Pd-Pb/SiO2催化高浓度乙烯基乙炔加氢合成丁二烯

doi:10.11949/j.issn.0438-1157.20160160

摘要/Abstract

摘要：

研究了硅胶负载钯铅双金属催化剂催化高浓度乙烯基乙炔加氢合成丁二烯过程。结果表明，加入适量的铅可起到分隔钯纳米粒子，阻碍钯纳米粒子团聚的作用，从而提高催化剂的催化活性，最佳Pb/Pd摩尔比为0.2。继续提高Pb/Pd摩尔比时，会生成铅钯合金相，造成催化剂活性降低。X射线光电子能谱结果表明，催化剂的催化活性与Pd 3d的电子结合能呈正相关关系。制备催化剂过程中，还原温度对催化剂的结构和催化性能影响显著。在350℃下还原得到的催化剂中金属氧化物还原不彻底，催化剂活性较低；还原温度为450℃时，则会引起钯纳米粒子烧结，造成催化剂的催化活性和对丁二烯的选择性同时降低；催化剂的最佳还原温度为400℃。在40℃催化乙烯基乙炔反应40 h后，积炭造成催化剂的孔道堵塞，催化剂失活。因此，需要进一步开展改善催化剂的抗积炭能力和使用寿命方面的研究。

关键词: 加氢, 催化剂, 催化, 乙烯基乙炔, 丁二烯

Abstract:

The hydrogenation of high-concentration monovinylacetylene over silica supported Pd-Pb bimetallic catalysts was investigated. It showed that the appropriate presence of Pb can prevent Pd nanoparticles from aggregation, hence facilitated the improvement of catalytic activity, i.e. the optimal molar ratio of Pb to Pd of 0.2. With the molar ratio of Pb to Pd above 0.2, Pd-Pb alloy can be formed, which causes catalytic activity loss. The positive correlation between the catalytic activity and the electron bonding energy of Pd 3d was manifested by X-ray photoelectron spectra. The temperature for PdO reduction exhibited a remarkable influence on the structure and the activity of the catalysts. The PdO reduction at 350℃ of the catalyst was incomplete thus with low activity. At 450℃ of the reduction temperature, it caused Pd nanoparticle sintering, hence with low activity and low butadiene selectivity. As a result, the optimal reduction temperature was 400℃. After 40 h, the catalyst was deactivated due to the blockage of pore by coke formation on catalyst surface. Subsequently, the improvement of anti-coking ability and the lifetime of the catalyst will be of interest.

Key words: hydrogenation, catalysts, catalysis, monovinylacetylene, butadiene

中图分类号:

O643

张一科, 贾则琨, 张帅, 甄彬, 韩明汉. Pd-Pb/SiO₂催化高浓度乙烯基乙炔加氢合成丁二烯[J]. 化工学报, 2016, 67(7): 2793-2798.

ZHANG Yike, JIA Zekun, ZHANG Shuai, ZHEN Bin, HAN Minghan. Hydrogenation of high-concentration monovinylacetylene for butadiene production over Pd-Pb/SiO₂ catalysts[J]. CIESC Journal, 2016, 67(7): 2793-2798.

