74(6): 2458-2467.
[14]	周继鹏, 何文军, 李涛. 异形催化剂上乙烯催化氧化失活动力学反应工程计算[J]. 化工学报, 2023, 74(6): 2416-2426.
[15]	张希庆, 王琰婷, 徐彦红, 常淑玲, 孙婷婷, 薛定, 张立红. Mg量影响的纳米片负载Pt-In催化异丁烷脱氢性能[J]. 化工学报, 2023, 74(6): 2427-2435.