活性炭表面性质对其吸附及氧化氢醌的影响

doi:10.11949/j.issn.0438-1157.20170864

摘要/Abstract

摘要：

研究了活性炭表面性质对活性炭吸附及氧化氢醌的影响。考察了3种材质活性炭在不同初始pH下吸附和氧化氢醌的性能以及氢醌吸附率、表观转化率与活性炭材质及用量的关系。实验结果表明：活性炭可以吸附及氧化氢醌，木屑材质活性炭对氢醌的吸附及转化效果好于其他两种，在未调节初始pH，反应时间3 h，反应温度25℃，木屑质活性炭用量为0.5 g·L^-1时，对氢醌的吸附率可达95.5%；木屑质活性炭用量为0.1 g·L^-1，其对氢醌的表观转化率为32.1%。木屑质活性炭微孔面积更大，表面的酚羟基、羧基和羰基官能团更丰富，故其吸附及转化氢醌的效果更好。在此基础上，提出了活性炭吸附及氧化氢醌的机理，为活性炭作为吸附剂或催化剂载体处理废水中酚类有机污染物提供理论依据。

关键词: 活性炭, 吸附, 模型, 氢醌, 含氧官能团

Abstract:

The oxygen-containing functional groups and pore structures of activated carbon in adsorption and oxidation mechanism of hydroquinone were studied. Effects of initial pH value, the dosage of activated carbon, on the adsorption and oxidation efficiency of hydroquinone were studied. Then the relationship between adsorption rate, apparent conversion rate of hydroquinone and the materials of activated carbon, the dosage of activated carbon was discussed. The results showed that the oxygen-containing functional groups of activated carbon could adsorb and oxidate hydroquinone, wood-chip activated carbon was better than the other two types of activated carbon on the adsorption and oxidation efficiency of hydroquinone. Under the condition of not to adjust the initial pH, reaction time 3 h, and reaction temperature 25℃, if wood-chip activated carbon dosage was 0.5 g·L^-1 quality its base adsorption was 95.5% and if dosage was 0.1 g·L^-1 the conversion of hydroquinone was 32.1%. The microporous surface area of sawdust activated carbon was larger than the other two activated carbon's, and the phenol hydroxyl group, carboxyl group, and carbonyl group were more abundant. Therefore, the adsorption and oxidation efficiency of hydroquinone using sawdust activated carbon was better. On the basis of this, the mechanism of activated carbon adsorption and oxidation of hydroquinone were proposed. It provided the theoretical basis for the treatment of wastewater containing phenolic organic pollutants by activated carbon as adsorbent and catalyst carrier.

Key words: activated carbon, adsorption, model, hydroquinone, oxygen-containing functional group

中图分类号:

X703.5

刘雨知, 王晨, 高玉, 隋振英, 邹东雷. 活性炭表面性质对其吸附及氧化氢醌的影响[J]. 化工学报, 2018, 69(4): 1595-1601.

LIU Yuzhi, WANG Chen, GAO Yu, SUI Zhenying, ZOU Donglei. Effects of surface properties of activated carbon on its adsorption and oxidation of hydroquinone[J]. CIESC Journal, 2018, 69(4): 1595-1601.

