Optimization of Ni-P/APO-11 amorphous catalyst for catalytic hydrogenation of turpentine using response surface methodology

doi:10.11949/j.issn.0438-1157.20161534

Abstract

Abstract:

APO-11 aluminophosphate molecular sieve was prepared from diisopropylamine and calmogastrin by hydrothermal synthesis method. The amorphous catalysts Ni-P/APO-11were prepared by chemical reduction and applied in the catalytic hydrogenation of turpentine. The α-pinene hydrogenation reactions were investigated and optimized by response surface methodology, meanwhile, amorphous catalysts were characterized by XRD, BET, SEM, XPS, and ICP. Under reaction temperature 124.8℃, reaction pressure 4.9 MPa, catalyst amount 6.3%, and reaction time 90 minutes, the conversion rate of α-pinene was 99.45%, the selectivity of cis-pinane was 97.35%. Meanwhile, the catalysts were used in catalytic hydrogenation of other components to broaden the range of catalysts and improve deep process of turpentine, the catalysts exhibited high catalytic activity, raw conversion was reached more than 99%, and the selectivity was reached more than 65%.

Key words: APO-11, amorphous, turpentine, catalysis

摘要：

以二异丙胺、氢氧化铝为原料，采用水热合成法制得APO-11磷酸铝分子筛。采用化学还原法制备非晶态Ni-P/APO-11催化剂用于α-蒎烯加氢反应，考察了α-蒎烯加氢反应条件，通过响应面法实现进一步优化，而后采用XRD、BET、SEM、XPS、ICP等对该催化剂进行了表征。结果显示，在反应温度124.8℃，反应压力4.9 MPa，催化剂用量6.3%，反应时间90 min时，α-蒎烯转化率为99.45%，顺式蒎烷选择性97.35%。为进一步拓宽该催化剂使用范围及提高松节油体系的深加工利用水平，将该催化剂用于松节油其他组分的加氢反应中，展现出良好的催化活性，原料转化率均可达到99%以上，选择性65%以上。

关键词: APO-11, 非晶态, 松节油, 催化

CLC Number:

TB333

PAN Deng, WANG Yaming, ZHONG Shenjie, JIANG Lihong. Optimization of Ni-P/APO-11 amorphous catalyst for catalytic hydrogenation of turpentine using response surface methodology[J]. CIESC Journal, 2017, 68(6): 2376-2385.

潘登, 王亚明, 钟申洁, 蒋丽红. 响应面法优化Ni-P/APO-11非晶态催化剂催化松节油加氢反应[J]. 化工学报, 2017, 68(6): 2376-2385.

