SiO2表面原位接枝聚环氧丙烷高分子刷的制备及表征

doi:10.11949/j.issn.0438-1157.20160831

化工学报 ›› 2017, Vol. 68 ›› Issue (1): 430-436.DOI: 10.11949/j.issn.0438-1157.20160831

• 材料化学工程与纳米技术 • 上一篇下一篇

SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征

曹芬^1,2, 陈可平², 田春蓉², 林晓艳¹, 梁书恩², 贾晓蓉², 王建华²

1 西南科技大学材料科学与工程学院, 四川绵阳 621010;
2 中国工程物理研究院化工材料研究所, 四川绵阳 621900

收稿日期:2016-06-20 修回日期:2016-10-13 出版日期:2017-01-05 发布日期:2017-01-05
通讯作者: 陈可平
基金资助:
国家自然科学基金项目（51273183）；国家自然科学基金委员会与中国工程物理研究院联合基金项目（U1530144）。

Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization

CAO Fen^1,2, CHEN Keping², TIAN Chunrong², LIN Xiaoyan¹, LIANG Shu'en², JIA Xiaorong², WANG Jianhua²

1 School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, Sichuan, China;
2 Institute of Chemical Materials, China Academy of Engineering Physics, Mianyang 621900, Sichuan, China

Received:2016-06-20 Revised:2016-10-13 Online:2017-01-05 Published:2017-01-05
Contact: 10.11949/j.issn.0438-1157.20160831
Supported by:
supported by the National Natural Science Foundation of China (51273183) and the Joint Fund of the National Natural Science Foundation of China and the China Academy of Engineering Physics (NSAF) (U1530144).

摘要/Abstract

摘要：

通过“Stober”法制备出单分散球形SiO₂粒子，并采用3-缩水甘油醚氧基丙基三甲氧基硅烷对其表面进行功能化修饰，然后，利用异丙醇铝作为多相催化剂，原位引发环氧丙烷（PO）单体开环聚合，制得了聚环氧丙烷（PPO）高分子刷接枝改性的SiO₂（PPO-g-SiO₂）。研究了单体添加量、反应温度及反应时间等因素对聚环氧丙烷高分子刷接枝量的影响规律。采用红外光谱（FT-IR）、X射线光电子能谱（XPS）、透射电子显微镜（TEM）、扫描电子显微镜（SEM）及热重分析（TGA）等分析方法对制备的PPO-g-SiO₂的化学结构、微观形貌以及接枝量进行了表征。结果显示，当单体添加量为2.38 mol·L^-1，反应温度为80℃，反应时间为24 h时，PPO在SiO₂表面的接枝量可达23.56%（质量分数）；其厚度约为15 nm。

关键词: 二氧化硅, 显微结构, 化学反应, 聚环氧丙烷, 开环聚合, 高分子刷

Abstract:

Monodispersed spherical SiO₂ particles were successfully prepared by Stober method, and the functional modification of SiO₂ was obtained by the reaction of Si-OH with 3-glycidoxypropyltrimethoxysilane(GPS).By using aluminum isopropoxide as a heterogeneous catalyst to initiate in-situ ring-opening polymerization of the propylene oxide(PO) monomers, a polypropylene oxide(PPO) polymer brush grafted SiO₂(PPO-g-SiO₂) was obtained.The effects of the amount of monomer, reaction temperature and reaction time on the grafted polymer brushes were discussed.In addition, the chemical structure and morphology of PPO-g-SiO₂ and grafted amount were characterized by Fourier transform infrared spectroscopy(FT-IR), X-ray photoelectron spectroscopy(XPS), transmission electron microscopy(TEM), scanning electron microscope(SEM) and thermogravimetric analysis(TGA).The results show when the amount of the monomer addition is 2.38 mol·L^-1, reaction temperature is 80℃, and reaction time is 24 h, respectively, the PPO graft quantity is up to 23.56%(mass) on SiO₂ surface and the thickness is about 15 nm.

Key words: silica, microstructure, chemical reaction, polypropylene oxide, ring-opening polymerization, polymer brushes

中图分类号:

O633.1

曹芬, 陈可平, 田春蓉, 林晓艳, 梁书恩, 贾晓蓉, 王建华. SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征[J]. 化工学报, 2017, 68(1): 430-436.

CAO Fen, CHEN Keping, TIAN Chunrong, LIN Xiaoyan, LIANG Shu'en, JIA Xiaorong, WANG Jianhua. Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization[J]. CIESC Journal, 2017, 68(1): 430-436.

