可溶磷对常压水热法制备高强α-半水石膏的影响

doi:10.11949/j.issn.0438-1157.20141449

化工学报 ›› 2015, Vol. 66 ›› Issue (5): 1983-1988.DOI: 10.11949/j.issn.0438-1157.20141449

• 材料化学工程与纳米技术 • 上一篇下一篇

可溶磷对常压水热法制备高强α-半水石膏的影响

茹晓红¹, 李海涛¹, 张新爱¹, 马保国², 卢斯文²

1 洛阳理工学院材料科学与工程系, 河南洛阳 471023;
2 武汉理工大学硅酸盐建筑材料国家重点实验室, 湖北武汉 430070

收稿日期:2014-09-24 修回日期:2015-02-25 出版日期:2015-05-05 发布日期:2015-05-05
通讯作者: 茹晓红

Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method

RU Xiaohong¹, LI Haitao¹, ZHANG Xin'ai¹, MA Baoguo², LU Siwen²

1 Department of Materials Science and Engineering, Luoyang Institute of Science and Technology, Luoyang 471023, Henan, China;
2 State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, Hubei, China

Received:2014-09-24 Revised:2015-02-25 Online:2015-05-05 Published:2015-05-05

摘要/Abstract

摘要： 研究了水热CaCl₂溶液中可溶磷对CaSO₄·2H₂O脱水形成α-半水石膏相以及晶形调控的影响,并从高强α-半水石膏相的晶体生长角度探讨了可溶磷的作用机理。结果表明:在98℃ 24%的水热CaCl₂溶液中,pH 的大小是决定二水石膏能否发生脱水相变反应形成α-半水石膏的主要因素;当pH不超过2.0时,可以得到针状的α-半水石膏,加入多元羧酸类媒晶剂NS后,可以得到长径比0.5～3.0的短柱状高强α-半水石膏,抗压强度超过20 MPa;可溶磷的存在可以降低体系的pH,增大α-半水石膏的过饱和度,降低晶体与液相界面的表面自由能,有利于α-HH相的形成;另一方面,酸根离子会影响到α-HH的结晶习性,减弱羧酸类媒晶剂的吸附效果。

关键词: 可溶磷, 水热, 相变, 制备, 高强a-半水石膏

Abstract: The effect of soluble phosphorus on CaSO₄·2H₂O (DH) dehydration to α-calcium sulfate hemihydrate gypsum (α-HH) in hydrothermal CaCl₂ solutions and the crystal shape regulation were investigated. The action mechanism of soluble phosphorus was studied by means of growth of hemihydrate crystal. The system pH was the main factor to determine whether DH could be dehydrated to α-HH in 24% CaCl₂ solution at 98℃. Acicular a-HH crystal could be obtained when pH was less than 2.0. High-strength α-HH crystal with aspect ratios from 0.5 to 3.0 could be observed when polycarboxylic crystal habit modifier NS was added. The corresponding compressive strength was more than 20 MPa. The presence of soluble phosphorus was favorable for α-HH formation by lowering system pH, increasing supersaturation degree and reducing interfacial energy. On the other hand, acid radical ions affected α-HH crystallization behavior and adsorption results of medium crystal agent NS.

Key words: soluble phosphorus, hydrothermal, phase change, preparation, high-strength a-hemihydrates gypsum

中图分类号:

TQ177.3

茹晓红, 李海涛, 张新爱, 马保国, 卢斯文. 可溶磷对常压水热法制备高强α-半水石膏的影响[J]. 化工学报, 2015, 66(5): 1983-1988.

RU Xiaohong, LI Haitao, ZHANG Xin'ai, MA Baoguo, LU Siwen. Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method[J]. CIESC Journal, 2015, 66(5): 1983-1988.

