循环捕集CO2后煅烧石灰石的硫化特性

doi:10.11949/j.issn.0438-1157.20141700

摘要/Abstract

摘要： ZEC(zero emission coal)系统中,粗煤气进入碳酸化/重整炉前需先脱除H₂S,提出利用经过多次碳酸化/煅烧捕集CO₂循环的煅烧石灰石(CaO)脱除H₂S,并研究循环碳酸化/煅烧次数、硫化温度、H₂S浓度和微观结构对循环CaO硫化特性的影响。结果表明,多次循环碳酸化/煅烧捕集CO₂后CaO仍具有较高H₂S吸收性能。前20次循环,CaO硫化转化率随循环次数增加迅速降低;20次循环后,CaO硫化转化率缓慢下降。硫化120 min后,未循环CaO的硫化转化率接近100%,而经历1、20和100次循环后CaO的硫化转化率分别为94%、81%和74%。H₂S浓度对循环CaO硫化性能影响较大。硫化温度(800～1000℃)对循环CaO的硫化性能影响较小,最佳硫化温度为900℃。随循环次数增加,CaO颗粒发生高温烧结,导致比表面积降低和20～150 nm内孔隙减少,而这是与H₂S吸收密切相关的孔隙,导致CaO硫化转化率降低。

关键词: H₂S吸收, CaO, 碳酸化/煅烧, 硫化, CO₂捕集, 制氢

Abstract: Zero emission coal (ZEC) process based on calcium looping in which CO₂is captured through a cyclic carbonation/calcination process is a promising technology for hydrogen production. In this process, H₂S should be removed before raw gas flows into the downstream carbonator/reformer. In this work, the cycled CaO derived from limestone after multiple carbonation/calcination cycles for CO₂ capture was used to remove H₂S from raw gas. Cyclic carbonation/calcination of CaO was performed in a dual fixed-bed reactor and then the cycled CaO was sent to a sulfidation reactor for H₂S removal. The effects of carbonation/calcination cycle number, sulfidation temperature, H₂S concentration and CaO microstructure on sulfidation performance of the cycled CaO from CO₂ capture cycles were investigated. The cycled CaO after the long-term carbonation/calcination cycles for CO₂ capture still had high H₂S removal capacity. Sulfidation conversion of CaO derived from limestone decreased rapidly with increasing number of carbonation/calcination cycles in the first 20 cycles, and then decreased slowly with further increasing cycle number. After sulfidation for 120 min, sulfidation conversion of the CaO after 0 cycle was nearly 100%. And sulfidation conversions of the cycled CaO after 1, 20 and 100 cycles were 94%, 81% and 74%, respectively. H₂S concentration showed a great effect on H₂S removal of the cycled CaO. Sulfidation temperature in the range of 800—1000℃ had a little effect on H₂S removal of the cycled CaO, and the optimum sulfidation temperature was 900℃. As the cycle number increased, specific surface area of the cycled CaO dropped due to sintering. The pores 20—150 nm in diameter of the cycled CaO which were closely related with H₂S adsorption also decreased. Thus, H₂S removal capacity of the cycled CaO decayed with the number of cycles.

Key words: H₂S adsorption, CaO, carbonation/calcination, sulfidation, CO₂ capture, hydrogen production

中图分类号:

X701.3

吴水木, 李英杰, 孙荣岳, 路春美. 循环捕集CO₂后煅烧石灰石的硫化特性[J]. 化工学报, 2015, 66(5): 1912-1918.

WU Shuimu, LI Yingjie, SUN Rongyue, LU Chunmei. Sulfidation performance of calcined limestone from CO₂ capture cycles[J]. CIESC Journal, 2015, 66(5): 1912-1918.

