Cr/W/稀土氧化物涂层的抑制结焦性能

doi:10.3969/j.issn.0438-1157.2014.11.045

化工学报 ›› 2014, Vol. 65 ›› Issue (11): 4530-4535.DOI: 10.3969/j.issn.0438-1157.2014.11.045

Cr/W/稀土氧化物涂层的抑制结焦性能

陆阳¹, 刘京雷¹, 徐宏¹, 屈笑雨¹, 刘建书^1,2, 万顺¹

1. 华东理工大学机械与动力工程学院, 上海 200237;
2. 无锡化工装备有限公司, 江苏无锡 214131

收稿日期:2014-04-14 修回日期:2014-06-25 出版日期:2014-11-05 发布日期:2014-11-05
通讯作者: 刘京雷
基金资助:
教育部博士学科点专项科研基金项目(20110074110009).

Anti-coking property of Cr/W/rare earth oxides coating for transfer line exchanger

LU Yang¹, LIU Jinglei¹, XU Hong¹, QU Xiaoyu¹, LIU Jianshu^1,2, WAN Shun¹

1. School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China;
2. Wuxi Chemical Equipment Co., Ltd., Wuxi 214131, Jiangsu, China

Received:2014-04-14 Revised:2014-06-25 Online:2014-11-05 Published:2014-11-05
Supported by:
supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China(20110074110009).

摘要/Abstract

摘要： 急冷锅炉(TLE)是乙烯热裂解装置的重要设备,在运行中急冷锅炉炉管内壁会有结焦现象,降低急冷锅炉传热系数并增加炉管压力降,严重影响传热效果,需要进行周期性清焦.为了能够有效地抑制结焦,在炉管内壁表面上制备了一层Cr/W/稀土Re_xO_y惰性涂层,借助乙烯裂解结焦模拟装置、金相显微镜、扫描电子显微镜(SEM)和透射电镜(TEM)等设备从试样结焦表面形貌特征和结焦量等方面对所开发的涂层进行了抑焦性能研究.实验结果表明,无涂层试样表面存在催化焦和颗粒状焦,结焦严重;而涂层试样抑焦效果明显,表面不存在催化结焦,且焦层与涂层表面黏附性差结合较弱容易脱落,其结焦抑制率可达79.1%.

关键词: 热裂解, 结焦, 表面, 涂层, 乙烯, 急冷锅炉

Abstract: Transfer line exchanger (TLE) is an important equipment for ethylene cracking unit. In actual operation, coke formation occurs on the inner surface of tubes in TLE. In effectively inhibit coking on the inner surface of tubes, inert coating of Cr/W/REO was applied on the surface of the tube metal. With aids of ethylene cracking simulator, metallurgic microscope, electronic scanning microscope (SEM), and transmission electron microscopy (TEM), coking inhibition performance of inert coating was studied, including the characteristics of coke surface and coking amounts of specimens. Serious coking occurred on the blank specimen surface with catalytic coke and granular coke, while the coated specimen showed great anti-coking effect without catalytic coke and the coke layer was easy to remove. Coking inhibition rate reached 79.1%.

Key words: pyrolysis, coking, surface, coating, ethylene, transfer line exchanger

中图分类号:

TK229.92⁺9

陆阳, 刘京雷, 徐宏, 屈笑雨, 刘建书, 万顺. Cr/W/稀土氧化物涂层的抑制结焦性能[J]. 化工学报, 2014, 65(11): 4530-4535.

LU Yang, LIU Jinglei, XU Hong, QU Xiaoyu, LIU Jianshu, WAN Shun. Anti-coking property of Cr/W/rare earth oxides coating for transfer line exchanger[J]. CIESC Journal, 2014, 65(11): 4530-4535.

