化工学报 ›› 2016, Vol. 67 ›› Issue (6): 2386-2392.DOI: 10.11949/j.issn.0438-1157.20151606

• 分离工程 • 上一篇    下一篇

AC/X-G吸附剂的制备及CH4/N2吸附分离性能

张冬梅1, 程文萍1, 张明胜1, 崔杏雨2, 马静红2, 李瑞丰1,2   

  1. 1. 太原理工大学化学化工学院, 山西 太原 030024;
    2. 太原理工大学精细化工研究所, 山西 太原 030024
  • 收稿日期:2015-10-23 修回日期:2016-03-03 出版日期:2016-06-05 发布日期:2016-06-05
  • 通讯作者: 程文萍
  • 基金资助:

    国家自然科学基金项目(51204120);山西省青年科技研究基金项目(2014021014-1);山西省自然科学基金项目(2012011005-6);山西省煤基重点科技攻关项目(FT201402-03)。

Preparation of AC/X-G adsorbent and CH4/N2 adsorption separation performance

ZHANG Dongmei1, CHENG Wenping1, ZHANG Mingsheng1, CUI Xingyu2, MA Jinghong2, LI Ruifeng1,2   

  1. 1. College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China;
    2. Institute of Special Chemicals, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China
  • Received:2015-10-23 Revised:2016-03-03 Online:2016-06-05 Published:2016-06-05
  • Supported by:

    supported by the National Natural Science Foundation of China (51204120), the Natural Science Foundation of Shanxi Province (2014021014-1, 2012011005-6) and the Key Scientific and Technological Project of Coal Fund of Shanxi Province (FT201402-03).

摘要:

采用浓度为0.2g·ml-1的葡萄糖溶液对13X沸石/活性炭复合材料(AC/X)进行碳沉积,研究沉积次数对复合吸附剂(AC/X-G)孔结构、表面性质和CH4/N2吸附分离性能的影响。通过X射线衍射,77K下的N2吸附/脱附,扫描电镜,CO2-TPD以及红外光谱表征样品的晶型、孔结构和表面性质,在298K、100kPa下对其CH4和N2吸附等温线进行测定,并将吸附结果与文献中碳材料和13X沸石的吸附性能进行比较。结果表明:随着沉积次数的增加,AC/X-G吸附剂中X型沸石的相对含量降低,微孔比表面积和微孔体积减少。AC/X-G的表面被碳膜覆盖,碱量降低,但出现强碱位和含氧基团C-O键。AC/X-G的CH4和N2吸附量下降,但吸附分离系数提高,沉积3次的样品AC/X-G-3的CH4/N2吸附分离系数达到3.0,表面的含氧基团有利于提高复合材料的CH4/N2吸附分离性能。

关键词: 吸附剂, 葡萄糖, 碳沉积, 吸附, 分离

Abstract:

The 13X/activated carbon composite was treated by 0.2 g·ml-1 glucose solution for carbon deposition. The effect of deposition times on the pore structure, surface properties and separation performance of CH4/N2 were studied. The crystalline, pore structure and surface properties of the samples were investigated by X-ray diffraction (XRD), N2 adsorption-desorption isotherms at 77 K, scanning electron microscopy (SEM), CO2-TPD and Fourier transform infrared spectrum (FT-IR). The adsorption isotherms of CH4 and N2 were tested at 298 K and 100 kPa,and compared with the adsorption separation properties of carbon materials and 13X zeolite reported in the literatures. The experimental results showed that the relative content of X zeolite, the micropore surface area and the micropore volume of AC/X-G were gradually decreased with the increase of deposition times. The surface of samples was covered by carbon membrane, which led to decrease of the alkaline functional groups but increase of containing C-O groups. The adsorption capacities of CH4 and N2 decreased, while the adsorption separation coefficient was improved. After third deposition, the adsorption separation coefficient of CH4/N2 reached 3.0. The oxygen-containing functional groups on the surface of AC/X-G were beneficial to improve the separation performance of CH4/N2.

Key words: adsorbent, glucose, carbon deposition, adsorption, separation

中图分类号: