窑法磷酸中磷酸钙对P2O5反吸过程

doi:10.11949/j.issn.0438-1157.20160688

摘要/Abstract

摘要：

窑法磷酸生产中，气体产物P₂O₅与磷矿发生副反应（俗称P₂O₅反吸）生成大量低熔点物料，导致窑内结圈堵料，造成生产装置不能稳定运行。以磷酸钙与P₂O₅的反应为研究对象，采用化学分析与SEM、XRD、IR、Raman、TG及DSC等表征手段对不同温度下该反应产物的P₂O₅含量、形貌、物相组成、结构及热稳定性能等进行研究，探讨磷矿对P₂O₅的反吸行为。研究表明，反吸过程与反应温度密切相关，磷酸钙与P₂O₅在500℃以上发生反应，在500～900℃时，磷酸钙与P₂O₅反应生成偏磷酸钙，900℃反吸产物几乎为纯偏磷酸钙；在1000～1300℃时，反吸产物偏磷酸钙分解为稳定的焦磷酸钙，同时释放出P₂O₅气体，1300℃时反吸产物几乎为纯焦磷酸钙。

关键词: 窑法磷酸, P₂O₅反吸, 偏磷酸钙, 焦磷酸钙, 烧结, 结垢, 化学过程

Abstract:

Side reactions of gaseous product P₂O₅ with phosphate ores (so-called P₂O₅ back absorption) in rotary kiln produce large quantities of low melting point solid products, which could form a kiln ring, block material flow and cause unstable operation of the kiln. The back absorption of gaseous P₂O₅ with calcium phosphate was studied at different temperatures and the products were characterized for P₂O₅ content, morphology, phase composition, structure and thermal stability by chemical analysis and other techniques of SEM, XRD, IR, Raman, TG and DSC. The experimental results show that temperature significantly affected the back absorption, which was occurred above 500℃. Calcium metaphosphate was formed at 500-900℃ with almost pure calcium metaphosphate at 900℃. Calcium metaphosphate decomposed into calcium pyrophosphate and P₂O₅ at 1000-1300℃ with almost pure calcium pyrophosphate at 1300℃.

Key words: rotary kiln phosphoric acid, P₂O₅ back absorption, calcium metaphosphate, calcium pyrophosphate, fouling, sintering, chemical processes

中图分类号:

TP273

吕莉, 梁斌, 刘强, 刘维燥, 杨宏辉, 吴潘, 李春. 窑法磷酸中磷酸钙对P₂O₅反吸过程[J]. 化工学报, 2016, 67(10): 4399-4405.

LÜ Li, LIANG Bin, LIU Qiang, LIU Weizao, YANG Honghui, WU Pan, LI Chun. Reactions between P₂O₅ and calcium phosphate in kiln phosphoric acid[J]. CIESC Journal, 2016, 67(10): 4399-4405.