参考文献 19

[1]	Cai H, Krzywicki A, Oballa M C. Coke formation in steam crackers for ethylene production [J]. Chemical Engineering and Processing: Process Intensification, 2002, 41(3): 199-214
[2]	Geem K M V, Dhuyvetter I, Prokopiev S, et al. Coke formation in the transfer line exchanger during steam cracking of hydrocarbons [J]. Industrial & Engineering Chemistry Research, 2009, 48(23): 10343- 10358
[3]	Guo Zhaoyang(郭兆阳), Wang Yuanhua(王元华), Xu Hong(徐宏), Shi Yonghong(史永红), Guo Chao(郭超), Yang Sheng(杨胜). Optimization and investigation of flow for circular and elliptic gas distributor tubes in transfer line exchanger [J]. CIESC Journal(化工学报), 2012, 63(8): 2365-2374
[4]	Manafzadeh H, Sadrameli S M, Towfighi J. Coke deposition by physical condensation of poly-cyclic hydrocarbons in the transfer line exchanger (TLX) of olefin plant [J]. Applied Thermal Engineering, 2003, 23(11): 1347-1358
[5]	Yu Tingting(于婷婷). Ethylene quench system process simulation and improvement research [D]. Tianjin: Tianjin University, 2008
[6]	Zhou Jianxin(周建新), Xu Hong(徐宏), Liu Jinglei(刘京雷). Research process of anti-coking coating for ethylene pyrolysis furnace tubes [J]. Petrochemical Industry(石油加工), 2007, 36(3): 310-314
[7]	Wang J, Reyniers M F, àan Geem K M, et al. Influence of silicon and silicon/sulfur-containing additives on coke formation during steam cracking of hydrocarbons [J]. Industrial & Engineering Chemistry Research, 2008, 47(5): 1468-1482
[8]	Zhou Jianxin, Wang Zhiyuan, Luan Xiaojian, et al. Anti-coking property of the SiO2/S coating during light naphtha steam cracking in a pilot plant setup [J]. Journal of Analytical & Applied Pyrolysis, 2011, 90(1):7-12
[9]	Wang Z, Xu H, Zhou J, et al. Simulation of SiO2/S coating deposition in a pilot plant set-up for coking inhibition [J]. Chemical Engineering Research and Design, 2013, 91(1): 120-133
[10]	Chang Shunli(常顺利), Ji Libin(吉李彬). Research of anti-coking technology for catalytic cracking unit [J]. China Petroleum and Chemical Industry Standard and Quality(中国石油和化工标准与质量), 2012, 33(11): 82-83
[11]	Alstrup I. A new model explaining carbon filament growth on nickel, iron, and Ni Cu alloy catalysts [J]. Journal of Catalysis, 1988, 109(2): 241-251
[12]	Jackson P R S,Trimm D L,Young D J．The coking kinetics of heat resistant austenitic steel in hydrogen-propylene atmospheres [J]. Journal of Materials Science, 1986, 21(9): 3125-3134
[13]	Wang Zhiyuan, Xu Hong, Luan Xiaojian, Hou Feng, Zhou Jianxin. Effect of potassium acetate on coke growth during light naphtha thermal cracking [J]. Industrial & Engineering Chemistry Research, 2011, 50(17): 10292-10297
[14]	Wang Jidong,Marie-Francoise Reyniers,Guy B Matin．Influence of dimethyl disulfide on coke formation during steam cracking of hydrocarbons [J]. Ind. Eng. Chem. Res., 2007, 46(12): 4137
[15]	Reyniers G C, Froment G F, Kopinke F D, et al. Coke formation in the thermal cracking of hydrocarbons(Ⅳ): Modeling of coke formation in naphtha cracking [J]. Industrial & Engineering Chemistry Research, 1994, 33(11): 2584-2590
[16]	Pyl S P, Schietekat C M, Reyniers M F, et al. Biomass to olefin: cracking of renewable naphtha [J]. Chemical Engineering Journal, 2011, 176/177: 178-187
[17]	Figueiredo J L. Reactivity of coke deposited on metal surfaces [J]. Materials and Corrosion, 1999, 50(12): 696-699
[18]	Ishiyama E M, Paterson W R, Wilson D I. Exploration of alternative models for the aging of fouling deposits [J]. AIChE J., 2011, 57(11): 3199-3209
[19]	Bach G, Zimmmermann G, Kopinke F D, et al. Transfer-line heat exchanger fouling during pyrolysis of hydrocarbons(Ⅰ): Deposits from dry cracked gases [J]. Industrial & Engineering Chemistry Research, 1995, 34(4): 1132-1139