参考文献 36

[1]	ETESAMI M, KAROONIAN F S, MOHAMED N. Electrooxidation of hydroquinone on simply prepared Au-Pt bimetallic nanoparticles[J]. Science China Chemistry, 2013, 56(6):746-754.
[2]	KALLEL M, BELAID C, MECHICHI T, et al. Removal of organic load and phenolic compounds from olive mill wastewater by Fenton oxidation with zero-valent iron[J]. Chemical Engineering Journal, 2009, 150(2/3):391-395.
[3]	ASTUDILLO P D, VALENCIA D P, GONZ LEZ-FUENTES M A, et al. Electrochemical and chemical formation of a low-barrier proton transfer complex between the quinone dianion and hydroquinone[J]. Electrochimica Acta, 2012, 81(22):197-204.
[4]	STEFANO J S, ROCHA D P, DORNELLAS R M, et al. Highly sensitive amperometric detection of drugs and antioxidants on non-functionalized multi-walled carbon nanotubes:effect of metallic impurities[J]. Electrochimica Acta, 2017, 240:80-89.
[5]	LUO H, LIANG H, CHEN J, et al. Hydroquinone induces TK6 cell growth arrest and apoptosis through PARP-1/p53 regulatory pathway[J]. Environmental Toxicology, 2017, 32(9):2163-2171.
[6]	MAZLOUM-ARDAKANI M, YAVARI M, KHOSHROO A. Different electrocatalytic response related to the morphological structure of TiO2 nanomaterial:hydroquinone as an analytical probe[J]. Electroanalysis, 2017, 29(1):231-237.
[7]	GOODWIN P M, ANTHONY C. The biochemistry, physiology and genetics of PQQ and PQQ-containing enzymes[J]. Advances in Microbial Physiology, 1998, 40(1):1-80.
[8]	MA W, LONG Y T. Quinone/hydroquinone-functionalized biointerfaces for biological applications from the macro-to nano-scale[J]. Chemical Society Reviews, 2014, 43(1):30-41.
[9]	ROLDA?N S, GRANDA M, MENE?NDEZ R, et al. Mechanisms of energy storage in carbon-based supercapacitors modified with a quinoid redox-active electrolyte[J]. The Journal of Physical Chemistry C, 2011, 115(35):17606-17611.
[10]	SALAS M, GÓMEZ M N, GONZÁLEZ F J, et al. Electrochemical reduction of 1, 4-benzoquinone. Interaction with alkylated thymine and adenine nucleobases[J]. Journal of Electroanalytical Chemistry, 2003, 543(1):73-81.
[11]	TANG P, DENG C, TANG X, et al. Degradation of p-nitrophenol by interior microelectrolysis of zero-valent iron/copper-coated magnetic carbon galvanic couples in the intermittent magnetic field[J]. Chemical Engineering Journal, 2012, 210(4):203-211.
[12]	LUO J, SONG G, LIU J, et al. Mechanism of enhanced nitrate reduction via micro-electrolysis at the powdered zero-valent iron/activated carbon interface[J]. Journal of Colloid & Interface Science, 2014, 435:21-25.
[13]	TSENG H H, SU J G, LIANG C. Synthesis of granular activated carbon/zero valent iron composites for simultaneous adsorption/dechlorination of trichloroethylene[J]. Journal of Hazardous Materials, 2011, 192(2):500-506.
[14]	LV X, XU J, JIANG G, et al. Removal of chromium(Ⅵ) from wastewater by nanoscale zero-valent iron particles supported on multiwalled carbon nanotubes[J]. Chemosphere, 2011, 85(7):1204-1209.
[15]	WU L, LIAO L, LV G, et al. Micro-electrolysis of Cr(Ⅵ) in the nanoscale zero-valent iron loaded activated carbon[J]. Journal of Hazardous Materials, 2013, 254/255C(12):277-283.
[16]	LAI B, ZHOU Y, YANG P, et al. Degradation of 3, 3'-iminobis-propanenitrile in aqueous solution by Fe0/GAC micro-electrolysis system[J]. Chemosphere, 2013, 90(4):1470-1477.
[17]	FU F, HAN W, HUANG C, et al. Removal of Cr(Ⅵ) from wastewater by supported nanoscale zero-valent iron on granular activated carbon[J]. Desalination & Water Treatment, 2013, 51(13/14/15):2680-2686.
