含氟体系中MFI型分子筛膜的制备及其乙醇/水分离性能

doi:10.3969/j.issn.0438-1157.2014.12.056

化工学报 ›› 2014, Vol. 65 ›› Issue (12): 5061-5066.DOI: 10.3969/j.issn.0438-1157.2014.12.056

• 材料化学工程与纳米技术 • 上一篇下一篇

含氟体系中MFI型分子筛膜的制备及其乙醇/水分离性能

孔晴晴, 张春, 王学瑞, 顾学红

南京工业大学化学化工学院, 材料化学工程国家重点实验室, 江苏南京 210009

收稿日期:2014-05-16 修回日期:2014-06-30 出版日期:2014-12-05 发布日期:2014-12-05
通讯作者: 顾学红
基金资助:
国家自然科学基金项目(21222602,21176117);江苏省杰出青年基金项目(BK20122040);江苏省自然科学基金青年基金项目(BK20130915);中国博士后基金面上项目(2012M521065);江苏高校优势学科建设工程项目.

Preparation of MFI zeolite membranes in fluoride media and separation performance for ethanol/water mixture

KONG Qingqing, ZHANG Chun, WANG Xuerui, GU Xuehong

State Key Laboratory of Materials-Oriented Chemical Engineering, School of Chemistry and Chemical Engineering, Nanjing Tech University, Nanjing 210009, Jiangsu, China

Received:2014-05-16 Revised:2014-06-30 Online:2014-12-05 Published:2014-12-05
Supported by:
supported by the National Natural Science Foundation of China (21222602, 21176117), the Outstanding Young Fund of Jiangsu Province (BK20122040), the Natural Science Foundation of Jiangsu Province (BK20130915), the General Financial Grant from the China Postdoctoral Science Foundation (2012M521065) and the Priority Academy Program Development of Jiangsu Higher Education Institutions(PAPD).

摘要/Abstract

摘要： 以氟化铵为矿化剂、四丙基溴化铵为模板剂,在负载晶种的钇稳定氧化锆(YSZ)中空纤维支撑体表面合成了MFI型分子筛膜,并用于乙醇/水的分离;系统考察了氟硅比(n_NH₄F/n_SiO₂)、合成时间等条件对膜分离性能的影响,在n_NH₄F/n_SiO₂为0.8、合成时间为8 h下合成出高性能膜,其通量达8.2 kg·m^-2·h^-1、乙醇/水分离因子为47;同时研究了MFI型分子筛膜在乙醇/水体系中的分离稳定性,揭示出该方法所合成膜表面无Si—OH,从而避免了Si—OH与乙醇反应而带来膜分离性能的下降.

关键词: MFI型分子筛膜, 中空纤维, 氟化铵, 稳定性, 乙醇分离

Abstract: MFI zeolite membranes were synthesized on seeded yttria stabilized zirconia (YSZ) hollow fiber substrates by using ammonium fluoride as mineralizing agent and tetrapropylammonium bromide as template. The as-synthesized membranes were tested for separation of ethanol/water mixture. The influences of n_NH₄F/n_SiO₂ ratio and synthesis time on separation performance were investigated. High-performance MFI zeolite membrane was synthesized at n_NH₄F/n_SiO₂=0.8 and synthesis time of 8 h, which showed a permeation flux of 8.2 kg·m^-2·h^-1 and ethanol/water separation factor of 47. The stability of MFI zeolite membranes in ethanol/water mixture was investigated. No Si—OH was detected on the surface of the as-synthesized MFI zeolite membranes, which could avoid decreased membrane separation performance by the reaction between Si—OH and ethanol.

Key words: MFI zeolite membrane, hollow fiber, ammonium fluoride, stability, ethanol separation

中图分类号:

TQ028.8

孔晴晴, 张春, 王学瑞, 顾学红. 含氟体系中MFI型分子筛膜的制备及其乙醇/水分离性能[J]. 化工学报, 2014, 65(12): 5061-5066.

KONG Qingqing, ZHANG Chun, WANG Xuerui, GU Xuehong. Preparation of MFI zeolite membranes in fluoride media and separation performance for ethanol/water mixture[J]. CIESC Journal, 2014, 65(12): 5061-5066.

