新型潜伏性固化剂的合成及性能

doi:10.3969/j.issn.0438-1157.2014.09.056

摘要/Abstract

摘要： 利用9，10-二氢-9-氧杂-10-磷杂菲-10-氧化物（DOPO）的亲核特点，将其与双氰胺进行加成反应，合成了一种潜伏性固化剂，并将其与环氧树脂进行固化反应。用FTIR、¹H NMR分析了固化剂的结构；用DSC、TG分析了固化剂和固化体系的热性能。结果表明，与双氰胺相比，固化剂的熔点降低了近100℃，固化温度下降近 40℃；优化了固化工艺参数；考察了体系的潜伏性和难燃特性，其储存期超过100 d，LOI达到22。

关键词: 改性双氰胺, DOPO, 环氧树脂, 潜伏性固化剂, 合成, 动力学, 稳定性

Abstract: A novel latent curing agent for epoxy resin was synthesized via modifying dicyandiamide (DICY) with 9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide （DOPO） through addition reaction. The chemical structure of the modified DICY was confirmed by FTIR and ¹H NMR. The thermal properties of this modified DICY and its epoxy curing system were evaluated by DSC and TG. It was found that the melting point of the modified DICY decreased markedly and curing temperature dropped by nearly 40℃. The optimized curing process was also presented. Moreover, latency and flame retardancy of this system was proven, the storage period was more than 100 d and limiting oxygen index (LOI) was 22.

Key words: modified dicyandiamide, DOPO, epoxy resin, latent curing agent, synthesis, kinetics, stability

中图分类号:

O631

王权, 史铁钧, 虞伕, 刘建华, 周讯. 新型潜伏性固化剂的合成及性能[J]. 化工学报, 2014, 65(9): 3712-3717.

WANG Quan, SHI Tiejun, YU Fu, LIU Jianhua, ZHOU Xun. Synthesis and properties of novel latent curing agent[J]. CIESC Journal, 2014, 65(9): 3712-3717.