参考文献 20

[1]	Chen Yan(陈燕), Yue Wenhai(岳文海), Dong Ruolan(董若兰). Gypsum Building Materials(石膏建筑材料) [M].Beijing: Building Materials Industry Press, 2012: 179-210
[2]	Ma Baoguo(马保国), Ru Xiaohong(茹晓红), Zou Kaibo (邹开波), et al. Preparation of α-calcium sulfate hemihydrate from phosphogypsum in Ca-Na-Cl solutions under atmospheric pressure [J]. CIESC Journal(化工学报), 2013, 64(7): 2701-2707
[3]	Ru Xiaohong(茹晓红). Processing theory and application technology research of phosphogypsum based gypsum plaster[D]. Wuhan: Wuhan University of Technology, 2013:51-107
[4]	Peng Jiahui(彭家惠), Peng Zhihui(彭志辉), Zhang Jianxin(张建新), et al. Study on the form and distribution of water-soluble P2O5 in phosphogypsum and effective mechanism of properties [J]. J. Chin. Ceram. Soc.(硅酸盐学报), 2000, 28(4): 309-313
[5]	Manjit S. Role of phosphogypsum impurities on strength and microstructure of selenite plaster [J]. Constr. Build. Mater., 2005, 19: 480-486
[6]	Lu Jinchi(陆金驰), Li Dongnan(李东南), Chen Kai(陈凯), et al. Effect of calcined phosphogypsum on hydration process of autoclaved silicate products [J]. CIESC Journal(化工学报), 2012, 63(7): 2317-2323
[7]	Kubota N, Mullin J W.A kinetic model for crystal growth from aqueous solution in the presence of impurity [J]. J. Cryst. Growth, 1995, 152:203-208
[8]	Guan Baohong, Yang Liuchun, Wu Zhongbiao. Preparation of alpha-calcium sulfate hemihydrate form FGD gypsum in K Mg containing concentrated CaCl2 solution under mild conditions [J]. Fuel, 2009, 88: 1286-1293
[9]	Alfred Z, Ivan O, Felicia T, et al. Autoclave-free formation of α-hemihydrate gypsum [J]. J. Am. Ceram. Soc., 1991, 74(5): 1117-1124
[10]	Thomas F, Demopoulos G P. The crystal growth kinetics of alpha calcium sulfate hemihydrate in concentrated CaCl2-HCl solutions [J]. J. Cryst. Growth, 2012, 351: 9-18
[11]	Li Zhibao, Demopoulos G P.Solubility of CaSO4 phase in aqueous HCl+CaCl2 solutions from 283K to 353K [J]. J. Chem. Eng. Data, 2005, 50:1971-1982
[12]	Thomas F, Demopoulos G P. Phase transformation kinetics of calcium sulfate phases in strong CaCl2-HCl solutions [J]. Hydrometallurgy, 2012, 129/130:126-134
[13]	Söhnel O, Mullin J W.Interpretation of crystallization induction period [J]. J. Colloid Interface Sci., 1998, 123: 43-50
[14]	Wang Zehong(王泽红), Qiao Jinghui(乔景慧), Han Yuexin(韩跃新), et al. Effect of pH value on calcium sulfate whiskers [J]. Metal Mine(金属矿山), 2004, 340(10):39-42
[15]	El-Shall H, Rashad M M, Abdel-Aal E A. Effect of cetyl pyridinium chloride additive on crystallization of gypsum in phosphoric and sulfuric acids medium [J]. Crystal Research and Technology, 2005, 40(9): 860-866
[16]	Marina P, Emilia O, Amedeo L, et al.Gypsum precipitation from an aqueous solution in the presence of ntrilotrimethylene phosphonic acid [J]. Industrial and Engineering Chemistry Research, 2006, 45(6): 2070-2076
[17]	Li Jun(李军), Wang Jianhua(王建华), Zhang Yunxiang(张允湘). Effect of fluorine, aluminium and silicon on the crystallization of gypsum [J]. J. Chem. Eng. Chinese Univ. (高校化学工程学报), 1997, 11(2): 45-51
[18]	Bai Yang(白杨), Li Xudong(李旭东). Medium crystal agent in high-strength gypsum with flue gas desulphurization gypsum [J]. J. Chin. Ceram. Soc.(硅酸盐学报), 2009, 37(7): 1142-1146
[19]	Liu Hongxia(刘红霞), Peng Jiahui(彭家惠), Qu Jindong(瞿金东), et al. Effect of citric acid on crystal morphology of a-hemihydrates gypsum and the impact of solution pH value [J].Bulletin of the Chinese Ceramic Society(硅酸盐通报), 2010, 29(3):518-523
[20]	Guan Baohong, Shen Zhuoxian, Wu Zhongbiao, et al. Effect of pH on the preparation of α-calcium sulfate hemihydrate from FGD gypsum with the hydrothermal method [J]. J. Am. Ceram. Soc., 2008, 91(12): 546-566

可溶磷对常压水热法制备高强α-半水石膏的影响

Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 20

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张双星, 刘舫辰, 张义飞, 杜文静. R-134a脉动热管相变蓄放热实验研究[J]. 化工学报, 2023, 74(S1): 165-171.
[2]	江河, 袁俊飞, 王林, 邢谷雨. 均流腔结构对微细通道内相变流动特性影响的实验研究[J]. 化工学报, 2023, 74(S1): 235-244.
[3]	吴延鹏, 刘乾隆, 田东民, 陈凤君. 相变材料与热管耦合的电子器件热管理研究进展[J]. 化工学报, 2023, 74(S1): 25-31.
[4]	史昊鹏, 钟达文, 廉学新, 张君峰. 朝下多尺度沟槽翅片结构表面沸腾换热实验研究[J]. 化工学报, 2023, 74(7): 2880-2888.
[5]	史方哲, 甘云华. 超薄热管启动特性和传热性能数值模拟[J]. 化工学报, 2023, 74(7): 2814-2823.
[6]	吴文涛, 褚良永, 张玲洁, 谭伟民, 沈丽明, 暴宁钟. 腰果酚生物基自愈合微胶囊的高效制备工艺研究[J]. 化工学报, 2023, 74(7): 3103-3115.
[7]	邢美波, 张中天, 景栋梁, 张洪发. 磁调控水基碳纳米管协同多孔材料强化相变储/释能特性[J]. 化工学报, 2023, 74(7): 3093-3102.
[8]	王志龙, 杨烨, 赵真真, 田涛, 赵桐, 崔亚辉. 搅拌时间和混合顺序对锂离子电池正极浆料分散特性的影响[J]. 化工学报, 2023, 74(7): 3127-3138.
[9]	张贲, 王松柏, 魏子亚, 郝婷婷, 马学虎, 温荣福. 超亲水多孔金属结构驱动的毛细液膜冷凝及传热强化[J]. 化工学报, 2023, 74(7): 2824-2835.
[10]	朱风, 陈凯琳, 黄小凤, 鲍银珠, 李文斌, 刘嘉鑫, 吴玮强, 高王伟. KOH改性电石渣脱除羰基硫的性能研究[J]. 化工学报, 2023, 74(6): 2668-2679.
[11]	李振, 张博, 王丽伟. PEG-EG固-固相变材料的制备和性能研究[J]. 化工学报, 2023, 74(6): 2680-2688.
[12]	代佳琳, 毕唯东, 雍玉梅, 陈文强, 莫晗旸, 孙兵, 杨超. 热物性对混合型CPCMs固液相变特性影响模拟研究[J]. 化工学报, 2023, 74(5): 1914-1927.
[13]	吴学红, 栾林林, 陈亚南, 赵敏, 吕财, 刘勇. 可降解柔性相变薄膜的制备及其热性能[J]. 化工学报, 2023, 74(4): 1818-1826.
[14]	杨灿, 孙雪琦, 尚明华, 张建, 张香平, 曾少娟. 相变离子液体体系吸收分离CO₂的研究现状及展望[J]. 化工学报, 2023, 74(4): 1419-1432.
[15]	李明川, 樊栓狮, 徐赋海, 卢惠东, 李晓军. 水合物热分解Stefan相变模型解的存在性及Laplace变换求解[J]. 化工学报, 2023, 74(4): 1746-1754.