参考文献 20

[1]	Travis C B. Fundamentals and applications of pervaporation through zeolite membranes [J]. J. Membr. Sci., 2004, 245(1/2): 1-33
[2]	Peter D C, Teresa O, Andrew G. Membranes for the dehydration of solvents by pervaporation [J]. J. Membr. Sci., 2008, 318(1/2): 5-37
[3]	Vane L M. Separation technologies for the recovery and dehydration of alcohols from fermentation broths [J]. Biofuels. Bioprod. Bioref., 2008, 2(6): 553-588
[4]	Kondo M, Komori M, Kita H. Tubular-type pervaporation module with zeolite NaA membrane [J]. J. Membr. Sci., 1997, 133(1): 133-141
[5]	Lai Z P, Bonilla G. Microstructural optimization of a zeolite membrane for organic vapor separation [J]. Science, 2003, 300(5618): 456-460
[6]	Drews T O, Tsapatsis M. Progress in manipulating zeolite morphology and related applications [J]. Curr. Opin. Colloid. In., 2005, 10(5/6): 233-238
[7]	Caro J, Noack M. Zeolite membranes—state of their development and perspective [J]. Micropor. Mesopor. Mater., 2000, 38(1): 3-24
[8]	Chapman P D, Oliveira T. Membranes for the dehydration of solvents by pervaporation [J]. J. Membr. Sci., 2008, 318: 5-37
[9]	Sano T, Yanagishita H, Kiyozumi Y. Separation of ethanol/water mixture by silicalite membrane [J]. Chem. Lett., 1992, 12: 2413-2414
[10]	Lin X, Kita H, Okamoto K. A novel method for the synthesis of high performance silicalite membranes [J]. Chem. Commun., 2000, 19: 1889-1890
[11]	Shu X J, Wang X R, Kong Q Q, Gu X H, Xu N P. High-flux MFI zeolite membrane supported on YSZ hollow fiber for separation of ethanol/water [J]. Ind. Eng. Chem. Res., 2012, 51(37): 12073-12080
[12]	Kuhn J, Sutanto S, Gascon J, Gross J, Kapteijn F. Performance and stability of multi-channel MFI zeolite membranes detemplated by calcination and ozonication in ethanol/water pervaporation [J]. J. Membr. Sci., 2009, 339(1/2): 261-274
[13]	Guth J L, Kessler H, Wey R. New route to pentasil-type zeolites using a non alkaline medium in the presence of fluoride ions [J]. Stud. Sur. Sci. Catal., 1986, 28: 121-128
[14]	Zhang X L, Zhu M H, Zhou R F, Chen X S, Kita H. Synthesis of silicalite-1 with high ethanol permeation in ultradilute solution containing fluoride [J]. Sep. Purif. Technol., 2011, 81(3): 480-484
[15]	Wang X R, Chen Y Y, Zhang C, Gu X H, Xu N P. Preparation and characterization of high-flux T-type zeolite membranes supported on YSZ hollow fibers [J]. J. Membr. Sci., 2014, 455: 494-304
[16]	Chezeau J M, Delmotte L, Guth J L. Influence of synthesis conditions and postsynthesis treatments on the nature and quantity of structural defects in highly siliceous MFI zeolites: a high-resolution solid state 29Si NMR study [J]. Zeolites, 1991, 11(6): 598-606
[17]	Mallon E E, Jeon M Y, Navarro M, Bhan A, Tsapatsis M. Probing the relationship between silicalite-1 defects and polyol adsorption properties [J]. Langmuir, 2013, 29(22): 6546-6555
[18]	Cheng C H, Bae T H, McCool B A, Chance R R, Nair R, Jones C W. Functionalization of the internal surface of pure-silica MFI zeolite with aliphatic alcohols [J]. J. Phys. Chem., 2008, 112: 3543-3551
[19]	Xu Ruren(徐如人), Pang Wenqing(庞文琴), Yu Jihong(于吉红), Huo Qisheng(霍启升). Chemistry-Zeolite and Porous Materials(分子筛与多孔材料化学)[M]. Beijing: Science Press, 2004: 238
[20]	Genoni F, Casati G P, Buzzoni R, Palmery S. FTIR and thermogravimetric study of silicalite treated with methanol [J]. Collect. Czech. Chem. Commun., 1997, 62: 1544-1550