参考文献 23

[1]	Hajime Kimura, Akihiro Matsumoto, Keiko Ohtsuka. New type of phenolic resin: curing reaction of phenol-novolac based benzoxazine with bisoxazolineor epoxy resin using latent curing agent and the properties of the cured resin [J]. Journal of Applied Polymer Science, 2009, 112: 1762-1770
[2]	Fedtke M, Domaratius F, Pfitzmann A. Curing of epoxy resins with dicyandiamide [J]. Polymer Bulletin, 1990, 23: 381-388
[3]	Pfitzmann A, Fliedner E, Fedtke M. Curing of epoxy resins with dicyandiamide: NMR and IR investigation of isolated main products [J]. Polymer Bulletin,1994, 32: 311-317
[4]	Pfitzmann A, Schlothauer K, Fedtke M. Epoxy resin curing by dicyandiamide using model compounds [J]. Polymer Bulletin, 1991, 27: 59-66
[5]	Bengu B, Boerio F J. Interaction of epoxy/dicyandiamide adhesives with metal substrates [J]. The Journal of Adhesion, 2006, 82: 1133-1155
[6]	Kasturiarachchi K A, Geoffrey Pritchard. Free dicyandiamide in crosslinked epoxy resins [J]. Journal of Materials Science Letters, 1984, 3: 283-286
[7]	Takao Yamad, Tadaoki Okumoto, Hajime Ohtani, Shin Tsuge. Characterization of epoxy resins cured with dicyandiamide in the presence of imidazole catalysts by high-resolution pyrolysis-gas chromatography [J]. Journal of Analytical and Applied Pyrolysis, 1995, 33: 157-166
[8]	Poisson N, Maazouz A, Sautereau H, Taha M, Gambert X. Curing of dicyandiamide epoxy resins accelerated with substituted ureas [J]. Journal of Applied Polymer Science, 1998, 69: 2487-2497
[9]	Pfitzmann A, Fischer A, Fryauf K, Fedtke M. Curing of epoxy resins by dicyandiamide [J]. Polymer Bulletin, 1992, 27: 557-564
[10]	Wang Rumin (王汝敏), Zheng Shuirong (郑水蓉), Zeng Zhaozhi (曾昭智). Study on epoxy resin cured with modified dicyandiamide (MDC-1) [J]. Fiber Reinforced Plastics/Composites (玻璃钢/复合材料), 2000 (1): 16-22
[11]	Chen Lianxi (陈连喜), Zhang Huiling (张惠玲), Liu Quanwen (刘全文), Lei Jiaheng (雷家珩). Syntheses of curing agent modified dicyandiamide by m-toluidine [J]. Journal of Wuhan University of Technology (武汉理工大学学报), 2005, 27 (8): 11-13
[12]	Chen Lianxi (陈连喜), Zhang Huiling (张惠玲), Wu Yi (吴益), Lei Jiaheng (雷家珩). Syntheses and properties of curing agent modified dicyandiamide by p-toluidine [J]. Adhesion (粘接), 2004, 25 (4): 17-19
[13]	Wang Zhongyi (王钟熠), Zhang Lianhong (张连红), Liang Hongyu (梁红玉), Zhao Xiaofeng (赵晓锋). Research progress in flame retarded curing agents for epoxy resin [J]. Contemporary Chemical Industry (当代化工), 2013, 42 (5): 692-694
[14]	Yang Liancheng (杨连成), Tao Zaizhou (陶再洲), Zhong Xiaoping (钟晓萍), Xu Longhe (徐龙鹤). Applications of reactive-type DOPO based flame retardant in epoxy resins [J]. Thermosetting Resin (热固性树脂), 2008, 23 (6): 38-44
[15]	Ching Hsuan Lin. Synthesis of novel phosphorus-containing cyanate esters and their curing reaction with epoxy resin [J]. Polymer, 2004, 45: 7911-7926
[16]	Jan Christoph Gaukler. Oligomer formation in epoxy-dicyandiamide systems [J]. The Journal of Adhesion, 2012, 88:720-750
[17]	Hong Shinngwo, Wu Chungsheng. DSC and FTIR analysis of the curing behaviors of epoxy/DICY/solvent open systems [J]. Thermochimica Acta, 1998, 316:167-175
[18]	Chen Lianxi (陈连喜), Zhang Huiling (张惠玲), Liu Quanwen (刘全文), Wang Jun (王钧). Characteristic of curing reaction of epoxy resin with dicyandiamide modified by aromatic amines [J]. J. Wuhan Univ.: Nat. Sci. Ed. (武汉大学学报: 理学版), 2006, 52 (4): 426-430
[19]	Zhou Jianping (周建萍), Zeng Qingyu (曾庆煜), Cao Wanrong (曹万荣), Di Ningyu (狄宁宇). Preparation of latent curing agents for waterborne epoxy via modification of dicyandiamide with formaldehyde [J]. Paint & Coatings Industry (涂料工业), 2010, 40 (12): 13-16
[20]	Du Xiaodi (杜小弟). Study on the mechanism of the synthesis of phenyl-biguanide and the kinetics of curing epoxy [D]. Wuhan: Wuhan University of Technology, 2007: 31-53
[21]	Chen Sufeng (陈苏锋), Shi Tiejun (史铁钧), Yang Zhaopan (杨兆攀), Tan Dexin (谭德新). Synthesis, characterization and non-isothermal curing kinetics of tri-propargyl isocyanurate [J]. CIESC Journal (化工学报), 2012, 63 (7): 2085-2091
[22]	Yang Zhaopan (杨兆攀), Shi Tiejun (史铁钧), Tan Dexing (谭德兴). Synthesis of dipropargyl ether of bisphenol A and thermal degradation kinetics of its polymer [J]. CIESC Journal (化工学报), 2011, 62 (12): 3554-3559
[23]	Liu Jing (刘静), Zhao Min (赵敏), Zhang Rongzhen (张荣珍), Liu Guangtian (刘广田), Ba Xinwu (巴信武). Study on the curing kinetics of epoxy resin by FTIR [J]. Journal of Functional Polymers (功能高分子学报), 2000, 13 (2): 207-210