参考文献 31

[1]	Blamey J, Anthony E J, Wang J, Fennell P S．The calcium looping cycle for large-scale CO2 capture [J]. Prog. Energ. Combust., 2010, 36 (2): 260-279
[2]	Chen Huichao (陈惠超), Zhao Changsui (赵长遂), Shen Peng (沈鹏). Effect of steam in flue gas on CO2 capture for calcium based sorbent [J]. CIESC Journal (化工学报), 2013, 64 (4): 1364-1372
[3]	Wu Qilong (吴琪珑), Zheng Ying (郑瑛), Luo Cong (罗聪), Ding Ning (丁宁), Bian Guan (边关), Zheng Chuguang (郑楚光). Reactivity and microstructure of synthetic CaO-based sorbents for CO2 capture [J]. CIESC Journal (化工学报), 2011, 62 (10): 2905-2913
[4]	Wang B W, Song X Y, Wang Z H, Zheng C G. Preparation and application of the sol-gel combustion synthesis-made CaO/CaZrO3 sorbent for cyclic CO2 capture through the severe calcination condition [J]. Chin. J. Chem. Eng., 2014, 22 (9): 991-999
[5]	Dean C C, Blamey J, Florin N H, Al-Jeboori M J, Fennell P S. The calcium looping cycle for CO2 capture from power generation, cement manufacture and hydogen production [J]. Chem. Eng. Res. Des., 2011, 89 (6): 836-855
[6]	Rozada B A. Post-combustion CO2 capture by Ca-looping in a 1.7 MWth pilot plant: current status and future developments//4th Intern. Workshop on Oxy-fuel FBC Technol.[C]. Nanjing, China: Southeast University, 2014
[7]	Luk H T, Lei H M, Ng W Y, Ju Y H, Lam K F. Techno-economic analysis of distributed hydrogen production from natural gas [J]. Chin. J. Chem. Eng., 2012, 20 (3): 489-496
[8]	Qiao Chunzhen (乔春珍), Xiao Yunhan (肖云汉), Yuan Kun (原鲲), Wang Feng (王峰). Impact of operation parameters on performance of “direct-coal-to-hydrogen” process [J]. Journal of Chemical Industry and Engineering (China) (化工学报), 2004, 55 (S1): 34-38
[9]	Lin S Y, Suzuki Y, Hatano H, Harada M. Hydrogen production from hydrocarbon by integration of water-carbon reaction and carbon dioxide removal (HyPr-RING method) [J]. Energy & Fuels, 2001, 15 (2): 339-343
[10]	Lin S Y, Suzuki Y, Hatano H, Harada M. Developing an innovative method, HyPr-RING, to produce hydrogen from hydrocarbons [J]. Energ. Convers. Manage., 2002, 43 (9): 1283-1290
[11]	Ziock H J, Lackner K S, Harrison D P. Zero emission coal power, a new concept [R/OL]. Los Alamos Report. LA-UR-01-2214. 2001. http://www.zeca.org/
[12]	Słowiński G. Some technical issues of zero-emission coal technology [J]. Int. J. Hydrogen Energ., 2006, 31 (8): 1091-1102
[13]	Shen Xun (沈洵). A new near zero emission coal utilization technology with combined gasification and combustion [D]. Hangzhou: Zhejiang University, 2004
[14]	Goldberg P, Chen Z Y, Connor W, Ziock H. CO2 mineral sequestration studies in US//Proc. of 1st National Conference on Carbon Sequestration [C]. Washington D C, USA, 2001
[15]	Sun P, Grace J R, Lim C J, Anthony E J. The effect of CaO sintering on cyclic CO2 capture in energy systems [J]. AIChE J., 2007, 53 (9): 2432-2442
[16]	Qiao Chunzhen (乔春珍), Wang Baoli (王宝利), Xiao Yunhan (肖云汉). Activity decline of Ca-based CO2 absorbent in repetitive calcination-carbonation [J]. CIESC Journal (化工学报), 2010, 61 (3): 720-724
[17]	Grasa G S, Abanades J C. CO2 capture capacity of CaO in long series of carbonation/calcination cycles [J]. Ind. Eng. Chem. Res., 2006, 45 (26): 8846-8851
[18]	Li Yingjie (李英杰), Sun Rongyue (孙荣岳), Liu Hongling (刘红玲), Zhao Jianli (赵建立), Han Kuihua (韩奎华), Lu Chunmei (路春美). Process analysis of cyclic CO2 capture using limestone and dolomite at high temperature [J]. CIESC Journal (化工学报), 2011, 62 (6): 1693-1700
[19]	Perdikaris N, Panopoulos K D, Fryda L, Kakaras E. Design and optimization of carbon-free power generation based on coal hydrogasification integrated with SOFC [J]. Fuel, 2009, 88 (8): 1365-1375
[20]	Fenouil L A, Lynn S. Study of calcium-based sorbents for high-temperature H2S removal (2): Kinetics of H2S sorption by calcined limestone [J]. Ind. Eng. Chem. Res., 1995, 34 (7): 2334-2342
[21]	Adánez J, de Diego L F, García-Labiano F, Abad A. Kinetics of H2S reaction with calcined calcium-based sorbents [J]. Energy & Fuels, 1998, 12 (3): 617-625
[22]	García-Labiano F, Adánez J, Abad A, de Diego L F, Gayán P. Effect of pressure on the sulfidation of calcined calcium-based sorbents [J]. Energy & Fuels, 2004, 18 (3): 761-769
[23]	Adánez J, García-Labiano F, de Diego L F, Fierro V. H2S removal in entrained flow reactors by injection of Ca-based sorbents at high temperatures [J]. Energy & Fuels, 1998, 12 (4): 726-733
[24]	García-Labiano F, de Diego L F, Adánez J. Effectiveness of natural, commercial, and modified calcium-based sorbents as H2S removal agents at high temperatures [J]. Environ. Sci. Technol., 1999, 33 (2): 288-293
[25]	Zhao Fengyun (赵风云), Zhao Hua (赵华), Zhao Ruihong (赵瑞红), Liu Runjing (刘润静), Hu Yongqi (胡永琪). Kinetics on removal of H2S and COS with CaCO3 and CaO [J]. Chemical Engineering (化学工程), 2006, 34 (12): 31-35
[26]	Lin S Y, Al-Shawabkeh A, Matsuda H, Hasatani M, Horio M. H2S reactions with limestone and calcined limestone [J]. J. Chem. Eng. Jpn., 1995, 28 (6): 708-714
[27]	Sun P, Grace J R, Lim C J, Anthony E J. Co-capture of H2S and CO2 in a pressurized-gasifier-based process [J]. Energy & Fuels, 2007, 21 (2): 836-844
[28]	Liu Yang (刘洋), Li Zhenshan (李振山), Cai Ningsheng (蔡宁生). Effect of H2S on the CO2 capture capacity of limestone in calcination/carbonation cycles [J]. Journal of Tsinghua University: Science and Technology (清华大学学报: 自然科学版), 2013, 53 (3): 342-347
[29]	Li Yingjie, Zhao Changsui, Chen Huichao. Fractal characteristics of CaO as CO2 carrier during cyclic calcination/carbonation reactions [J]. CIESC Journal (化工学报), 2009, 60 (9):2284-2291
[30]	Sun R Y, Li Y J, Liu H L, Wu S M, Lu C M. CO2 capture performance of calcium-based sorbent doped with manganese salts during calcium looping cycle [J]. Appl. Energ., 2012, 89 (1): 368-373
[31]	Borgwardt R H, Roache N F, Bruce K R. Surface area of calcium oxide and kinetics of calcium sulfide formation [J]. Environ. Prog., 1984, 3 (2): 129-135

