Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels

doi:10.11949/j.issn.0438-1157.20150600

Abstract

Abstract:

Flexible silica aerogels with super-hydrophobicity and elasticity were successfully prepared via acid-base two-step sol-gel method, followed by supercritical drying process. They were synthesized with tetraethoxysilane (TEOS) and methyltrimethoxysilane (MTMS) as coprecursors, methyl alcohol as solvent and cetyl trimethyl ammonium bromide (CTAB) as surfactant. The influence of acid-base catalysts concentration on silica aerogels was studied in detail. Aerogels prepared with higher base concentration and lower acid concentration were found to have more uniform pore structures and narrower pore size distributions. It was observed that the optimum aerogels can be obtained with 0.01 mol·L^-1 oxalic acid and 5 mol·L^-1 ammonia as acid-base catalysts, respectively. The density of the as-prepared aerogel was as low as 0.135 g·cm^-3, the porosity was around 93% and the specific surface area was as high as 807 m²·g^-1. The maximum compression ratio of the aerogel was as high as 60% with 100% compression resilience ratio.

Key words: silica, supercritical drying, surfactants, catalyst, elasticity

摘要：

以甲基三甲氧基硅烷(MTMS)和正硅酸乙酯(TEOS)作为混合硅源,甲醇为溶剂,十六烷基三甲基溴化铵(CTAB)为表面活性剂,通过酸碱两步催化溶胶凝胶法制备醇凝胶,经超临界干燥可以制备高弹性疏水块状硅气凝胶。分别采用0.1 mol·L^-1 和0.01 mol·L^-1 的草酸作为酸催化剂,5 mol·L^-1 和10 mol·L^-1 的氨水作为碱催化剂,研究不同酸碱催化剂浓度对其网络结构的影响。发现高浓度酸和高浓度碱以及低浓度酸和低浓度碱作为催化剂合成的硅气凝胶的网络结构更加均匀,孔径分布更窄。其中,在草酸浓度为0.01 mol·L^-1、氨水浓度为5mol·L^-1 时,所得硅气凝胶密度为0.135 g·cm^-3、比表面积为807 m²·g^-1、孔隙率约为93%,凝胶最大可压缩至其起始长度的60%,压缩回弹率为100%。

关键词: 二氧化硅, 超临界干燥, 表面活性剂, 催化剂, 弹性

CLC Number:

TQ328.9

CAI Long, PU Qun, QU Kang, SHAN Guorong. Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels[J]. CIESC Journal, 2016, 67(2): 648-653.

蔡龙, 浦群, 曲康, 单国荣. 酸碱催化剂浓度对柔性硅气凝胶性能和结构的影响[J]. 化工学报, 2016, 67(2): 648-653.