参考文献 24

[1]	江善襄, 方天翰, 戴元法, 等. 磷酸、磷肥和复混肥料[M]. 北京:化学工业出版社, 1999:578. JIANG S X, FANG T H, DAI Y F, et al. Phosphoric Acid Phosphate Fertilizer and Compound Fertilizer[M]. Beijing:Chemical Industry Press, 1999:578.
[2]	邓淑元, 梁斌, 李春, 等. 窑法磷酸技术研究进展[J]. 化工进展, 2012, 31(7):1402-1406. DENG S Y, LIANG B, LI C, et al. Research progress of kiln phosphoric acid process[J]. Chemical Industry and Engineering Progress, 2012, 31(7):1402-1406.
[3]	ROBERT A H, LAGUNA B C. Process for reducing phosphate ore:US4389384[P]. 1983-06-21.
[4]	JACOB M U, FREDERIC L, PARK W C, et al. Reduction of phosphate ores by carbon (Ⅰ):Process variables for design of rotary kiln system[J]. Metallurgical Transactions B, 1986, 17(4):861-868.
[5]	FREDERIC L, HOWARD R, JACOB M U, et al. Reduction of phosphate ores by carbon (Ⅱ):Rate limiting steps[J]. Metallurgical Transactions B, 1986, 17(4):869-877.
[6]	JOSEPH M, MISSION V, ROBERT A H, et al. Process for reducing phosphate ore:US4351813[P]. 1982-09-28.
[7]	JOSEPH M. Phosphorous pentoxide producing methods:US7378070[P]. 2008-03-27.
[8]	陈刚, 黄焯枢, 侯拥和, 等. 窑法磷酸工艺中球团内碳还原剂烧损的抑制[J]. 矿冶工程, 1997, 17(1):51-54. CHEN G, HUANG Z S, HOU Y H, et al. Inhibition of reducing agent carbon pellet in the kiln phosphoric acid process[J]. Mining Engineering, 1997, 17(1):51-54.
[9]	江礼科, 邱礼有, 梁斌, 等. 氟磷灰石热炭固态还原反应机理[J]. 成都科技大学学报, 1995, (1):1-5. JIANG L K, QIU L Y, LIANG B, et al. The mechanism of the solid state reduction reaction of the thermal carbon[J]. Journal of Chengdu University of Science and Technology, 1995, (1):1-5.
[10]	江礼科, 梁斌, 邱礼有, 等. 氟磷灰石热炭还原的动力学[J]. 成都科技大学学报, 1995, (5):1-8. JIANG L K, LIANG B, QIU L Y, et al. Kinetics of thermal carbon reduction of fluorine[J]. Journal of Chengdu University of Science and Technology, 1995, (5):1-8.
[11]	江善襄, 陆友俊, 王富生, 等.隧道窑法制磷酸:1044077A[P]. 1990-07-25. JIANG S X, LU Y J, WANG F S, et al. Production of phosphoric acid by tunnel kiln method:1044077A[P]. 1990-07-25.
[12]	李燕凤, 胡慧, 余晨, 等. 窑法磷酸工业生产试验进展[J]. 磷肥与复肥, 2013, 28(1):25-29. LI Y F, HU H, YU C, et al. Industrial production experiments development of kiln-process phosphoric acid[J]. Phosphate & Compound Fertilizer, 2013, 28(1):25-29.
[13]	殷宪国. 我国回转窑窑法磷酸(CDK)试生产现状与探讨[J]. 磷肥与复肥, 2007, 22(1):33-35. YIN X G. Discussion on the current trial production of CDK kiln-method phosphoric acid technology in China[J]. Phosphate & Compound Fertilizer, 2007, 22(1):33-35.
[14]	江善襄. 提高窑法磷酸还原率的探讨[J]. 磷肥与复肥, 1995, (1):13-17, 56. JIANG S X. Discussion on improving the reduction rate of KPA[J]. Phosphate & Compound Fertilizer, 1995, (1):13-17, 56.
[15]	江善襄. 提高窑法磷酸还原率的探讨(续)[J]. 磷肥与复肥, 1995, (2):10-15, 80. JIANG S X. Discussion on improving the reduction rate of KPA (continued)[J]. Phosphate & Compound Fertilizer, 1995, (2):10-15, 80.
[16]	JOSEPH A M. Phosphorous pentoxide producing methods:US7378070B2[P]. 2008-5-27.
[17]	VINCENT S. Chemistry & Technology of Fertilizer[M]. New York:Reinhold Publishing Corp., 1960:346.
[18]	刘戎生. 用黄磷和磷矿石生产偏磷酸钙肥料[J]. 云南化工, 1989, (3):44-46. LIU R S. With the production of yellow phosphorus and phosphate fertilizer of calcium metaphosphate[J]. Yunnan Chemical Technology, 1989, (3):44-46.
[19]	杨宏辉, 李春, 梁斌, 等. 窑法制磷酸反应的热力学[J]. 化学反应工程与工艺, 2011, 27(6):543-549. YANG H H, LI C, LIANG B, et al. Thermodynamics of kiln-process phosphoric acid[J]. Chemical Reaction Engineering and Technology, 2011, 27(6):543-549.
[20]	梁晓峰, 尹光福, 杨世源, 等. 偏磷酸钙玻璃陶瓷的结晶化研究[J]. 人工晶体学报, 2010, 39(3):813-816. LIANG X F, YIN G F, YANG S Y, et al. Study on crystallization of calcium metaphosphate glass-ceramics[J]. Journal of Synthetic Crystals, 2010, 39(3):813-816.
[21]	翁诗甫. 傅里叶变换红外光谱分析[M]. 北京:化学工业出版社, 2010:351. WENG S F. Fourier Translation Infrared Spectroscopy[M]. Beijing:Chemical Industry Press, 2010:351.
[22]	PROKUPKOVA P, MOSNER P, KOUDELKA L, et al. Preparation and study of Ca1-xMgx(PO3)2 glassy and crystalline phases[J]. J. Mater. Sci., 1998, 33(3):743-748.
[23]	梁晓峰, 杨世源, 尹光福. 偏磷酸钙玻璃制备过程结构变化的拉曼光谱分析[J]. 无机化学学报, 2010, 26(8):1404-1408. LIANG X F, YANG S Y, YIN G F. Raman spectra analusis for metaphosphate structure transformation in glass preparation process[J]. Chinese Journal of Inorganic Chemistry, 2010, 26(8):1404-1408.
[24]	汪磊, 尤静林, 王媛媛, 等. Ca2P2O7温致相变的拉曼光谱研究[J]. 光散射学报, 2012, 24(3):260-265. WANG L, YOU J L, WANG Y Y, et al. Temperature dependent Raman spectra and phase transformation study of Ca2P2O7[J]. The Journal of Light Scattering, 2012, 24(3):260-265.