含氟体系中MFI型分子筛膜的制备及其乙醇/水分离性能

Preparation of MFI zeolite membranes in fluoride media and separation performance for ethanol/water mixture

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 20

相关文章 15

编辑推荐

Metrics

本文评价

[1]	江河, 袁俊飞, 王林, 邢谷雨. 均流腔结构对微细通道内相变流动特性影响的实验研究[J]. 化工学报, 2023, 74(S1): 235-244.
[2]	郑玉圆, 葛志伟, 韩翔宇, 王亮, 陈海生. 中高温钙基材料热化学储热的研究进展与展望[J]. 化工学报, 2023, 74(8): 3171-3192.
[3]	孟令玎, 崇汝青, 孙菲雪, 孟子晖, 刘文芳. 改性聚乙烯膜和氧化硅固定化碳酸酐酶[J]. 化工学报, 2023, 74(8): 3472-3484.
[4]	毛磊, 刘冠章, 袁航, 张光亚. 可捕集CO₂的纳米碳酸酐酶粒子的高效制备及性能研究[J]. 化工学报, 2023, 74(6): 2589-2598.
[5]	韩奎奎, 谭湘龙, 李金芝, 杨婷, 张春, 张永汾, 刘洪全, 于中伟, 顾学红. 四通道中空纤维MFI分子筛膜用于二甲苯异构体分离[J]. 化工学报, 2023, 74(6): 2468-2476.
[6]	蔡斌, 张效林, 罗倩, 党江涛, 左栗源, 刘欣梅. 导电薄膜材料的研究进展[J]. 化工学报, 2023, 74(6): 2308-2321.
[7]	徐文超, 孙志高, 李翠敏, 李娟, 黄海峰. 静态条件下表面活性剂E-1310对HCFC-141b水合物生成的影响[J]. 化工学报, 2023, 74(5): 2179-2185.
[8]	王子健, 柯明, 李佳涵, 李舒婷, 孙巾茹, 童燕兵, 赵治平, 刘加英, 任璐. 短b轴ZSM-5分子筛制备方法及应用研究进展[J]. 化工学报, 2023, 74(4): 1457-1473.
[9]	陈向上, 马振杰, 任希华, 贾悦, 吕晓龙, 陈华艳. 三维网络萃取膜的制备及传质效率研究[J]. 化工学报, 2023, 74(3): 1126-1133.
[10]	刘润竹, 储甜甜, 张孝阿, 王成忠, 张军营. α，ω-端羟基亚苯基氟硅聚合物的合成及性能[J]. 化工学报, 2023, 74(3): 1360-1369.
[11]	杨宏欣, 李兴亚, 葛亮, 徐铜文. 含哌啶阳离子侧长链型一/二价阴离子选择性分离膜的制备[J]. 化工学报, 2022, 73(8): 3739-3748.
[12]	宋健斐, 孙立强, 解明, 魏耀东. 旋风分离器内气相旋转流不稳定性的实验研究[J]. 化工学报, 2022, 73(7): 2858-2864.
[13]	朱江伟, 马鹏飞, 杜晓, 杨言言, 郝晓刚, 罗善霞. 基于可变价NiFe-LDH/rGO对磷酸根离子的特异性电控分离[J]. 化工学报, 2022, 73(7): 3057-3067.
[14]	徐珂, 史国强, 薛冬峰. 无机杂化钙钛矿团簇材料：介尺度钙钛矿材料发光性质研究[J]. 化工学报, 2022, 73(6): 2748-2756.
[15]	宋超宇, 熊亚选, 张金花, 金宇贺, 药晨华, 王辉祥, 丁玉龙. 污泥焚烧炉渣基定型复合相变储热材料的制备和性能[J]. 化工学报, 2022, 73(5): 2279-2287.