References 22

[1]	段远源, 林杰, 王晓东, 等. 二氧化硅气凝胶的气相热导率模型分析[J]. 化工学报, 2012, 63(S1):54-58. DOI:10.3969/j.issn. 0438-1157. 2012.zl.011. DUAN Y Y, LIN J, WANG X D, et al. Analysis of gaseous thermal conductivity models for silica aerogel[J]. CIESC Journal, 2012, 63(S1):54-58. DOI:10.3969/j.issn.0438-1157.2012.zl.011.
[2]	何方, 吴菊英, 黃渝鸿, 等. 影响二氧化硅气凝胶隔热涂料热导率的因素[J]. 化工进展, 2014, 33(8):2134-2139. DOI:10.3969/j.issn. 1000-6613.2014.08.032. HE F, WU J Y, HUANG Y H, et al. Effect of contents and sizes on the thermal conductivity of silica aerogel thermal insulation coatings[J]. Chemical Industry and Engineering Progress, 2014, 33(8):2134-2139. DOI:10.3969/j.issn.1000-6613.2014.08.032.
[3]	GIBIAT V, LEFEUVRE O, WOIGNIER T, et al. Acoustic properties and potential applications of silica aerogels[J]. Journal of Non-Crystalline Solids, 1995, 186:244-255. DOI:10.1016/0022-3093(95)00049-6.
[4]	YU K M K, YEUNG C M Y, THOMPSETT D, et al. Aerogel-coated metal nanoparticle colloids as novel entities for the synthesis of defined supported metal catalysts[J]. The Journal of Physical Chemistry B, 2003, 107(19):4515-4526. DOI:10.1021/jp0275239.
[5]	STANDEKER S, NOVAK Z, KNEZ Z. Adsorption of toxic organic compounds from water with hydrophobic silica aerogels[J]. Journal of Colloid and Interface Science, 2007, 310(2):362-368. DOI:10.1016/j.jcis.2007.02.021.
[6]	曲康, 浦群, 单国荣. 有机-无机杂化柔性硅气凝胶的制备与表征[J]. 化工学报, 2014, 65(1):346-351. DOI:10.3969/j.issn. 0438-1157. 2014.01.045. QU K, PU Q, SHAN G R. Preparation and characterization of organic-inorganic hybrid flexible silica aerogel[J]. CIESC Journal, 2014, 65(1):346-351. DOI:10.3969/j.issn.0438-1157.2014.01.045.
[7]	UNLUSU B, SUNOL A K, SUNOL S G. Stress formation during heating in supercritical drying[J]. Journal of Non-Crystalline Solids, 2001, 279(2):110-118. DOI:10.1016/S0022-3093(00)00398-7.
[8]	ECONOMOPOULOS E, IOANNIDES T. Synthesis of transparent silica aerogels using tetraalkylammonium fluoride catalysts[J]. Journal of Sol-Gel Science and Technology, 2009, 49(3):347-354. DOI:10.1007/s10971-008-1878-x.
[9]	MATYJASZEWSKI K. Atom transfer radical polymerization (ATRP):current status and future perspectives[J]. Macromolecules, 2012, 45(10):4015-4039. DOI:10.1021/ma3001719
[10]	吴国友, 程璇, 余煜玺, 等. 甲基三甲氧基硅烷对块状SiO2气凝胶性能和结构的影响[J]. 化学进展, 2010, 22(10):1892-1900. WU G Y, CHENG X, YU Y X, et al. Preparation of silica aerogels via ambient pressure drying[J]. Progress in Chemistry, 2010, 22(10):1892-1900.
[11]	MEADOR M A B, SCHERZER C M, VIVOD S L, et al. Epoxy reinforced aerogels made using a streamlined process[J]. ACS Applied Materials & Interfaces, 2010, 2(7):2162-2168. DOI:10.1021/am100422x.
[12]	NGUYEN B N, MEADOR M A B, TOUSLEY M E, et al. Tailoring elastic properties of silica aerogels cross-linked with polystyrene[J]. ACS Applied Materials & Interfaces, 2009, 1(3):621-630. DOI:10.1021/am8001617.
[13]	LIU C, PAN C. Grafting polystyrene onto silica nanoparticles via RAFT polymerization[J]. Polymer, 2007, 48(13):3679-3685. DOI:10.1016/j.polymer.2007.04.055.
[14]	CAI J, LIU S, FENG J, et al. Cellulose-silica nanocomposite aerogels by in-situ formation of silica in cellulose gel[J]. Angewandte Chemie International Edition, 2012, 51(9):2076-2079. DOI:10.1002/anie. 201105730.
[15]	LIAO Y, WU H, DING Y, et al. Engineering thermal and mechanical properties of flexible fiber-reinforced aerogel composites[J]. Journal of Sol-Gel Science and Technology, 2012, 63(3):445-456. DOI:10.1007/s10971-012-2806-7.
[16]	YUAN B, DING S, WANG D, et al. Heat insulation properties of silica aerogel/glass fiber composites fabricated by press forming[J]. Materials Letters, 2012, 75:204-206. DOI:10.1016/j.matlet. 2012.01.114.
[17]	SARAWADE P B, KIM J, KIM H, et al. High specific surface area TEOS-based aerogels with large pore volume prepared at an ambient pressure[J]. Applied Surface Science, 2007, 254(2):574-579. DOI:10.1016/j.apsusc.2007.06.063.
[18]	RAO A V, BHAGAT S D, HIRASHIMA H, et al. Synthesis of flexible silica aerogels using methyltrimethoxysilane (MTMS) precursor[J]. Journal of Colloid and Interface Science, 2006, 300(1):279-285. DOI:10.1016/j.jcis.2006.03.044.
[19]	NADARGI D Y, RAO A V. Methyltriethoxysilane:new precursor for synthesizing silica aerogels[J]. Journal of Alloys and Compounds, 2009, 467(1/2):397-404. DOI:10.1016/j.jallcom.2007.12.019.
[20]	RAO A V, PAJONK G M. Effect of methyltrimethoxysilane as a co-precursor on the optical properties of silica aerogels[J]. Journal of Non-Crystalline Solids, 2001, 285(1):202-209. DOI:10.1016/S0022-3093(01)00454-9.
[21]	NADARGI D Y, LATTHE S S, HIRASHIMA H, et al. Studies on rheological properties of methyltriethoxysilane (MTES) based flexible superhydrophobic silica aerogels[J]. Microporous and Mesoporous Materials, 2009, 117(3):617-626. DOI:10.1016/j. micromeso. 2008.08.025.
[22]	YU Y, WU X, GUO D, et al. Preparation of flexible, hydrophobic, and oleophilic silica aerogels based on a methyltriethoxysilane precursor[J]. Journal of Materials Science, 2014, 49(22):7715-7722. DOI:10.1007/s10853-014-8480-0.