参考文献 24

[1]	张梁, 田靖, 刘兵. 丁烯氧化脱氢制丁二烯反应过程研究[J]. 天然气化工, 2015, 40(4): 15-18. ZHANG L, TIAN J, LIU B. Study on reaction process for oxidative dehydrogenation of 1-butene to butadiene [J]. Nat. Gas. Chem. Ind., 2015, 40(4): 15-18.
[2]	曾少娟, 田肖, 董海峰, 等. 丁二烯抽提工艺中离子液体添加剂的筛选及分离性能[J]. 化工学报, 2014, 65(6): 2120-2129. ZENG S J, TIAN X, DONG H F, et al. Selection and separation performance of ionic liquid as additive in butadiene extraction with CAN [J]. CIESC Journal, 2014, 65(6): 2120-2129.
[3]	常红, 童莉, 李广茹, 等. 丁二烯生产技术应用及发展建议[J]. 现代化工, 2013, 33(5): 8-12. CHANG H, TONG L, LI G R, et al. Suggestions for application and development of butadiene production technology [J]. Mod. Chem. Ind., 2013, 33(5): 8-12.
[4]	LYNCH M. Manufacture and use of chloroprene monomer [J]. Chem-Biol. Interact., 2001, 135/136: 155-167.
[5]	LIU J G, ZUO Y Z, HAN M H, et al. Stability improvement of the Nieuwland catalyst in the dimerization of acetylene to monovinylacetylene [J]. J. Nat. Gas Chem., 2012, 21(5): 495-500.
[6]	LIU J G, ZUO Y Z, HAN M H, et al. Improvement of anhydrous catalyst stability in acetylene dimerization by regulating acidity [J]. J. Chem. Technol. Biotechnol., 2013, 88(3): 408-414.
[7]	LIU J G, HAN M H, WANG Z W. Effect of solvent on catalytic performance of anhydrous catalyst in acetylene dimerization to monovinylacetylene [J]. J. Energy Chem., 2013, 22(4): 599-604.
[8]	MOLNÁR Á, SÁRKÁNY A, MÓNIKA V. Hydrogenation of carbon-carbon multiple bonds: chemo-, regio- and stereo-selectivity [J]. J. Mol. Catal. A-Chem., 2001, 173(1/2): 185-221.
[9]	BRIDIER B, KARHÁNEK D, PÉREZ-RAMÍREZ J, et al. Molecular understanding of enyne hydrogenation over palladium and copper catalysts [J]. ChemCatChem, 2012, 4(9): 1420-1427.
[10]	CRESPO-QUESADA M, CARDENAS-LIZANA F, DESSIMOZ A L, et al. Modern trends in catalyst and process design for alkyne hydrogenations [J]. ACS Catal., 2012, 2(8): 1773-1786.
[11]	徐海升, 李谦定, 马建平. 碳四馏分选择加氢研究进展[J]. 现代化工, 2002, 22(8): 9-12. XU H S, LI Q D, MA J P. Advances in selective hydrogenation of C4 fraction [J]. Mod. Chem. Ind., 2002, 22(8): 9-12.
[12]	DORBON M, HUGUES F, VILTARD J C, et al. Process for obtaining butane: US 6242662 [P]. 2001-10-22.
[13]	ZHEN B, CHEN W Q, JIA Z K, et al. Continuous hydrogenation of monovinylacetylene for 1, 3-butadiene production catalyzed by ionic liquid stabilized Pd nanoparticles [J]. Catal. Lett., 2014, 144(12): 2216-2220.
[14]	GOETZ J, VOLPE M A, GIGOLA C E, et al. Low-loaded Pd-Pb/α-Al2O3 catalysts: effect of alloying in the hydrogenation of buta-1, 3-diene and hydrogenation and isomerization of butenes [J]. J. Catal., 2001, 199(2): 338-345.
[15]	GOETZ J, VOLPE M A, SICA A M, et al. Low-loaded Pd-Pb/α-Al2O3 catalysts: indication of alloy formation from FTIR and X-ray photoelectron spectroscopy[J]. J. Catal., 1997, 167(2): 314-323.
[16]	LEE J H, KIM S K, AHN I Y, et al. Performance of Pd-Ag/Al2O3 catalysts prepared by the selective deposition of Ag onto Pd in acetylene hydrogenation [J]. Catal. Commun., 2011, 12(13): 1251-1254.
[17]	KIM S K, LEE J H, AHN I Y, et al. Performance of Cu-promoted Pd catalysts prepared by adding Cu using a surface redox method in acetylene hydrogenation [J]. Appl. Catal. A-Gen., 2011, 401(1/2): 12-19.
[18]	AHN Y I, KIM W J, MOON S H. Performance of La2O3- or Nb2O5- added Pd/SiO2 catalysts in acetylene hydrogenation [J]. Appl. Catal. A-Gen., 2006, 308: 75-81.
[19]	KONTAPAKDEE K, PANPRANOT J, PRASERTHDAM P. Effect of Ag addition on the properties of Pd-Ag/TiO2 catalysts containing different TiO2 crystalline phases [J]. Catal. Commun., 2007, 8(12): 2166-2170.
[20]	徐立英, 乐毅, 朱云仙, 等. 碳四馏分选择加氢工艺及催化剂的研究[J]. 石油化工, 2001, 30(9): 681-685. XU L Y, LE Y, ZHU Y X, et al. The process of C4 fraction selective hydrogenation and the catalyst [J]. Petrochem. Techno., 2001, 30(9): 681-685.
[21]	GIGOLA C E, ADURIZ H R, BODNARIUK P. Particle size effect in the hydrogenation of acetylene under industrial conditions [J]. Appl. Catal., 1986, 27(1): 133-144.
[22]	YANG B, BURCH R, HARDACRE C, et al. Mechanistic study of 1, 3-butadiene formation in acetylene hydrogenation over the Pd-based catalysts using density functional calculations [J]. J. Phys. Chem. C, 2014, 118(3): 1560-1567.
[23]	朱警, 戴伟, 穆玮, 等. 选择加氢催化剂载体氧化铝的改性及其工业应用(Ⅰ)[J]. 化工进展, 2004, 23(2): 192-194. ZHU J, DAI W, MU W, et al. Modification of aluminum oxide supporter for selective hydrogenation catalysts and its industrial application (Ⅰ) [J]. Chem. Ind. Eng. Prog., 2004, 23(2): 192-194.
[24]	穆玮, 朱警, 戴伟, 等. 选择加氢催化剂载体氧化铝的改性及其工业应用(Ⅱ)[J]. 化工进展, 2004, 23(3): 300-303. MU W, ZHU J, DAI W, et al. Modification of aluminum oxide supporter for selective hydrogenation catalysts and its industrial application (Ⅱ) [J]. Chem. Ind. Eng. Prog., 2004, 23(3): 300-303.

Pd-Pb/SiO₂催化高浓度乙烯基乙炔加氢合成丁二烯

Hydrogenation of high-concentration monovinylacetylene for butadiene production over Pd-Pb/SiO₂ catalysts

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 24

相关文章 15

编辑推荐

Metrics

本文评价

[1]	杨欣, 王文, 徐凯, 马凡华. 高压氢气加注过程中温度特征仿真分析[J]. 化工学报, 2023, 74(S1): 280-286.
[2]	吴雷, 刘姣, 李长聪, 周军, 叶干, 刘田田, 朱瑞玉, 张秋利, 宋永辉. 低阶粉煤催化微波热解制备含碳纳米管的高附加值改性兰炭末[J]. 化工学报, 2023, 74(9): 3956-3967.
[3]	李艺彤, 郭航, 陈浩, 叶芳. 催化剂非均匀分布的质子交换膜燃料电池操作条件研究[J]. 化工学报, 2023, 74(9): 3831-3840.
[4]	范孝雄, 郝丽芳, 范垂钢, 李松庚. LaMnO₃/生物炭催化剂低温NH₃-SCR催化脱硝性能研究[J]. 化工学报, 2023, 74(9): 3821-3830.
[5]	杨学金, 杨金涛, 宁平, 王访, 宋晓双, 贾丽娟, 冯嘉予. 剧毒气体PH₃的干法净化技术研究进展[J]. 化工学报, 2023, 74(9): 3742-3755.
[6]	曹跃, 余冲, 李智, 杨明磊. 工业数据驱动的加氢裂化装置多工况切换过渡状态检测[J]. 化工学报, 2023, 74(9): 3841-3854.
[7]	杨绍旗, 赵淑蘅, 陈伦刚, 王晨光, 胡建军, 周清, 马隆龙. Raney镍-质子型离子液体体系催化木质素平台分子加氢脱氧制备烷烃[J]. 化工学报, 2023, 74(9): 3697-3707.
[8]	程业品, 胡达清, 徐奕莎, 刘华彦, 卢晗锋, 崔国凯. 离子液体基低共熔溶剂在转化CO₂中的应用[J]. 化工学报, 2023, 74(9): 3640-3653.
[9]	陈杰, 林永胜, 肖恺, 杨臣, 邱挺. 胆碱基碱性离子液体催化合成仲丁醇性能研究[J]. 化工学报, 2023, 74(9): 3716-3730.
[10]	杨菲菲, 赵世熙, 周维, 倪中海. Sn掺杂的In₂O₃催化CO₂选择性加氢制甲醇[J]. 化工学报, 2023, 74(8): 3366-3374.
[11]	李凯旋, 谭伟, 张曼玉, 徐志豪, 王旭裕, 纪红兵. 富含零价钴活性位点的钴氮碳/活性炭设计及甲醛催化氧化应用研究[J]. 化工学报, 2023, 74(8): 3342-3352.
[12]	杨欣, 彭啸, 薛凯茹, 苏梦威, 吴燕. 分子印迹-TiO₂光电催化降解增溶PHE废水性能研究[J]. 化工学报, 2023, 74(8): 3564-3571.
[13]	陈雅鑫, 袁航, 刘冠章, 毛磊, 杨纯, 张瑞芳, 张光亚. 蛋白质纳米笼介导的酶自固定化研究进展[J]. 化工学报, 2023, 74(7): 2773-2782.
[14]	汤晓玲, 王嘉瑞, 朱玄烨, 郑仁朝. 基于Pickering乳液的卤醇脱卤酶催化合成手性环氧氯丙烷[J]. 化工学报, 2023, 74(7): 2926-2934.
[15]	余娅洁, 李静茹, 周树锋, 李清彪, 詹国武. 基于天然生物模板构建纳米材料及集成催化剂研究进展[J]. 化工学报, 2023, 74(7): 2735-2752.