[18]	LENG L, YUAN X, ZENG G, et al. Surface characterization of rice husk bio-char produced by liquefaction and application for cationic dye(Malachite green) adsorption[J]. Fuel, 2015, 155:77-85.
[19]	ZHANG W X. Nanoscale iron particles for environmental remediation:an overview[J]. Journal of Nanoparticle Research, 2003, 5(3):323-332.
[20]	HOSSEINI S M, ATAIE-ASHTIANI B, KHOLGHI M. Nitrate reduction by nano-Fe/Cu particles in packed column[J]. Desalination, 2011, 276(1/2/3):214-221.
[21]	NIGROVSKI B, ZAVYALOVA U, SCHOLZ P, et al. Microwave-assisted catalytic oxidative dehydrogenation of ethylbenzene on iron oxide loaded carbon nanotubes[J]. Carbon, 2008, 46(13):1678-1686.
[22]	曲健林, 韩敏, 张秀丽, 等. 棉杆活性炭负载Co-B催化剂催化硼氢化钠水解制氢的性能[J]. 化工学报, 2015, 66(1):105-113. QU J L, HAN M, ZHANG X L, et al. Hydrogen generation by sodium borohydride hydrolysis on Co-B catalysts supported on cotton stalk-based activated carbon[J]. CIESC Journal, 2015, 66(1):105-113.
[23]	蒋剑春. 活性炭应用理论与技术[M]. 北京:化学工业出版社, 2010. JIANG J C. Application Theory and Technology of Activated Carbon[M]. Beijing:Chemical Industry Press, 2010.
[24]	XIA G, SHEN S, ZHU F, et al. Effect of oxygen-containing functional groups of carbon materials on the performance of Li-O2 batteries[J]. Electrochemistry Communications, 2015, 60:26-29.
[25]	周王帆, 陈新, 曹红亮, 等. 法国梧桐枯叶基活性炭的制备及其在超级电容器中的应用[J]. 化工学报, 2017, 68(7):2918-2924. ZHOU W F, CHEN X, CAO H L, et al. Preparation of platanus leaf-based activated carbon and its application to supercapacitors[J]. CIESC Journal, 2017, 68(7):2918-2924.
[26]	LAHAYEA J. The chemistry of carbon surfaces[J]. Fuel, 1998, 77(6):543-547.
[27]	ARENILLAS A, SMITH K M, DRAGE T C, et al. CO2 capture using some fly ash-derived carbon materials[J]. Fuel, 2005, 84(17):2204-2210.
[28]	CUI H, TURN S Q, REESE M A. Removal of sulfur compounds from utility pipelined synthetic natural gas using modified activated carbons[J]. Catalysis Today, 2009, 139(4):274-279.
[29]	DAUD W M A W, HOUSHAMND A H. Textural characteristics, surface chemistry and oxidation of activated carbon[J]. Journal of Natural Gas Chemistry, 2010, 19(3):267-279.
[30]	FIGUEIREDO J L, PEREIRA M F R. The role of surface chemistry in catalysis with carbons[J]. Catalysis Today, 2010, 150(1/2):2-7.
[31]	FIGUEIREDO J L, PEREIRA M F R, FREITAS M M A, et al. Modification of the surface chemistry of activated carbons[J]. Carbon, 1999, 37(9):1379-1389.
[32]	范延臻, 王宝贞, 王琳, 等. 改性活性炭对有机物的吸附性能[J]. 环境化学, 2001, 20(5):444-448. FAN Y Z, WANG B Z, WANG L, et al. Adsorption of organic micropollutants on modifiedactivated carbons[J]. Environmental Chemistry, 2001, 20(5):444-448.
[33]	尤翔宇, 杨杰, 王云燕, 等. 苯酚在活性炭上的吸附模型[J]. 中国有色金属学报, 2012, 22(10):2924-2929. YOU X Y, YANG J, WANG Y Y, et al. Adsorption model of phenol on activated carbon[J]. Chinese Journal of Nonferrous Metals, 2012, 22(10):2924-2929.
[34]	HAYDAR S, FERRO-GARCÍA M A, RIVERA-UTRILLA J, et al. Adsorption of p-nitrophenol on an activated carbon with different oxidations[J]. Carbon, 2003, 41:387-395.
[35]	JIAN M. Determination of phenol aniline and hydroquinone by UV[J]. Environmental Science & Technology, 2011, 34(6G):249-251.
[36]	刘少俊, 高翔, 曹飞飞. 化学性质对活性炭脱硫的影响[J]. 煤炭学报, 2013, 38(7):1242-1247. LIU S J, GAO X, CAO F F. Effect of chemical properties on SO2 removal by activated carbons[J]. Journal of China Coal Society, 2013, 38(7):1242-1247.