循环捕集CO₂后煅烧石灰石的硫化特性

Sulfidation performance of calcined limestone from CO₂ capture cycles

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 31

相关文章 15

编辑推荐

Metrics

本文评价

[1]	黄琮琪, 吴一梅, 陈建业, 邵双全. 碱性电解水制氢装置热管理系统仿真研究[J]. 化工学报, 2023, 74(S1): 320-328.
[2]	周小文, 杜杰, 张战国, 许光文. 基于甲烷脉冲法的Fe₂O₃-Al₂O₃载氧体还原特性研究[J]. 化工学报, 2023, 74(6): 2611-2623.
[3]	李勇, 高佳琦, 杜超, 赵亚丽, 李伯琼, 申倩倩, 贾虎生, 薛晋波. Ni@C@TiO₂核壳双重异质结的构筑及光热催化分解水产氢[J]. 化工学报, 2023, 74(6): 2458-2467.
[4]	王承泽, 顾凯丽, 张晋华, 石建轩, 刘艺娓, 李锦祥. 硫化协同老化零价铁增效去除水中Cr（Ⅵ）的作用机制[J]. 化工学报, 2023, 74(5): 2197-2206.
[5]	白天昊, 王晓雯, 杨梦滋, 段新伟, 米杰, 武蒙蒙. 类水滑石衍生锌基氧化物高温煤气脱硫过程中COS释放行为及其抑制研究[J]. 化工学报, 2023, 74(4): 1772-1780.
[6]	张生安, 刘桂莲. 高效太阳能电解水制氢系统及其性能的多目标优化[J]. 化工学报, 2023, 74(3): 1260-1274.
[7]	宋悦, 张启成, 彭文朝, 李阳, 张凤宝, 范晓彬. MoS₂基单原子催化剂的合成及其在电催化中的应用[J]. 化工学报, 2023, 74(2): 535-545.
[8]	焦巡, 童成, 李存璞, 魏子栋. 锂硫电池的动力学调控策略[J]. 化工学报, 2023, 74(1): 170-191.
[9]	党迎喜, 谈朋, 刘晓勤, 孙林兵. 辐射冷却和太阳能加热驱动的CO₂变温捕获[J]. 化工学报, 2023, 74(1): 469-478.
[10]	鞠小兵, 李雪纯, 孙芳. 二硫代水杨酸衍生物对光固化材料性能的影响[J]. 化工学报, 2022, 73(9): 4187-4193.
[11]	戚新刚, 路利波, 陈渝楠, 葛志伟, 郭烈锦. 造纸黑液超临界水气化制氢与高附加值化学品回收研究进展[J]. 化工学报, 2022, 73(8): 3338-3354.
[12]	徐振和, 李泓江, 高雨, 礼峥, 张含烟, 徐宝彤, 丁茯, 孙亚光. In₂O₃/Ag：ZnIn₂S₄“Type Ⅱ”型异质结构材料的制备及可见光催化性能[J]. 化工学报, 2022, 73(8): 3625-3635.
[13]	彭琳, 牛明鑫, 白羽, 孙克宁. 中空硫球-MoS₂/rGO材料的制备及其在锂硫电池中的应用[J]. 化工学报, 2022, 73(8): 3688-3698.
[14]	王沛, 魏荣阔. 光热驱动多孔氧化铈热化学循环解水制氢非热质平衡模型[J]. 化工学报, 2022, 73(7): 2885-2894.
[15]	刘晓涯, 王金超, 刘莹, 马敬环. 水合肼制氢纳米催化剂改性制备及机理研究进展[J]. 化工学报, 2022, 73(7): 2819-2834.