窑法磷酸中磷酸钙对P₂O₅反吸过程

Reactions between P₂O₅ and calcium phosphate in kiln phosphoric acid

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 24

相关文章 15

编辑推荐

Metrics

本文评价

[1]	曾如宾, 沈中杰, 梁钦锋, 许建良, 代正华, 刘海峰. 基于分子动力学模拟的Fe₂O₃纳米颗粒烧结机制研究[J]. 化工学报, 2023, 74(8): 3353-3365.
[2]	黄磊, 孔令学, 白进, 李怀柱, 郭振兴, 白宗庆, 李平, 李文. 油页岩添加对准东高钠煤灰熔融行为影响的研究[J]. 化工学报, 2023, 74(5): 2123-2135.
[3]	葛泽峰, 吴雨青, 曾名迅, 查振婷, 马宇娜, 侯增辉, 张会岩. 灰化学成分对生物质气化特性的影响规律[J]. 化工学报, 2023, 74(5): 2136-2146.
[4]	胡月, 马守骏, 蹇锡高, 翁志焕. 新型聚芳醚腈固化邻苯二甲腈树脂的研究[J]. 化工学报, 2023, 74(2): 871-882.
[5]	李亚芾, 付亮亮, 白浩隆, 白丁荣, 许光文. 菱镁矿浮选尾矿直接合成同时制备镁橄榄石和镁砂研究[J]. 化工学报, 2022, 73(8): 3679-3687.
[6]	李淼, 赵虹, 姜标, 陈思远, 闫龙. 煤制乙炔关键中间体BaC₂合成的热力学分析[J]. 化工学报, 2022, 73(5): 1908-1919.
[7]	郭志强, 燕可洲, 张吉元, 柳丹丹, 高阳艳, 郭彦霞. 煤矸石/粉煤灰对赤泥钠化还原焙烧反应的影响机制[J]. 化工学报, 2022, 73(5): 2194-2205.
[8]	张浩, 赵宇, 徐志明, 李晋辉. 羧甲基葡聚糖的快速沉降法阻垢特性研究[J]. 化工学报, 2022, 73(4): 1515-1522.
[9]	孙雄康, 李强. 多级复合芯结构的强化沸腾传热研究[J]. 化工学报, 2022, 73(3): 1127-1135.
[10]	张凤丽, 潘辉, 王金江. 基于多元状态估计的热交换器多参数关联预警方法[J]. 化工学报, 2022, 73(2): 814-826.
[11]	谢广烁, 张斯亮, 王家瑞, 肖娟, 王斯民. 自转式内置转子颗粒污垢抑制特性研究[J]. 化工学报, 2022, 73(12): 5384-5393.
[12]	王景涛, 宋凡福, 徐志明, 贾玉婷. Ni-P-PTFE复合镀层对颗粒污垢沉积特性影响研究[J]. 化工学报, 2022, 73(10): 4594-4602.
[13]	王晓蓉, 曾玺, 王芳, 张光义, 许德平, 许光文. 温度和气氛对高K高S糠醛渣灰分的烧结特性研究[J]. 化工学报, 2022, 73(1): 411-424.
[14]	刘恒源, 王海辉, 徐建鸿. 电催化氮还原合成氨电化学系统研究进展[J]. 化工学报, 2022, 73(1): 32-45.
[15]	袁壮, 凌逸群, 杨哲, 李传坤. 基于TA-ConvBiLSTM的化工过程关键工艺参数预测[J]. 化工学报, 2022, 73(1): 342-351.