Cr/W/稀土氧化物涂层的抑制结焦性能

Anti-coking property of Cr/W/rare earth oxides coating for transfer line exchanger

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 19

相关文章 15

编辑推荐

Metrics

本文评价

[1]	吴馨, 龚建英, 靳龙, 王宇涛, 黄睿宁. 超声波激励下铝板表面液滴群输运特性的研究[J]. 化工学报, 2023, 74(S1): 104-112.
[2]	王浩, 王振雷. 基于自适应谱方法的裂解炉烧焦模型化简策略[J]. 化工学报, 2023, 74(9): 3855-3864.
[3]	林典, 江国梅, 徐秀彬, 赵波, 刘冬梅, 吴旭. 硅基类液防原油黏附涂层的研制及其减阻性能研究[J]. 化工学报, 2023, 74(8): 3438-3445.
[4]	杨越, 张丹, 郑巨淦, 涂茂萍, 杨庆忠. NaCl水溶液喷射闪蒸-掺混蒸发的实验研究[J]. 化工学报, 2023, 74(8): 3279-3291.
[5]	孟令玎, 崇汝青, 孙菲雪, 孟子晖, 刘文芳. 改性聚乙烯膜和氧化硅固定化碳酸酐酶[J]. 化工学报, 2023, 74(8): 3472-3484.
[6]	杨欣, 彭啸, 薛凯茹, 苏梦威, 吴燕. 分子印迹-TiO₂光电催化降解增溶PHE废水性能研究[J]. 化工学报, 2023, 74(8): 3564-3571.
[7]	诸程瑛, 王振雷. 基于改进深度强化学习的乙烯裂解炉操作优化[J]. 化工学报, 2023, 74(8): 3429-3437.
[8]	陈天华, 刘兆轩, 韩群, 张程宾, 李文明. 喷雾冷却换热强化研究进展及影响因素[J]. 化工学报, 2023, 74(8): 3149-3170.
[9]	张蒙蒙, 颜冬, 沈永峰, 李文翠. 电解液类型对双离子电池阴阳离子储存行为的影响[J]. 化工学报, 2023, 74(7): 3116-3126.
[10]	赵婧, 顾程文, 蹇锡高, 翁志焕. 厚朴酚基环氧树脂防腐涂层的制备及性能评价[J]. 化工学报, 2023, 74(7): 3010-3017.
[11]	崔张宁, 胡紫璇, 吴雷, 周军, 叶干, 刘田田, 张秋利, 宋永辉. 可降解纤维素基材料的耐水性能研究进展[J]. 化工学报, 2023, 74(6): 2296-2307.
[12]	王新悦, 王俊杰, 曹思贤, 王翠, 李灵坤, 吴宏宇, 韩静, 吴昊. 玻璃内包材界面修饰对机械应力诱导的单克隆抗体聚集体形成的影响[J]. 化工学报, 2023, 74(6): 2580-2588.
[13]	徐文超, 孙志高, 李翠敏, 李娟, 黄海峰. 静态条件下表面活性剂E-1310对HCFC-141b水合物生成的影响[J]. 化工学报, 2023, 74(5): 2179-2185.
[14]	葛运通, 王玮, 李楷, 肖帆, 于志鹏, 宫敬. 多相分散体系中微油滴与改性二氧化硅表面间作用力的AFM研究[J]. 化工学报, 2023, 74(4): 1651-1659.
[15]	刘倩, 曹禹, 周琦, 穆景山, 历伟. 孔道结构修饰的Ziegler-Natta催化剂设计与高抗冲低缠结UHMWPE的制备[J]. 化工学报, 2023, 74(3): 1092-1101.