Synthesis of polyoxymethylene dimethyl ethers from methanol and formaldehyde catalyzed by ZnCl2

SHI Midong, HE Gaoyin, DAI Fangfang, WANG Yunfang, LI Qingsong   

  1. State Key Laboratory of Heavy Oil Processing, China University of Petroleum, Qingdao 266580, Shandong, China
  • Received:2016-03-01 Revised:2016-04-25 Online:2016-07-05 Published:2016-07-05
  • Supported by:

    supported by the Postdoctoral Foundation of Qingdao (2015000111).

摘要:

聚甲氧基二甲醚(PODEn)是一种环保、友好、高效的柴油添加剂,具有非常广阔的应用前景。以甲醇与甲醛为原料,氯化锌为催化剂合成了PODEn,探讨了其合成机理,考察了反应温度、时间、催化剂用量和原料配比等条件对反应的影响,并将氯化锌、强酸性大孔树脂和氯化锌改性树脂进行比较。实验结果表明,氯化锌对甲醇和甲醛反应合成PODEn具有一定的催化活性,其较优的反应条件为:甲醇与甲醛质量比2:(3~4)、催化剂用量3.0%(质量分数)、反应温度105℃,反应时间300 min;氯化锌改性树脂具有更高的催化活性,产物含量较氯化锌提高10个百分点以上,同时降低了反应温度。

关键词: 催化剂, 聚甲氧基二甲醚, 醇, 甲醛, 合成

Abstract:

Polyoxymethylene dimethyl ethers (PODEn) are kind of diesel fuel additives with features of environment friendly and high efficiency. PODEn were catalytically synthetized from methanol and formaldehyde by ZnCl2. In this work, the mechanism of the synthesis reaction was discussed, and the effects of preparation conditions, such as temperatures, time, usage of catalyst and reactant mass ratio were investigated. The comparison of different catalysts of ZnCl2, strong acid resin and ZnCl2 modified resin was carried out. The concentrations of the PODEn compounds and methanol were quantitatively analyzed using gas chromatography (GC), and formaldehyde was also determined by chemical titration method. Sulfuric acid standard solution was used to titrate sodium hydroxide formed by reaction of formaldehyde and excessive sodium sulfite. To obtain accurate experimental data, all the experiments were conducted strictly using the following procedures: poly-formaldehyde was de-polymerized to form anhydrous formaldehyde-methanol mixture solution; reaction device was heated to reaction temperatures (80, 95, 105 and 115℃); different proportions [2:(3—4)] of the mixture solution obtained, and ZnCl2 were added into reaction vessel; then, the pressurized vessel was sealed quickly and fixed, and rotational speed of the reaction device was set for 20 r·min-1; this moment was considered as the starting time of reaction; sampling time was placed after reacting 60—360 min. Reaction mechanism of synthetising PODEn from methanol and formaldehyde catalyzed by ZnCl2 was proposed as follows: formaldehyde was polarized firstly in the presence of catalyst, the first intermediate obtained came from the reaction of formaldehyde polarized and methanol, then other intermediates and PODEn were produced from the reactions of the first intermediate and raw materials. The experimental results confirmed that ZnCl2 could be used as catalyst for synthesis of PODEn from methanol and formaldehyde. The yield and selectivity of PODE2—6 reached 19.90%, 67.50%, respectively, when the better reaction conditions were used (mass ratio of methanol and formaldehyde 2:(3—4), catalyst usage 3.0% (mass), temperature 105℃ and reaction time 300 min). Content of the products was more than 10 percentage points higher for ZnCl2 modified resin catalyst which had higher catalytic activity than for ZnCl2 catalyst.

Key words: catalyst, polyoxymethylene dimethyl ethers, alcohol, formaldehyde, synthesis