References 32

[1]	NIE G K, ZOU J J, FENG R, et al. HPW/MCM-41 catalyzed isomerization and dimerization of pure pinene and crude turpentine[J]. Catalysis Today, 2014, 234: 271-277.
[2]	BERNARD M, SAMUEL P D V, SASON S. Mechanism of oxidation reactions catalyzed by cytochrome P450 enzymes[J]. Chemical Reviews, 2004, 104(9): 3947-9780.
[3]	PAUL R, DARBHA S. Selective oxidations over zeolite-and mesoporous silica-based catalysts: selected examples[J]. Catalysis Today, 2009, 141(1/2): 3-11.
[4]	SUH Y W, KIM N K, AHN W S, et al. Redox-mesoporous molecular sieve as a bifunctional catalyst for the one-pot synthesis of campholenic aldehyde from α-pinene[J]. Journal of Molecular Catalysis A: Chemical, 2001, 174(1/2): 249-254.
[5]	SELVARAJ M, KANDASWAMY M, PARK D W, et al. Highly efficient and clean synthesis of verbenone over well ordered two-dimensional mesoporous chromium silicate catalysts[J]. Catalysis Today, 2010, 158(3/4): 286-295.
[6]	MARJA K L, TATJA M, ARI M P K. Co(Ⅱ) catalysed oxidation of α-pinene by molecular oxygen[J]. Tetrahedron, 2000, 56(41): 8167-8171.
[7]	JPSEPH P B. Preparation of 2,6-dimethyl-2,7-octadiene: US3277206 [P]. 1966-10-04.
[8]	赵振东, 刘先章. 松节油的精细化学利用(Ⅱ)[J]. 林产化工通讯, 2001, 35(2): 41-46.
	ZHAO Z D, LIU X Z. Fine chemical utilization of turpentine(Ⅱ)[J]. Forestry Chemical Communication, 2001, 35(2): 41-46.
[9]	赵振东, 刘先章. 松节油的精细化学利用(Ⅲ)[J]. 林产化工通讯, 2001, 35(3): 38-43.
	ZHAO Z D, LIU X Z. Fine chemical utilization of turpentine (Ⅲ)[J]. Forestry Chemical Communication, 2001, 35(3): 38-43.
[10]	赵振东, 孙震. 松节油的精细化学利用(Ⅳ)[J]. 林产化工通讯, 2001, 35(4): 34-40.
	ZHAO Z D, SUN Z. Fine chemical utilization of turpentine(Ⅳ)[J]. Forestry Chemical Communication, 2001, 35(4): 34-40.
[11]	IRINA L S, YULIA S, IRINA D. Modeling of kinetics and stereoselectivity in liquid-phase α-pinene hydrogenation over Pd/C[J]. Applied Catalysis A: General, 2009, 356(2): 216-224.
[12]	DALIDA C C. Hydrogenation of alphα-pinene to cis-pinane[J]. Industrial & Engineering Chemistry Research, 2001, 40: 255l-2554.
[13]	GERHARD W, GERHARD T, HEINZ W V. Ultrasound method of reactivating deactivated hydrogenation catalysts: US5132270[P]. 1992-07-21.
[14]	JENKE T, SUSS F G. Kinetische enantiomerendifferenzierung bei der katalytischen hydrierung nicht funktionalisierter terpenolefine mit chiral modifizierten ruthenium clustern[J]. Journal of Organometallic Chemisty, 1991, 405(3): 383-391.
[15]	ANTERO L, OLLI A, JUHA K. Hydrogenation of α-pinene: WO2002072508[P]. 2002-9-19.
[16]	LANDIS C R, HALPERN J. Asymmetric hydrogenation of methyl (Z)-alpha-acetamidocinnamate catalyzed by [1,2-bis((phenyl-o-anisoyl) phosphino)ethane] rhodium (Ⅰ): Kinetics, mechanism and origin of enantioselection[J]. Journal of the American Chemical Society, 1987, 109(6): 1746-1754.
[17]	REN S B, QIU J H, WANG C Y, et al. Dispersion state of nickel ions on γ-Al2O3 and catalytic activity of derived nickel catalysts for hydrogenation of α-pinene[J]. Chinese Journal of Inorganic Chemistry, 2007, 23(6): 1021-1028.
[18]	ZHANG M J, LI W Z, ZU S, et al. Catalytic hydrogenation for bio-oil upgrading by a supported NiMoB amorphous alloy[J]. Chemical Engineering & Technology, 2013, 36(12): 2108-2116.
[19]	WEI S, CUI H, WANG J, et al. Preparation and activity evaluation of NiMoB/γ-Al2O3 catalyst by liquid-phase furfural hydrogenation[J]. Particuology, 2011, 9(1): 69-74.
[20]	WANG W, YANG Y, LUO H, et al. Amorphous Co-Mo-B catalyst with high activity for the hydrodeoxygenation of bio-oil[J]. Catalysis Communications, 2011, 12(6): 436-440.
[21]	WANG W Y, YANG Y Q, LUO H, et al. Preparation of Ni-W-B amorphous catalysts for cyclopentanone hydrodeoxygenation[J]. Catalysis Communications, 2011, 12(14): 1275-1279.
[22]	LI H, LIU J, XIE S H, et al. Highly active Co-B amorphous alloy catalyst with uniform nanoparticles prepared in oil-in-water microemulsion[J]. Journal of Catalysis, 2008, 259(1): 104-110.
[23]	KO S H, CHOU T C. Selective hydrogenation of (-)-α-pinene over nickel catalysts prepared by electroless deposition[J]. Industrial & Engineering Chemistry Research, 1995, 34: 457-467.
[24]	张家华, 蒋丽红, 伍水生, 等. 非晶态镍硼/石墨烯复合材料的制备及其蒎烯催化加氢活性[J]. 化工学报, 2016, 67(6): 2363-2370.
	ZHANG J H, JIANG L H, WU S S, et al. Preparation of amorphous Ni-B/graphene composites for catalytic hydrogenation of pinene[J]. CIESC Journal, 2016, 67(6): 2363-2370.
[25]	李凝, 马庆丰, 刘伟, 等. 负载型NiB非晶态合金上α-蒎烯催化加氢性能研究[J]. 精细化工, 2010, 27(11): 1073-1077.
	LI N, MA Q F, LIU W, et al. Study on catalytical performance of supported NiB amorphous alloy on hydrogenation of α-pinene[J]. Fine Chemicals, 2010, 27(11): 1073-1077.
[26]	DHANAPAI K, NARAYANAN V, STEPHEN A. Influence of Sn on the magnetic ordering of Ni-Sn alloy synthesized using chemical reduction method[J]. Journal of Magnetism and Magnetic Materials, 2016, 406:103-109.
[27]	王来军, 张明慧, 李伟, 等. Ni-B、NiB/MgO非晶态合金催化剂的制备、表征及其加氢性能[J]. 石油化工, 2004, 33(1): 14-18.
	WANG L J, ZHANG M H, LI W, et al. Preparation, characterization and catalytic performance of NiB and NiB/MgO amorphous alloy catalysts in hydrogenation of sulfolene[J]. Petrochemical Technology, 2004, 33(1): 14-18.
[28]	王来军, 张明慧, 李伟, 等. 非晶态合金催化剂Ni-B、Ni-B/TiO2的制备、表征及其环丁烯砜加氢催化活性的研究[J]. 分子催化, 2003, 17(6): 450-455.
	WANG L J, ZHANG M H, LI W, et al. Preparation, characterization and catalytic behavior of the NiB and NiB/TiO2 amorphous catalysts[J]. Journal of Molecular Catalysis, 2003, 17(6): 450-455.
[29]	王益, 沈俭一, Han Warlimont. 雷尼镍催化剂的吸附热研究[J]. 催化学报, 1998, 19(2): 163-165.
	WANG Y , SHEN J Y, HAN W. Microcalorimetric studies of Raney nickel catalysts[J]. Chinese Journal of Catalysis, 1998, 19(2): 163-165.
[30]	CHEN Y Z, LIAW B J, CHIANG S J. Selective hydrogenation of citral over amorphous Ni-B and CoB nano-catalysts [J]. Applied Catalysis A: General, 2005, 284(1/2): 97-104.
[31]	REN S B, QIU J H, WANG C Y, et al. Influence of nickel salt precursors on the hydrogenation activity of Ni/Al2O3 catalyst[J]. Industrial Catalysis, 2007, 28(7): 651-656.
[32]	陈小鹏, 王琳琳, 阳承利, 等. α-蒎烯催化加氢反应的研究[J]. 天然气化工: C1化学与化工, 2002, 27(6): 55-58.
	CHEN X P, WANG L L, YANG C L, et al. Study on catalytic hydrogenation of α-pinene [J]. Natural Gas Chemical Industry, 2002, 27(6): 55-58.