参考文献 23

[1]	DA CRUZ A G B, WARDELL J L, ROCCO A M. Hybrid organic-inorganic materials based on polypyrrole and 1, 3-dithiole-2-thione-4, 5-dithiolate (DMIT) containing dianions[J]. Journal of Materials Science, 2008, 43(17):5823-5836.
[2]	SAMUNEVA B, KABAIVANOVA L, CHERNEV G, et al. Sol-gel synthesis and structure of silica hybrid materials[J]. Journal of Sol-Gel Science and Technology, 2008, 48(1/2):73-79.
[3]	聂飞, 贺高红, 赵薇, 等. 疏水SiO2/PTFPMS杂化复合膜的制备及其气体分离性能[J]. 化工学报, 2014, 65(8):3019-3025. NIE F, HE G H, ZHAO W, et al. Preparation and gas separation performance of hydrophobic SiO2/PTFPMS hybrid composite membrane[J]. CIESC Journal, 2014, 65(8):3019-3025.
[4]	GIANNELIS E, KRISHNAMOORTI R, MANIAS E. Polymer-Silicate Nanocomposites:Model Systems For Confined Polymers and Polymer Brushes[M]//GRANICK S, BINDER K, DE GENNES P-G, et al. Polymers in Confined Environments. Berlin:Springer Berlin Heidelberg, 1999:107-147.
[5]	AYRES N. Polymer brushes:applications in biomaterials and nanotechnology[J]. Polymer Chemistry, 2010, 1(6):769-777.
[6]	MILNER S. Polymer brushes[J]. Science, 1991, 251(4996):905-914.
[7]	EJAZ M, YAMAMOTO S, OHNO K, et al. Controlled graft polymerization of methyl methacrylate on silicon substrate by the combined use of the Langmuir-Blodgett and atom transfer radical polymerization techniques[J]. Macromolecules, 1998, 31(17):5934-5936.
[8]	HUANG X, WIRTH M. Surface initiation of living radical polymerization for growth of tethered chains of low polydispersity[J]. Macromolecules, 1999, 32(5):1694-1696.
[9]	HUSSEMAN M, MALMSTR M E E, MCNAMARA M, et al. Controlled synthesis of polymer brushes by "living" free radical polymerization techniques[J]. Macromolecules, 1999, 32(5):1424-1431.
[10]	ZHAO B, BRITTAIN W J. Synthesis of tethered polystyrene-block-poly (methyl methacrylate) monolayer on a silicate substrate by sequential carbocationic polymerization and atom transfer radical polymerization[J]. Journal of the American Chemical Society, 1999, 121(14):3557-3558.
[11]	史博, 梁亮. 高分子刷表面修饰SiO2颗粒的研究进展及发展建议[J]. 高分子通报, 2011, (3):94-98. SHI B, LIANG L. Research progress and advice in polymer brushes constructed on silica particles[J]. Polymer Bulletin, 2011, (3):94-98.
[12]	姚灏, 田威, 白阳, 等. 聚合物分子刷的研究进展[J]. 应用化工, 2013, 42(3):510-516. YAO H, TIAN W, BAI Y, et al. Progress in polymer molecular brushes[J]. Applied Chemical Industry, 2013, 42(3):510-516.
[13]	KHAN M, HUCK W T. Hyperbranched polyglycidol on Si/SiO2 surfaces via surface-initiated polymerization[J]. Macromolecules, 2003, 36(14):5088-5093.
[14]	LEE S H, DREYER D R, AN J, et al. Polymer brushes via controlled, surface-initiated atom transfer radical polymerization (ATRP) from graphene oxide[J]. Macromolecular Rapid Communications, 2010, 31(3):281-288.
[15]	唐龙祥, 石洪莹, 刘春华, 等. 原子转移自由基聚合法在纳米SiO2表面接枝PS及其对SBS的改性[J]. 高分子材料科学与工程, 2013, 29(8):97-100. TANG L X, SHI H Y, LIU C H, et al. Grafting PS onto surfaces of nanosilica via ATRP reaction and modification to SBS[J]. Polymer Materials and Engineering, 2013, 29(8):97-100.
[16]	任骏. 表面引发活性聚合SiO2/PMMA核壳复合纳米粒子的制备及表征[J]. 胶体与聚合物, 2011, 29(4):147-153. REN J. Synthesis and Characterisation of SiO2-PMMA core/shell composite nanoparticles via surface-initiated living radical polymerisation[J]. Chinese Journal of Colloid & Polymer, 2011, 29(4):147-153.
[17]	JOUBERT M, DELAITE C, BOURGEAT-LAMI E, et al. Hairy PEO-silica nanoparticles through surface-initiated polymerization of ethylene oxide[J]. Macromolecular Rapid Communications, 2005, 26(8):602-607.
[18]	高霞, 陈可平, 王建华, 等. 纳米SiO2表面接枝聚环氧丙醇及其对聚氨酯泡沫力学性能的影响[J]. 西南科技大学学报, 2015, 30(2):17-22. GAO X, CHEN K P, WANG J H, et al. Nano-silica grafted with polyglycidol and its influence on the mechanical properties of polyurethane foam (PUF)[J]. Journal of Southwest University of Science and Technology, 2015, 30(2):17-22.
[19]	王芳辉, 朱红, 朱捷. 环氧丙烷接枝聚合改性超细二氧化硅的研究[J]. 现代化工, 2007, 27(10):38-40. WANG F H, ZHU H, ZHU J. Study on modification of ultrafine silicon dioxide directly with propylene oxide by graft polymerization[J]. Modern Chemical Industry, 2007, 27(10):38-40.
[20]	FENG L B, WANG Y L, WANG N, et al. Preparation of poly(ethylene glycol)-grafted silica nanoparticles using a facile esterification condensation method[J]. Polymer Bulletin, 2009, (63):313-327.
[21]	张治国, 尹红. 环氧乙烷环氧丙烷开环聚合反应动力学研究[J]. 化学进展, 2007, 4(4):575-576. ZHANG Z G, YIN H. Ring-opening polymerization of ethylene oxide and propylene oxide[J]. Progress in Chemistry, 2007, 4(4):575-576.
[22]	JOUBERT M, DELAITE C, BOURGEAT-LAMI E, et al. Ring-opening polymerization of ε-caprolactone and L-lactide from silica nanoparticles surface[J]. Journal of Polymer Science Part A:Polymer Chemistry, 2004, 42(8):1976-1984.
[23]	郭兴忠, 杨辉, 王建武, 等. 聚乙二醇表面改性SiC粉体的物性表征[J]. 材料工程, 2004, (3):7-10. GUO X Z, YANG H, WANG J W, et al. The material properties characterization of SiC powder surface-modified by polyethylene glycol[J]. Materials Engineering, 2004, (3):7-10.

SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征

Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 23

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈美思, 陈威达, 李鑫垚, 李尚予, 吴有庭, 张锋, 张志炳. 硅基离子液体微颗粒强化气体捕集与转化的研究进展[J]. 化工学报, 2023, 74(9): 3628-3639.
[2]	陈杰, 林永胜, 肖恺, 杨臣, 邱挺. 胆碱基碱性离子液体催化合成仲丁醇性能研究[J]. 化工学报, 2023, 74(9): 3716-3730.
[3]	何晓崐, 刘锐, 薛园, 左然. MOCVD生长AlN单晶薄膜的气相和表面化学反应综述[J]. 化工学报, 2023, 74(7): 2800-2813.
[4]	刘春雨, 周桓宇, 马跃, 岳长涛. CaO调质含油污泥干燥特性及数学模型[J]. 化工学报, 2023, 74(7): 3018-3027.
[5]	张全碧, 羊依金, 郭旭晶. 芬顿氧化法对利福平制药废水中溶解性有机物的催化降解[J]. 化工学报, 2023, 74(5): 2217-2227.
[6]	葛运通, 王玮, 李楷, 肖帆, 于志鹏, 宫敬. 多相分散体系中微油滴与改性二氧化硅表面间作用力的AFM研究[J]. 化工学报, 2023, 74(4): 1651-1659.
[7]	任金胜, 刘克润, 焦志伟, 刘家祥, 于源. 涡流空气分级机近导叶处团聚体解团机理研究[J]. 化工学报, 2023, 74(4): 1528-1538.
[8]	禹进, 余彬彬, 蒋新生. 一种基于虚拟组分的燃烧调控化学作用量化及分析方法研究[J]. 化工学报, 2023, 74(3): 1303-1312.
[9]	张雪婷, 胡激江, 赵晶, 李伯耿. 高分子量聚丙二醇在微通道反应器中的制备[J]. 化工学报, 2023, 74(3): 1343-1351.
[10]	郭祥, 乔金硕, 王振华, 孙旺, 孙克宁. 碳燃料固体氧化物燃料电池结构研究进展[J]. 化工学报, 2023, 74(1): 290-302.
[11]	戴文华, 辛忠. Si掺杂对Cu/ZrO₂催化CO₂加氢制甲醇性能的影响[J]. 化工学报, 2022, 73(8): 3586-3596.
[12]	张鑫, 许蕊, 路馨语, 牛永安. SiO₂@BiOCl-Bi₂₄O₃₁Cl₁₀核壳微球的合成及光催化[J]. 化工学报, 2022, 73(8): 3636-3646.
[13]	郑默, 李晓霞. ReaxFF MD模拟揭示的煤热解挥发分自由基反应的竞争与协调[J]. 化工学报, 2022, 73(6): 2732-2741.
[14]	李岩, 田阿慧, 周毅. 反应性双射流中标量输运和化学反应特性[J]. 化工学报, 2022, 73(5): 1947-1963.
[15]	余彬彬, 蒋新生, 禹进, 蔡运雄, 李玉玺, 何东海, 于佳佳. 全氟己酮抑制航空煤油燃烧实验及化学动力学研究[J]. 化工学报, 2022, 73(4): 1834-1844.